Preparation and porous properties of materials prepared by selective leaching of phlogopite View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2002-10-01

AUTHORS

Kiyoshi Okada, Noriyuki Nakazawa, Yoshikazu Kameshima, Atsuo Yasumori, Jadambaa Temuujin, Kenneth J. D. MacKenzie, Mark E. Smith

ABSTRACT

Porous silica products obtained by selective leaching of phlogopite using an acid solution were investigated by XRD, MAS NMR, SEM, TEM, DTA/TG, and N2 and Ar gas adsorptions. The phlogopite powder was leached by a nitric acid solution at various concentrations (0.01–10 M) at 5–150°C for 10 min–480 h. Selective leaching of the phlogopite powder became extensive when the concentration of nitric acid was >1 M. Only SiO2 remained after the treatment, the other components (MgO, Al2O3, K2O and Fe2O3) being selectively leached from the product. At higher leaching temperatures, the leaching rate became faster and the resulting maximum specific surface area of the porous silica product became larger at each leaching temperature. The porous silica products were found by SEM and TEM, to maintain their original platy particle shape even after the selective leaching. The 29Si MAS NMR spectra of the products, however, revealed that the linkage structure of SiO4 tetrahedra converted to a framework type from a layered type in the original phlogopite. The porous silica product with the maximum specific surface area (532 m2/g) was obtained by leaching in a nitric acid solution with concentration of 5 M at 90°C for 15 min. The pore-size distribution of the porous silica product was bimodal with micropores of ∼0.7 nm and mesopores of ∼4 nm. The pore size of the products changed from 0.7 nm to 4 nm and further to 6 nm with increased leaching time. The present results are discussed in relation to those reported for phlogopite by other workers. More... »

PAGES

624-632

Identifiers

URI

http://scigraph.springernature.com/pub.10.1346/000986002320679503

DOI

http://dx.doi.org/10.1346/000986002320679503

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1065017341


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/04", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Earth Sciences", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/05", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Environmental Sciences", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0403", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Geology", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0503", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Soil Sciences", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan", 
          "id": "http://www.grid.ac/institutes/grid.32197.3e", 
          "name": [
            "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Okada", 
        "givenName": "Kiyoshi", 
        "id": "sg:person.0770256433.01", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0770256433.01"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan", 
          "id": "http://www.grid.ac/institutes/grid.32197.3e", 
          "name": [
            "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Nakazawa", 
        "givenName": "Noriyuki", 
        "id": "sg:person.016065235647.51", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016065235647.51"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan", 
          "id": "http://www.grid.ac/institutes/grid.32197.3e", 
          "name": [
            "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Kameshima", 
        "givenName": "Yoshikazu", 
        "id": "sg:person.01310016643.54", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01310016643.54"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan", 
          "id": "http://www.grid.ac/institutes/grid.32197.3e", 
          "name": [
            "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Yasumori", 
        "givenName": "Atsuo", 
        "id": "sg:person.01136150570.36", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01136150570.36"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan", 
          "id": "http://www.grid.ac/institutes/grid.32197.3e", 
          "name": [
            "Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Temuujin", 
        "givenName": "Jadambaa", 
        "id": "sg:person.016275474025.53", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016275474025.53"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "The New Zealand Institute for Industrial Research and Development, Lower Hutt, New Zealand", 
          "id": "http://www.grid.ac/institutes/grid.418016.a", 
          "name": [
            "The New Zealand Institute for Industrial Research and Development, Lower Hutt, New Zealand"
          ], 
          "type": "Organization"
        }, 
        "familyName": "MacKenzie", 
        "givenName": "Kenneth J. D.", 
        "id": "sg:person.011221006045.25", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011221006045.25"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Physics, University of Warwick, Coventry, UK", 
          "id": "http://www.grid.ac/institutes/grid.7372.1", 
          "name": [
            "Department of Physics, University of Warwick, Coventry, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Smith", 
        "givenName": "Mark E.", 
        "id": "sg:person.01264356750.37", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01264356750.37"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1346/ccmn.1994.0420607", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1065020095", 
          "https://doi.org/10.1346/ccmn.1994.0420607"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1346/ccmn.1998.0460301", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1065020411", 
          "https://doi.org/10.1346/ccmn.1998.0460301"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1346/ccmn.1996.0440208", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1065020214", 
          "https://doi.org/10.1346/ccmn.1996.0440208"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2002-10-01", 
    "datePublishedReg": "2002-10-01", 
    "description": "Porous silica products obtained by selective leaching of phlogopite using an acid solution were investigated by XRD, MAS NMR, SEM, TEM, DTA/TG, and N2 and Ar gas adsorptions. The phlogopite powder was leached by a nitric acid solution at various concentrations (0.01\u201310 M) at 5\u2013150\u00b0C for 10 min\u2013480 h. Selective leaching of the phlogopite powder became extensive when the concentration of nitric acid was >1 M. Only SiO2 remained after the treatment, the other components (MgO, Al2O3, K2O and Fe2O3) being selectively leached from the product. At higher leaching temperatures, the leaching rate became faster and the resulting maximum specific surface area of the porous silica product became larger at each leaching temperature. The porous silica products were found by SEM and TEM, to maintain their original platy particle shape even after the selective leaching. The 29Si MAS NMR spectra of the products, however, revealed that the linkage structure of SiO4 tetrahedra converted to a framework type from a layered type in the original phlogopite. The porous silica product with the maximum specific surface area (532 m2/g) was obtained by leaching in a nitric acid solution with concentration of 5 M at 90\u00b0C for 15 min. The pore-size distribution of the porous silica product was bimodal with micropores of \u223c0.7 nm and mesopores of \u223c4 nm. The pore size of the products changed from 0.7 nm to 4 nm and further to 6 nm with increased leaching time. The present results are discussed in relation to those reported for phlogopite by other workers.", 
    "genre": "article", 
    "id": "sg:pub.10.1346/000986002320679503", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1026103", 
        "issn": [
          "0009-8604", 
          "1552-8367"
        ], 
        "name": "Clays and Clay Minerals", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "5", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "50"
      }
    ], 
    "keywords": [
      "maximum specific surface area", 
      "silica products", 
      "specific surface area", 
      "surface area", 
      "selective leaching", 
      "only SiO2", 
      "pore size distribution", 
      "pore size", 
      "higher leaching temperatures", 
      "nitric acid solution", 
      "porous properties", 
      "gas adsorption", 
      "acid solution", 
      "TEM", 
      "leaching temperature", 
      "DTA/TG", 
      "SEM", 
      "leaching rate", 
      "particle shape", 
      "mesopores", 
      "nitric acid", 
      "powder", 
      "leaching", 
      "XRD", 
      "SiO2", 
      "adsorption", 
      "micropores", 
      "temperature", 
      "MAS NMR", 
      "solution", 
      "products", 
      "preparation", 
      "size", 
      "concentration", 
      "materials", 
      "properties", 
      "linkage structure", 
      "SiO4 tetrahedra", 
      "N2", 
      "structure", 
      "area", 
      "shape", 
      "acid", 
      "framework type", 
      "Tg", 
      "distribution", 
      "present results", 
      "min", 
      "NMR", 
      "components", 
      "types", 
      "results", 
      "time", 
      "rate", 
      "tetrahedra", 
      "H.", 
      "relation", 
      "treatment", 
      "phlogopite", 
      "workers"
    ], 
    "name": "Preparation and porous properties of materials prepared by selective leaching of phlogopite", 
    "pagination": "624-632", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1065017341"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1346/000986002320679503"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1346/000986002320679503", 
      "https://app.dimensions.ai/details/publication/pub.1065017341"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2022-12-01T06:23", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20221201/entities/gbq_results/article/article_346.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1346/000986002320679503"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1346/000986002320679503'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1346/000986002320679503'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1346/000986002320679503'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1346/000986002320679503'


 

This table displays all metadata directly associated to this object as RDF triples.

185 TRIPLES      21 PREDICATES      89 URIs      76 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1346/000986002320679503 schema:about anzsrc-for:04
2 anzsrc-for:0403
3 anzsrc-for:05
4 anzsrc-for:0503
5 schema:author Nad1bef6772cf42ce892e545b7e9a47ea
6 schema:citation sg:pub.10.1346/ccmn.1994.0420607
7 sg:pub.10.1346/ccmn.1996.0440208
8 sg:pub.10.1346/ccmn.1998.0460301
9 schema:datePublished 2002-10-01
10 schema:datePublishedReg 2002-10-01
11 schema:description Porous silica products obtained by selective leaching of phlogopite using an acid solution were investigated by XRD, MAS NMR, SEM, TEM, DTA/TG, and N2 and Ar gas adsorptions. The phlogopite powder was leached by a nitric acid solution at various concentrations (0.01–10 M) at 5–150°C for 10 min–480 h. Selective leaching of the phlogopite powder became extensive when the concentration of nitric acid was >1 M. Only SiO2 remained after the treatment, the other components (MgO, Al2O3, K2O and Fe2O3) being selectively leached from the product. At higher leaching temperatures, the leaching rate became faster and the resulting maximum specific surface area of the porous silica product became larger at each leaching temperature. The porous silica products were found by SEM and TEM, to maintain their original platy particle shape even after the selective leaching. The 29Si MAS NMR spectra of the products, however, revealed that the linkage structure of SiO4 tetrahedra converted to a framework type from a layered type in the original phlogopite. The porous silica product with the maximum specific surface area (532 m2/g) was obtained by leaching in a nitric acid solution with concentration of 5 M at 90°C for 15 min. The pore-size distribution of the porous silica product was bimodal with micropores of ∼0.7 nm and mesopores of ∼4 nm. The pore size of the products changed from 0.7 nm to 4 nm and further to 6 nm with increased leaching time. The present results are discussed in relation to those reported for phlogopite by other workers.
12 schema:genre article
13 schema:isAccessibleForFree false
14 schema:isPartOf Neb93a768efca4994805c28e89369ed0a
15 Nee77c33a2b664fc9b99005436998e432
16 sg:journal.1026103
17 schema:keywords DTA/TG
18 H.
19 MAS NMR
20 N2
21 NMR
22 SEM
23 SiO2
24 SiO4 tetrahedra
25 TEM
26 Tg
27 XRD
28 acid
29 acid solution
30 adsorption
31 area
32 components
33 concentration
34 distribution
35 framework type
36 gas adsorption
37 higher leaching temperatures
38 leaching
39 leaching rate
40 leaching temperature
41 linkage structure
42 materials
43 maximum specific surface area
44 mesopores
45 micropores
46 min
47 nitric acid
48 nitric acid solution
49 only SiO2
50 particle shape
51 phlogopite
52 pore size
53 pore size distribution
54 porous properties
55 powder
56 preparation
57 present results
58 products
59 properties
60 rate
61 relation
62 results
63 selective leaching
64 shape
65 silica products
66 size
67 solution
68 specific surface area
69 structure
70 surface area
71 temperature
72 tetrahedra
73 time
74 treatment
75 types
76 workers
77 schema:name Preparation and porous properties of materials prepared by selective leaching of phlogopite
78 schema:pagination 624-632
79 schema:productId N5480f1eb2a00458197c1d532911c8e87
80 Nc5f252c9498a47be943e4b15dbc7cac2
81 schema:sameAs https://app.dimensions.ai/details/publication/pub.1065017341
82 https://doi.org/10.1346/000986002320679503
83 schema:sdDatePublished 2022-12-01T06:23
84 schema:sdLicense https://scigraph.springernature.com/explorer/license/
85 schema:sdPublisher N02995c2fc7a349b99c8930aa673ddafc
86 schema:url https://doi.org/10.1346/000986002320679503
87 sgo:license sg:explorer/license/
88 sgo:sdDataset articles
89 rdf:type schema:ScholarlyArticle
90 N02995c2fc7a349b99c8930aa673ddafc schema:name Springer Nature - SN SciGraph project
91 rdf:type schema:Organization
92 N0b6789090ebf45d5b1d4652618685315 rdf:first sg:person.01136150570.36
93 rdf:rest N3e82680c57264e8fad983907c9ddf4d8
94 N38fbd2d4247e493f87e349199db46591 rdf:first sg:person.01310016643.54
95 rdf:rest N0b6789090ebf45d5b1d4652618685315
96 N3e82680c57264e8fad983907c9ddf4d8 rdf:first sg:person.016275474025.53
97 rdf:rest Nae41ec49460b48059399c0ed84bdc677
98 N5480f1eb2a00458197c1d532911c8e87 schema:name doi
99 schema:value 10.1346/000986002320679503
100 rdf:type schema:PropertyValue
101 Nad1bef6772cf42ce892e545b7e9a47ea rdf:first sg:person.0770256433.01
102 rdf:rest Nf2bce15c100248c0adeb527e73cb187f
103 Nae41ec49460b48059399c0ed84bdc677 rdf:first sg:person.011221006045.25
104 rdf:rest Ne8a127ef9515403cbcdfd88e82740eff
105 Nc5f252c9498a47be943e4b15dbc7cac2 schema:name dimensions_id
106 schema:value pub.1065017341
107 rdf:type schema:PropertyValue
108 Ne8a127ef9515403cbcdfd88e82740eff rdf:first sg:person.01264356750.37
109 rdf:rest rdf:nil
110 Neb93a768efca4994805c28e89369ed0a schema:issueNumber 5
111 rdf:type schema:PublicationIssue
112 Nee77c33a2b664fc9b99005436998e432 schema:volumeNumber 50
113 rdf:type schema:PublicationVolume
114 Nf2bce15c100248c0adeb527e73cb187f rdf:first sg:person.016065235647.51
115 rdf:rest N38fbd2d4247e493f87e349199db46591
116 anzsrc-for:04 schema:inDefinedTermSet anzsrc-for:
117 schema:name Earth Sciences
118 rdf:type schema:DefinedTerm
119 anzsrc-for:0403 schema:inDefinedTermSet anzsrc-for:
120 schema:name Geology
121 rdf:type schema:DefinedTerm
122 anzsrc-for:05 schema:inDefinedTermSet anzsrc-for:
123 schema:name Environmental Sciences
124 rdf:type schema:DefinedTerm
125 anzsrc-for:0503 schema:inDefinedTermSet anzsrc-for:
126 schema:name Soil Sciences
127 rdf:type schema:DefinedTerm
128 sg:journal.1026103 schema:issn 0009-8604
129 1552-8367
130 schema:name Clays and Clay Minerals
131 schema:publisher Springer Nature
132 rdf:type schema:Periodical
133 sg:person.011221006045.25 schema:affiliation grid-institutes:grid.418016.a
134 schema:familyName MacKenzie
135 schema:givenName Kenneth J. D.
136 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011221006045.25
137 rdf:type schema:Person
138 sg:person.01136150570.36 schema:affiliation grid-institutes:grid.32197.3e
139 schema:familyName Yasumori
140 schema:givenName Atsuo
141 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01136150570.36
142 rdf:type schema:Person
143 sg:person.01264356750.37 schema:affiliation grid-institutes:grid.7372.1
144 schema:familyName Smith
145 schema:givenName Mark E.
146 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01264356750.37
147 rdf:type schema:Person
148 sg:person.01310016643.54 schema:affiliation grid-institutes:grid.32197.3e
149 schema:familyName Kameshima
150 schema:givenName Yoshikazu
151 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.01310016643.54
152 rdf:type schema:Person
153 sg:person.016065235647.51 schema:affiliation grid-institutes:grid.32197.3e
154 schema:familyName Nakazawa
155 schema:givenName Noriyuki
156 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016065235647.51
157 rdf:type schema:Person
158 sg:person.016275474025.53 schema:affiliation grid-institutes:grid.32197.3e
159 schema:familyName Temuujin
160 schema:givenName Jadambaa
161 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016275474025.53
162 rdf:type schema:Person
163 sg:person.0770256433.01 schema:affiliation grid-institutes:grid.32197.3e
164 schema:familyName Okada
165 schema:givenName Kiyoshi
166 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0770256433.01
167 rdf:type schema:Person
168 sg:pub.10.1346/ccmn.1994.0420607 schema:sameAs https://app.dimensions.ai/details/publication/pub.1065020095
169 https://doi.org/10.1346/ccmn.1994.0420607
170 rdf:type schema:CreativeWork
171 sg:pub.10.1346/ccmn.1996.0440208 schema:sameAs https://app.dimensions.ai/details/publication/pub.1065020214
172 https://doi.org/10.1346/ccmn.1996.0440208
173 rdf:type schema:CreativeWork
174 sg:pub.10.1346/ccmn.1998.0460301 schema:sameAs https://app.dimensions.ai/details/publication/pub.1065020411
175 https://doi.org/10.1346/ccmn.1998.0460301
176 rdf:type schema:CreativeWork
177 grid-institutes:grid.32197.3e schema:alternateName Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan
178 schema:name Department of Metallurgy and Ceramics Science, Graduate School of Science and Engineering, Tokyo Institute of Technology, O-okayama, Meguro, 152-8552, Tokyo, Japan
179 rdf:type schema:Organization
180 grid-institutes:grid.418016.a schema:alternateName The New Zealand Institute for Industrial Research and Development, Lower Hutt, New Zealand
181 schema:name The New Zealand Institute for Industrial Research and Development, Lower Hutt, New Zealand
182 rdf:type schema:Organization
183 grid-institutes:grid.7372.1 schema:alternateName Department of Physics, University of Warwick, Coventry, UK
184 schema:name Department of Physics, University of Warwick, Coventry, UK
185 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...