Novel Degradation Mechanism of a Structural Wire Rope During Its Life Cycle View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2019-01-07

AUTHORS

Kaushal Kishore, Goutam Mukhopadhyay

ABSTRACT

High-carbon steel wire ropes are used for various high-load-bearing applications. They achieve tensile strength of the order of 2 GPa owing to a combination of fine pearlitic microstructure and work hardening during the drawing process. Despite these high strength levels, they can fail during service due to either manufacturing defects or service abuse. In this study, failure analysis of main hoist steel wire rope used in a basic oxygen furnace (BOF) was carried out. Several locations of the wire rope showed unprecedented microstructural degradation. The presence of surface martensite with transverse cracks was observed in severely abraded wires. Some locations of the rope revealed fusion of adjacent wires with increased interlamellar spacing of pearlite and formation of divorced pearlite in heat-affected and fusion zones, respectively. A significant variation in hardness across the wire rope was noted due to these in-service microstructural changes. Such macroscopic and microstructural deterioration has not been reported in open literature. Detailed failure analysis of the wire rope along with a novel theory explaining the mechanisms of such microstructural degradation is presented herein. This study confirms that the wire rope suffered premature damage due to improper lubrication during service that led to direct metal-to-metal contact, associated friction, abrasion, and fusion of wires. Excessive friction and abrasion of wires subsequently led to fatigue of some of the wires, as manifested by square or crown breaks and striation marks.Graphical Abstract More... »

PAGES

189-200

References to SciGraph publications

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s13632-018-0511-9

DOI

http://dx.doi.org/10.1007/s13632-018-0511-9

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1111248670


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India", 
          "id": "http://www.grid.ac/institutes/grid.460003.1", 
          "name": [
            "R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Kishore", 
        "givenName": "Kaushal", 
        "id": "sg:person.014607070430.40", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014607070430.40"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India", 
          "id": "http://www.grid.ac/institutes/grid.460003.1", 
          "name": [
            "R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Mukhopadhyay", 
        "givenName": "Goutam", 
        "id": "sg:person.012627373741.97", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012627373741.97"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1007/978-1-4899-3051-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1109705848", 
          "https://doi.org/10.1007/978-1-4899-3051-4"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2019-01-07", 
    "datePublishedReg": "2019-01-07", 
    "description": "High-carbon steel wire ropes are used for various high-load-bearing applications. They achieve tensile strength of the order of 2\u00a0GPa owing to a combination of fine pearlitic microstructure and work hardening during the drawing process. Despite these high strength levels, they can fail during service due to either manufacturing defects or service abuse. In this study, failure analysis of main hoist steel wire rope used in a basic oxygen furnace (BOF) was carried out. Several locations of the wire rope showed unprecedented microstructural degradation. The presence of surface martensite with transverse cracks was observed in severely abraded wires. Some locations of the rope revealed fusion of adjacent wires with increased interlamellar spacing of pearlite and formation of divorced pearlite in heat-affected and fusion zones, respectively. A significant variation in hardness across the wire rope was noted due to these in-service microstructural changes. Such macroscopic and microstructural deterioration has not been reported in open literature. Detailed failure analysis of the wire rope along with a novel theory explaining the mechanisms of such microstructural degradation is presented herein. This study confirms that the wire rope suffered premature damage due to improper lubrication during service that led to direct metal-to-metal contact, associated friction, abrasion, and fusion of wires. Excessive friction and abrasion of wires subsequently led to fatigue of some of the wires, as manifested by square or crown breaks and striation marks.Graphical Abstract", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s13632-018-0511-9", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136434", 
        "issn": [
          "2192-9262", 
          "2192-9270"
        ], 
        "name": "Metallography, Microstructure, and Analysis", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "2", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "8"
      }
    ], 
    "keywords": [
      "steel wire rope", 
      "basic oxygen furnace", 
      "wire rope", 
      "microstructural degradation", 
      "failure analysis", 
      "fine pearlitic microstructure", 
      "high strength levels", 
      "detailed failure analysis", 
      "pearlitic microstructure", 
      "fusion zone", 
      "improper lubrication", 
      "transverse cracks", 
      "oxygen furnace", 
      "premature damage", 
      "tensile strength", 
      "novel degradation mechanism", 
      "metal contacts", 
      "drawing process", 
      "direct metal", 
      "associated friction", 
      "interlamellar spacing", 
      "strength levels", 
      "microstructural changes", 
      "open literature", 
      "degradation mechanism", 
      "striation marks", 
      "excessive friction", 
      "wire", 
      "adjacent wires", 
      "friction", 
      "surface martensite", 
      "rope", 
      "abrasion", 
      "microstructural deterioration", 
      "pearlite", 
      "furnace", 
      "cracks", 
      "martensite", 
      "microstructure", 
      "lubrication", 
      "hardening", 
      "hardness", 
      "degradation", 
      "GPa", 
      "strength", 
      "spacing", 
      "metals", 
      "service abuse", 
      "crown break", 
      "fatigue", 
      "applications", 
      "location", 
      "novel theory", 
      "zone", 
      "life cycle", 
      "contact", 
      "process", 
      "cycle", 
      "order", 
      "defects", 
      "analysis", 
      "deterioration", 
      "fusion", 
      "significant variation", 
      "mechanism", 
      "formation", 
      "variation", 
      "breaks", 
      "damage", 
      "combination", 
      "theory", 
      "study", 
      "presence", 
      "changes", 
      "literature", 
      "marks", 
      "levels", 
      "services", 
      "abuse", 
      "High-carbon steel wire ropes", 
      "main hoist steel wire rope", 
      "hoist steel wire rope", 
      "unprecedented microstructural degradation", 
      "service microstructural changes", 
      "such microstructural degradation", 
      "fusion of wires", 
      "abrasion of wires", 
      "Graphical Abstract Novel Degradation Mechanism", 
      "Abstract Novel Degradation Mechanism", 
      "Structural Wire Rope"
    ], 
    "name": "Novel Degradation Mechanism of a Structural Wire Rope During Its Life Cycle", 
    "pagination": "189-200", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1111248670"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s13632-018-0511-9"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s13632-018-0511-9", 
      "https://app.dimensions.ai/details/publication/pub.1111248670"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2021-12-01T19:44", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20211201/entities/gbq_results/article/article_800.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s13632-018-0511-9"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s13632-018-0511-9'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s13632-018-0511-9'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s13632-018-0511-9'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s13632-018-0511-9'


 

This table displays all metadata directly associated to this object as RDF triples.

159 TRIPLES      22 PREDICATES      116 URIs      107 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s13632-018-0511-9 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author N85c8815b69044ebcbd38fd59f94e212d
4 schema:citation sg:pub.10.1007/978-1-4899-3051-4
5 schema:datePublished 2019-01-07
6 schema:datePublishedReg 2019-01-07
7 schema:description High-carbon steel wire ropes are used for various high-load-bearing applications. They achieve tensile strength of the order of 2 GPa owing to a combination of fine pearlitic microstructure and work hardening during the drawing process. Despite these high strength levels, they can fail during service due to either manufacturing defects or service abuse. In this study, failure analysis of main hoist steel wire rope used in a basic oxygen furnace (BOF) was carried out. Several locations of the wire rope showed unprecedented microstructural degradation. The presence of surface martensite with transverse cracks was observed in severely abraded wires. Some locations of the rope revealed fusion of adjacent wires with increased interlamellar spacing of pearlite and formation of divorced pearlite in heat-affected and fusion zones, respectively. A significant variation in hardness across the wire rope was noted due to these in-service microstructural changes. Such macroscopic and microstructural deterioration has not been reported in open literature. Detailed failure analysis of the wire rope along with a novel theory explaining the mechanisms of such microstructural degradation is presented herein. This study confirms that the wire rope suffered premature damage due to improper lubrication during service that led to direct metal-to-metal contact, associated friction, abrasion, and fusion of wires. Excessive friction and abrasion of wires subsequently led to fatigue of some of the wires, as manifested by square or crown breaks and striation marks.Graphical Abstract
8 schema:genre article
9 schema:inLanguage en
10 schema:isAccessibleForFree false
11 schema:isPartOf N1c09cd9a59f94c2c9ff98f034faaf2b8
12 N87067fd4502440459018af7607a32f41
13 sg:journal.1136434
14 schema:keywords Abstract Novel Degradation Mechanism
15 GPa
16 Graphical Abstract Novel Degradation Mechanism
17 High-carbon steel wire ropes
18 Structural Wire Rope
19 abrasion
20 abrasion of wires
21 abuse
22 adjacent wires
23 analysis
24 applications
25 associated friction
26 basic oxygen furnace
27 breaks
28 changes
29 combination
30 contact
31 cracks
32 crown break
33 cycle
34 damage
35 defects
36 degradation
37 degradation mechanism
38 detailed failure analysis
39 deterioration
40 direct metal
41 drawing process
42 excessive friction
43 failure analysis
44 fatigue
45 fine pearlitic microstructure
46 formation
47 friction
48 furnace
49 fusion
50 fusion of wires
51 fusion zone
52 hardening
53 hardness
54 high strength levels
55 hoist steel wire rope
56 improper lubrication
57 interlamellar spacing
58 levels
59 life cycle
60 literature
61 location
62 lubrication
63 main hoist steel wire rope
64 marks
65 martensite
66 mechanism
67 metal contacts
68 metals
69 microstructural changes
70 microstructural degradation
71 microstructural deterioration
72 microstructure
73 novel degradation mechanism
74 novel theory
75 open literature
76 order
77 oxygen furnace
78 pearlite
79 pearlitic microstructure
80 premature damage
81 presence
82 process
83 rope
84 service abuse
85 service microstructural changes
86 services
87 significant variation
88 spacing
89 steel wire rope
90 strength
91 strength levels
92 striation marks
93 study
94 such microstructural degradation
95 surface martensite
96 tensile strength
97 theory
98 transverse cracks
99 unprecedented microstructural degradation
100 variation
101 wire
102 wire rope
103 zone
104 schema:name Novel Degradation Mechanism of a Structural Wire Rope During Its Life Cycle
105 schema:pagination 189-200
106 schema:productId N663c5b0d21f24fe79b8a91c4a9888186
107 Nf87883a81da34099a8a31c1e82541730
108 schema:sameAs https://app.dimensions.ai/details/publication/pub.1111248670
109 https://doi.org/10.1007/s13632-018-0511-9
110 schema:sdDatePublished 2021-12-01T19:44
111 schema:sdLicense https://scigraph.springernature.com/explorer/license/
112 schema:sdPublisher N17e271d35b014ad38320320e4ebd7831
113 schema:url https://doi.org/10.1007/s13632-018-0511-9
114 sgo:license sg:explorer/license/
115 sgo:sdDataset articles
116 rdf:type schema:ScholarlyArticle
117 N012466381b244eaab133eb512fe4b167 rdf:first sg:person.012627373741.97
118 rdf:rest rdf:nil
119 N17e271d35b014ad38320320e4ebd7831 schema:name Springer Nature - SN SciGraph project
120 rdf:type schema:Organization
121 N1c09cd9a59f94c2c9ff98f034faaf2b8 schema:volumeNumber 8
122 rdf:type schema:PublicationVolume
123 N663c5b0d21f24fe79b8a91c4a9888186 schema:name dimensions_id
124 schema:value pub.1111248670
125 rdf:type schema:PropertyValue
126 N85c8815b69044ebcbd38fd59f94e212d rdf:first sg:person.014607070430.40
127 rdf:rest N012466381b244eaab133eb512fe4b167
128 N87067fd4502440459018af7607a32f41 schema:issueNumber 2
129 rdf:type schema:PublicationIssue
130 Nf87883a81da34099a8a31c1e82541730 schema:name doi
131 schema:value 10.1007/s13632-018-0511-9
132 rdf:type schema:PropertyValue
133 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
134 schema:name Engineering
135 rdf:type schema:DefinedTerm
136 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
137 schema:name Materials Engineering
138 rdf:type schema:DefinedTerm
139 sg:journal.1136434 schema:issn 2192-9262
140 2192-9270
141 schema:name Metallography, Microstructure, and Analysis
142 schema:publisher Springer Nature
143 rdf:type schema:Periodical
144 sg:person.012627373741.97 schema:affiliation grid-institutes:grid.460003.1
145 schema:familyName Mukhopadhyay
146 schema:givenName Goutam
147 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012627373741.97
148 rdf:type schema:Person
149 sg:person.014607070430.40 schema:affiliation grid-institutes:grid.460003.1
150 schema:familyName Kishore
151 schema:givenName Kaushal
152 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014607070430.40
153 rdf:type schema:Person
154 sg:pub.10.1007/978-1-4899-3051-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1109705848
155 https://doi.org/10.1007/978-1-4899-3051-4
156 rdf:type schema:CreativeWork
157 grid-institutes:grid.460003.1 schema:alternateName R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India
158 schema:name R&D and Scientific Services, Tata Steel Limited, 831001, Jamshedpur, India
159 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...