Preparation and Properties of Poly(lactic Acid)/PLA-g-ABS Blends View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2018-10

AUTHORS

Charungkit Chaikeaw, Kawee Srikulkit

ABSTRACT

PLA/PLA-g-ABS blends were prepared and evaluated for mechanical properties performance. Firstly, carboxylic acid functionalized ABS particles were synthesized by grafting polymethacrylic acid (PMAA) onto ABS particle surface using potassium persulfate as an initiator. The reaction was followed by FTIR analysis. The resultant carboxylated ABS was melt mixed with virgin PLA in an internal mixer to obtain PLA/PLA-g-ABS blends. The obtained PLA/PLA-g-ABS blends were subject to injection molding to obtain specimens for testing evaluation. It was found that impact resistance values significantly outperformed neat PLA by 60 %, 87 %, and 150 % for PLA/PLA-g-ABS 10 wt%, PLA/PLA-g-ABS 20 wt%, and PLA/PLA-g-ABS 30 wt%, respectively. A significant increase in impact strength was contributable to ABS rubber which exhibited even dispersion and good interfacial adhesion. The impact strength was dependent on the percent loading of PLAg-ABS; the more the PLA/PLA-g-ABS the higher the impact strength value. In a similar manner, tensile strength increases when loaded with PLA/PLA-g-ABS albeit at lesser effect. Considering the percent elongation, a massive increase in percent elongation was recorded in case of PLA/PLA-g-ABS 20 wt% and PLA/PLA-g-ABS 30 wt%, implying that these blends were extremely flexible and tough when compared to neat PLA, control, and PLA/PLA-g-ABS 10 wt%. More... »

PAGES

2016-2022

References to SciGraph publications

Journal

TITLE

Fibers and Polymers

ISSUE

10

VOLUME

19

Author Affiliations

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s12221-018-8320-y

DOI

http://dx.doi.org/10.1007/s12221-018-8320-y

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1107924601


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Chulalongkorn University", 
          "id": "https://www.grid.ac/institutes/grid.7922.e", 
          "name": [
            "Department of Materials Science, Faculty of Science, Chulalongkorn University, 10330, Bangkok, Thailand"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Chaikeaw", 
        "givenName": "Charungkit", 
        "id": "sg:person.010623757032.01", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010623757032.01"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Chulalongkorn University", 
          "id": "https://www.grid.ac/institutes/grid.7922.e", 
          "name": [
            "Department of Materials Science, Faculty of Science, Chulalongkorn University, 10330, Bangkok, Thailand", 
            "Center of Excellence on Petrochemicals and Materials Technology Center, Chulalongkorn University, 10330, Bangkok, Thailand"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Srikulkit", 
        "givenName": "Kawee", 
        "id": "sg:person.013147624565.07", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013147624565.07"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "https://doi.org/10.1016/j.porgcoat.2012.05.013", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006072624"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s10971-016-4252-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006475592", 
          "https://doi.org/10.1007/s10971-016-4252-4"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s10971-016-4252-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006475592", 
          "https://doi.org/10.1007/s10971-016-4252-4"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/(sici)1099-0518(19970130)35:2<219::aid-pola3>3.0.co;2-n", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1012000427"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s10924-012-0448-z", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1012993866", 
          "https://doi.org/10.1007/s10924-012-0448-z"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/pen.23186", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1014019928"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/pen.20970", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1018703659"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.polymer.2007.02.065", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1019641276"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.matchemphys.2011.05.016", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1019868573"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/(sici)1097-4628(19960222)59:8<1281::aid-app11>3.0.co;2-9", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1021251401"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0079-6700(02)00012-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1026265914"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.polymdegradstab.2012.06.031", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1031253183"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.cap.2006.01.009", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1032622833"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0014-3057(98)00265-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1032842654"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/pat.624", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034593180"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/pat.624", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034593180"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.polymertesting.2012.09.003", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034715500"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/app.1651", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034754834"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0032-3861(03)00615-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034997690"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0032-3861(03)00615-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034997690"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0142-9612(00)00101-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040712337"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.polymer.2006.03.065", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1042233763"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf00296720", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1043639893", 
          "https://doi.org/10.1007/bf00296720"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/app.31666", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049143930"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1002/app.31666", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049143930"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.eurpolymj.2007.06.045", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049744728"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.polymdegradstab.2013.02.006", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1053083482"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1021/ie2022288", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1055604689"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.eurpolymj.2017.06.004", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1085857932"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2018-10", 
    "datePublishedReg": "2018-10-01", 
    "description": "PLA/PLA-g-ABS blends were prepared and evaluated for mechanical properties performance. Firstly, carboxylic acid functionalized ABS particles were synthesized by grafting polymethacrylic acid (PMAA) onto ABS particle surface using potassium persulfate as an initiator. The reaction was followed by FTIR analysis. The resultant carboxylated ABS was melt mixed with virgin PLA in an internal mixer to obtain PLA/PLA-g-ABS blends. The obtained PLA/PLA-g-ABS blends were subject to injection molding to obtain specimens for testing evaluation. It was found that impact resistance values significantly outperformed neat PLA by 60 %, 87 %, and 150 % for PLA/PLA-g-ABS 10 wt%, PLA/PLA-g-ABS 20 wt%, and PLA/PLA-g-ABS 30 wt%, respectively. A significant increase in impact strength was contributable to ABS rubber which exhibited even dispersion and good interfacial adhesion. The impact strength was dependent on the percent loading of PLAg-ABS; the more the PLA/PLA-g-ABS the higher the impact strength value. In a similar manner, tensile strength increases when loaded with PLA/PLA-g-ABS albeit at lesser effect. Considering the percent elongation, a massive increase in percent elongation was recorded in case of PLA/PLA-g-ABS 20 wt% and PLA/PLA-g-ABS 30 wt%, implying that these blends were extremely flexible and tough when compared to neat PLA, control, and PLA/PLA-g-ABS 10 wt%.", 
    "genre": "research_article", 
    "id": "sg:pub.10.1007/s12221-018-8320-y", 
    "inLanguage": [
      "en"
    ], 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136310", 
        "issn": [
          "1229-9197", 
          "1875-0052"
        ], 
        "name": "Fibers and Polymers", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "10", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "19"
      }
    ], 
    "name": "Preparation and Properties of Poly(lactic Acid)/PLA-g-ABS Blends", 
    "pagination": "2016-2022", 
    "productId": [
      {
        "name": "readcube_id", 
        "type": "PropertyValue", 
        "value": [
          "c1d55a5eb7bd3f1a954b595e8dc77eae0ce6129a77b2088807134fc9d5547736"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s12221-018-8320-y"
        ]
      }, 
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1107924601"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s12221-018-8320-y", 
      "https://app.dimensions.ai/details/publication/pub.1107924601"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2019-04-10T16:52", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-uberresearch-data-dimensions-target-20181106-alternative/cleanup/v134/2549eaecd7973599484d7c17b260dba0a4ecb94b/merge/v9/a6c9fde33151104705d4d7ff012ea9563521a3ce/jats-lookup/v90/0000000001_0000000264/records_8669_00000573.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://link.springer.com/10.1007%2Fs12221-018-8320-y"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s12221-018-8320-y'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s12221-018-8320-y'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s12221-018-8320-y'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s12221-018-8320-y'


 

This table displays all metadata directly associated to this object as RDF triples.

147 TRIPLES      21 PREDICATES      52 URIs      19 LITERALS      7 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s12221-018-8320-y schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author Nc4ea682452674afc99d651cc2da25b1b
4 schema:citation sg:pub.10.1007/bf00296720
5 sg:pub.10.1007/s10924-012-0448-z
6 sg:pub.10.1007/s10971-016-4252-4
7 https://doi.org/10.1002/(sici)1097-4628(19960222)59:8<1281::aid-app11>3.0.co;2-9
8 https://doi.org/10.1002/(sici)1099-0518(19970130)35:2<219::aid-pola3>3.0.co;2-n
9 https://doi.org/10.1002/app.1651
10 https://doi.org/10.1002/app.31666
11 https://doi.org/10.1002/pat.624
12 https://doi.org/10.1002/pen.20970
13 https://doi.org/10.1002/pen.23186
14 https://doi.org/10.1016/j.cap.2006.01.009
15 https://doi.org/10.1016/j.eurpolymj.2007.06.045
16 https://doi.org/10.1016/j.eurpolymj.2017.06.004
17 https://doi.org/10.1016/j.matchemphys.2011.05.016
18 https://doi.org/10.1016/j.polymdegradstab.2012.06.031
19 https://doi.org/10.1016/j.polymdegradstab.2013.02.006
20 https://doi.org/10.1016/j.polymer.2006.03.065
21 https://doi.org/10.1016/j.polymer.2007.02.065
22 https://doi.org/10.1016/j.polymertesting.2012.09.003
23 https://doi.org/10.1016/j.porgcoat.2012.05.013
24 https://doi.org/10.1016/s0014-3057(98)00265-1
25 https://doi.org/10.1016/s0032-3861(03)00615-3
26 https://doi.org/10.1016/s0079-6700(02)00012-6
27 https://doi.org/10.1016/s0142-9612(00)00101-0
28 https://doi.org/10.1021/ie2022288
29 schema:datePublished 2018-10
30 schema:datePublishedReg 2018-10-01
31 schema:description PLA/PLA-g-ABS blends were prepared and evaluated for mechanical properties performance. Firstly, carboxylic acid functionalized ABS particles were synthesized by grafting polymethacrylic acid (PMAA) onto ABS particle surface using potassium persulfate as an initiator. The reaction was followed by FTIR analysis. The resultant carboxylated ABS was melt mixed with virgin PLA in an internal mixer to obtain PLA/PLA-g-ABS blends. The obtained PLA/PLA-g-ABS blends were subject to injection molding to obtain specimens for testing evaluation. It was found that impact resistance values significantly outperformed neat PLA by 60 %, 87 %, and 150 % for PLA/PLA-g-ABS 10 wt%, PLA/PLA-g-ABS 20 wt%, and PLA/PLA-g-ABS 30 wt%, respectively. A significant increase in impact strength was contributable to ABS rubber which exhibited even dispersion and good interfacial adhesion. The impact strength was dependent on the percent loading of PLAg-ABS; the more the PLA/PLA-g-ABS the higher the impact strength value. In a similar manner, tensile strength increases when loaded with PLA/PLA-g-ABS albeit at lesser effect. Considering the percent elongation, a massive increase in percent elongation was recorded in case of PLA/PLA-g-ABS 20 wt% and PLA/PLA-g-ABS 30 wt%, implying that these blends were extremely flexible and tough when compared to neat PLA, control, and PLA/PLA-g-ABS 10 wt%.
32 schema:genre research_article
33 schema:inLanguage en
34 schema:isAccessibleForFree false
35 schema:isPartOf N01f02a4e20cb4b48a7ea494f78c90f2b
36 N0308e62223f4403f94d12434f9083988
37 sg:journal.1136310
38 schema:name Preparation and Properties of Poly(lactic Acid)/PLA-g-ABS Blends
39 schema:pagination 2016-2022
40 schema:productId N56f55e86e2f44a1bb6e331cd721a4769
41 Na5f9243be28041c5b272d64e1f90a7bf
42 Nd9618ff49d1c490bbb4ce793208ce114
43 schema:sameAs https://app.dimensions.ai/details/publication/pub.1107924601
44 https://doi.org/10.1007/s12221-018-8320-y
45 schema:sdDatePublished 2019-04-10T16:52
46 schema:sdLicense https://scigraph.springernature.com/explorer/license/
47 schema:sdPublisher N0c089ff440874e758879819f6f1ee634
48 schema:url https://link.springer.com/10.1007%2Fs12221-018-8320-y
49 sgo:license sg:explorer/license/
50 sgo:sdDataset articles
51 rdf:type schema:ScholarlyArticle
52 N01f02a4e20cb4b48a7ea494f78c90f2b schema:issueNumber 10
53 rdf:type schema:PublicationIssue
54 N0308e62223f4403f94d12434f9083988 schema:volumeNumber 19
55 rdf:type schema:PublicationVolume
56 N0c089ff440874e758879819f6f1ee634 schema:name Springer Nature - SN SciGraph project
57 rdf:type schema:Organization
58 N56f55e86e2f44a1bb6e331cd721a4769 schema:name dimensions_id
59 schema:value pub.1107924601
60 rdf:type schema:PropertyValue
61 Na5f9243be28041c5b272d64e1f90a7bf schema:name doi
62 schema:value 10.1007/s12221-018-8320-y
63 rdf:type schema:PropertyValue
64 Nb06598d0509d4c2a8db407ef2dfb9e9d rdf:first sg:person.013147624565.07
65 rdf:rest rdf:nil
66 Nc4ea682452674afc99d651cc2da25b1b rdf:first sg:person.010623757032.01
67 rdf:rest Nb06598d0509d4c2a8db407ef2dfb9e9d
68 Nd9618ff49d1c490bbb4ce793208ce114 schema:name readcube_id
69 schema:value c1d55a5eb7bd3f1a954b595e8dc77eae0ce6129a77b2088807134fc9d5547736
70 rdf:type schema:PropertyValue
71 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
72 schema:name Engineering
73 rdf:type schema:DefinedTerm
74 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
75 schema:name Materials Engineering
76 rdf:type schema:DefinedTerm
77 sg:journal.1136310 schema:issn 1229-9197
78 1875-0052
79 schema:name Fibers and Polymers
80 rdf:type schema:Periodical
81 sg:person.010623757032.01 schema:affiliation https://www.grid.ac/institutes/grid.7922.e
82 schema:familyName Chaikeaw
83 schema:givenName Charungkit
84 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010623757032.01
85 rdf:type schema:Person
86 sg:person.013147624565.07 schema:affiliation https://www.grid.ac/institutes/grid.7922.e
87 schema:familyName Srikulkit
88 schema:givenName Kawee
89 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013147624565.07
90 rdf:type schema:Person
91 sg:pub.10.1007/bf00296720 schema:sameAs https://app.dimensions.ai/details/publication/pub.1043639893
92 https://doi.org/10.1007/bf00296720
93 rdf:type schema:CreativeWork
94 sg:pub.10.1007/s10924-012-0448-z schema:sameAs https://app.dimensions.ai/details/publication/pub.1012993866
95 https://doi.org/10.1007/s10924-012-0448-z
96 rdf:type schema:CreativeWork
97 sg:pub.10.1007/s10971-016-4252-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006475592
98 https://doi.org/10.1007/s10971-016-4252-4
99 rdf:type schema:CreativeWork
100 https://doi.org/10.1002/(sici)1097-4628(19960222)59:8<1281::aid-app11>3.0.co;2-9 schema:sameAs https://app.dimensions.ai/details/publication/pub.1021251401
101 rdf:type schema:CreativeWork
102 https://doi.org/10.1002/(sici)1099-0518(19970130)35:2<219::aid-pola3>3.0.co;2-n schema:sameAs https://app.dimensions.ai/details/publication/pub.1012000427
103 rdf:type schema:CreativeWork
104 https://doi.org/10.1002/app.1651 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034754834
105 rdf:type schema:CreativeWork
106 https://doi.org/10.1002/app.31666 schema:sameAs https://app.dimensions.ai/details/publication/pub.1049143930
107 rdf:type schema:CreativeWork
108 https://doi.org/10.1002/pat.624 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034593180
109 rdf:type schema:CreativeWork
110 https://doi.org/10.1002/pen.20970 schema:sameAs https://app.dimensions.ai/details/publication/pub.1018703659
111 rdf:type schema:CreativeWork
112 https://doi.org/10.1002/pen.23186 schema:sameAs https://app.dimensions.ai/details/publication/pub.1014019928
113 rdf:type schema:CreativeWork
114 https://doi.org/10.1016/j.cap.2006.01.009 schema:sameAs https://app.dimensions.ai/details/publication/pub.1032622833
115 rdf:type schema:CreativeWork
116 https://doi.org/10.1016/j.eurpolymj.2007.06.045 schema:sameAs https://app.dimensions.ai/details/publication/pub.1049744728
117 rdf:type schema:CreativeWork
118 https://doi.org/10.1016/j.eurpolymj.2017.06.004 schema:sameAs https://app.dimensions.ai/details/publication/pub.1085857932
119 rdf:type schema:CreativeWork
120 https://doi.org/10.1016/j.matchemphys.2011.05.016 schema:sameAs https://app.dimensions.ai/details/publication/pub.1019868573
121 rdf:type schema:CreativeWork
122 https://doi.org/10.1016/j.polymdegradstab.2012.06.031 schema:sameAs https://app.dimensions.ai/details/publication/pub.1031253183
123 rdf:type schema:CreativeWork
124 https://doi.org/10.1016/j.polymdegradstab.2013.02.006 schema:sameAs https://app.dimensions.ai/details/publication/pub.1053083482
125 rdf:type schema:CreativeWork
126 https://doi.org/10.1016/j.polymer.2006.03.065 schema:sameAs https://app.dimensions.ai/details/publication/pub.1042233763
127 rdf:type schema:CreativeWork
128 https://doi.org/10.1016/j.polymer.2007.02.065 schema:sameAs https://app.dimensions.ai/details/publication/pub.1019641276
129 rdf:type schema:CreativeWork
130 https://doi.org/10.1016/j.polymertesting.2012.09.003 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034715500
131 rdf:type schema:CreativeWork
132 https://doi.org/10.1016/j.porgcoat.2012.05.013 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006072624
133 rdf:type schema:CreativeWork
134 https://doi.org/10.1016/s0014-3057(98)00265-1 schema:sameAs https://app.dimensions.ai/details/publication/pub.1032842654
135 rdf:type schema:CreativeWork
136 https://doi.org/10.1016/s0032-3861(03)00615-3 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034997690
137 rdf:type schema:CreativeWork
138 https://doi.org/10.1016/s0079-6700(02)00012-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1026265914
139 rdf:type schema:CreativeWork
140 https://doi.org/10.1016/s0142-9612(00)00101-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1040712337
141 rdf:type schema:CreativeWork
142 https://doi.org/10.1021/ie2022288 schema:sameAs https://app.dimensions.ai/details/publication/pub.1055604689
143 rdf:type schema:CreativeWork
144 https://www.grid.ac/institutes/grid.7922.e schema:alternateName Chulalongkorn University
145 schema:name Center of Excellence on Petrochemicals and Materials Technology Center, Chulalongkorn University, 10330, Bangkok, Thailand
146 Department of Materials Science, Faculty of Science, Chulalongkorn University, 10330, Bangkok, Thailand
147 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...