Compatibilization of poly(lactic acid)/polycarbonate blends by different coupling agents View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2017-08

AUTHORS

Fatma Yemisci, Ayse Aytac

ABSTRACT

In this study, PLA/PC blends were prepared in order to investigate the effects of the addition of PC loading level into PLA matrix on the mechanical properties of these blends. After that, PLA/PC (70/30), which has the lowest tensile strength value, was selected as a control sample for the compatibilization study. Commercial styrene-acrylic multi-functional-epoxide oligomeric agent (SAmfE), styrene maleic anhydride copolymer (SMA), tetrasilanol phenyl polyhedral oligomeric silsesquioxane (T-POSS) and glycidyl isooctyl-polyhedral oligomeric silsesquioxane (G-POSS) were used as compatibilizers for PLA/PC blends. The variation of mechanical, thermal, structural and morphological properties were examined by conducting tensile tests, dynamic mechanical analyses, differential scanning calorimetry, Fourier Transform IR and scanning electron microscope analyses. Tensile test results showed that the tensile strength and elongation at break values of the PLA/PC blend compatibilized with SAmfE were higher than those of the other blends. DSC analyses revealed that Tg and Tm values of the blends were not significantly affected by compatibilizer but, degree of crystallinity was found to be sensitive to compatibilizer type. DMA results showed that the best mechanical properties were obtained for the PLA/PC/SAmfE blend. When all of the results evaluated, it was found that the SAmfE is the most effective compatibilizer among the using compatibilizer types for PLA/PC blends. More... »

PAGES

1445-1451

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s12221-017-6671-4

DOI

http://dx.doi.org/10.1007/s12221-017-6671-4

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1092196412


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/03", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Chemical Sciences", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0303", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Macromolecular and Materials Chemistry", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Department of Chemical Engineering, Kocaeli University, Engineering Faculty, 41380, Kocaeli, Turkey", 
          "id": "http://www.grid.ac/institutes/grid.411105.0", 
          "name": [
            "Department of Chemical Engineering, Kocaeli University, Engineering Faculty, 41380, Kocaeli, Turkey"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Yemisci", 
        "givenName": "Fatma", 
        "id": "sg:person.07673733661.92", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07673733661.92"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Polymer Science and Technology, Kocaeli University, 41380, Kocaeli, Turkey", 
          "id": "http://www.grid.ac/institutes/grid.411105.0", 
          "name": [
            "Department of Chemical Engineering, Kocaeli University, Engineering Faculty, 41380, Kocaeli, Turkey", 
            "Department of Polymer Science and Technology, Kocaeli University, 41380, Kocaeli, Turkey"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Aytac", 
        "givenName": "Ayse", 
        "id": "sg:person.016365363244.79", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016365363244.79"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1007/s12221-013-1422-7", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1005414943", 
          "https://doi.org/10.1007/s12221-013-1422-7"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s00397-011-0538-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006464692", 
          "https://doi.org/10.1007/s00397-011-0538-1"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s12221-014-2607-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1043580640", 
          "https://doi.org/10.1007/s12221-014-2607-4"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2017-08", 
    "datePublishedReg": "2017-08-01", 
    "description": "In this study, PLA/PC blends were prepared in order to investigate the effects of the addition of PC loading level into PLA matrix on the mechanical properties of these blends. After that, PLA/PC (70/30), which has the lowest tensile strength value, was selected as a control sample for the compatibilization study. Commercial styrene-acrylic multi-functional-epoxide oligomeric agent (SAmfE), styrene maleic anhydride copolymer (SMA), tetrasilanol phenyl polyhedral oligomeric silsesquioxane (T-POSS) and glycidyl isooctyl-polyhedral oligomeric silsesquioxane (G-POSS) were used as compatibilizers for PLA/PC blends. The variation of mechanical, thermal, structural and morphological properties were examined by conducting tensile tests, dynamic mechanical analyses, differential scanning calorimetry, Fourier Transform IR and scanning electron microscope analyses. Tensile test results showed that the tensile strength and elongation at break values of the PLA/PC blend compatibilized with SAmfE were higher than those of the other blends. DSC analyses revealed that Tg and Tm values of the blends were not significantly affected by compatibilizer but, degree of crystallinity was found to be sensitive to compatibilizer type. DMA results showed that the best mechanical properties were obtained for the PLA/PC/SAmfE blend. When all of the results evaluated, it was found that the SAmfE is the most effective compatibilizer among the using compatibilizer types for PLA/PC blends.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s12221-017-6671-4", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136310", 
        "issn": [
          "1229-9197", 
          "1875-0052"
        ], 
        "name": "Fibers and Polymers", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "8", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "18"
      }
    ], 
    "keywords": [
      "PLA/PC blends", 
      "mechanical properties", 
      "PC blends", 
      "styrene-maleic anhydride copolymer", 
      "compatibilizer type", 
      "good mechanical properties", 
      "lower tensile strength values", 
      "tensile test results", 
      "tensile strength values", 
      "oligomeric silsesquioxane", 
      "dynamic mechanical analysis", 
      "scanning electron microscope analysis", 
      "different coupling agents", 
      "electron microscope analysis", 
      "PLA matrix", 
      "tensile tests", 
      "tensile strength", 
      "loading levels", 
      "phenyl polyhedral oligomeric silsesquioxane", 
      "polyhedral oligomeric silsesquioxane", 
      "mechanical analysis", 
      "DMA results", 
      "break values", 
      "degree of crystallinity", 
      "coupling agent", 
      "strength values", 
      "effective compatibilizer", 
      "maleic anhydride copolymer", 
      "compatibilizer", 
      "compatibilization study", 
      "morphological properties", 
      "blends", 
      "differential scanning calorimetry", 
      "microscope analysis", 
      "test results", 
      "anhydride copolymer", 
      "DSC analysis", 
      "scanning calorimetry", 
      "Fourier transform IR", 
      "silsesquioxane", 
      "properties", 
      "compatibilization", 
      "crystallinity", 
      "strength", 
      "elongation", 
      "matrix", 
      "results", 
      "control samples", 
      "calorimetry", 
      "values", 
      "copolymers", 
      "analysis", 
      "Tg", 
      "order", 
      "test", 
      "types", 
      "PC", 
      "variation", 
      "effect", 
      "addition", 
      "study", 
      "samples", 
      "Tm values", 
      "degree", 
      "agents", 
      "levels", 
      "IR"
    ], 
    "name": "Compatibilization of poly(lactic acid)/polycarbonate blends by different coupling agents", 
    "pagination": "1445-1451", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1092196412"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s12221-017-6671-4"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s12221-017-6671-4", 
      "https://app.dimensions.ai/details/publication/pub.1092196412"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2022-09-02T16:00", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20220902/entities/gbq_results/article/article_732.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s12221-017-6671-4"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s12221-017-6671-4'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s12221-017-6671-4'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s12221-017-6671-4'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s12221-017-6671-4'


 

This table displays all metadata directly associated to this object as RDF triples.

145 TRIPLES      21 PREDICATES      95 URIs      84 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s12221-017-6671-4 schema:about anzsrc-for:03
2 anzsrc-for:0303
3 schema:author Nd0110c261772441b8ae9ff4945de1252
4 schema:citation sg:pub.10.1007/s00397-011-0538-1
5 sg:pub.10.1007/s12221-013-1422-7
6 sg:pub.10.1007/s12221-014-2607-4
7 schema:datePublished 2017-08
8 schema:datePublishedReg 2017-08-01
9 schema:description In this study, PLA/PC blends were prepared in order to investigate the effects of the addition of PC loading level into PLA matrix on the mechanical properties of these blends. After that, PLA/PC (70/30), which has the lowest tensile strength value, was selected as a control sample for the compatibilization study. Commercial styrene-acrylic multi-functional-epoxide oligomeric agent (SAmfE), styrene maleic anhydride copolymer (SMA), tetrasilanol phenyl polyhedral oligomeric silsesquioxane (T-POSS) and glycidyl isooctyl-polyhedral oligomeric silsesquioxane (G-POSS) were used as compatibilizers for PLA/PC blends. The variation of mechanical, thermal, structural and morphological properties were examined by conducting tensile tests, dynamic mechanical analyses, differential scanning calorimetry, Fourier Transform IR and scanning electron microscope analyses. Tensile test results showed that the tensile strength and elongation at break values of the PLA/PC blend compatibilized with SAmfE were higher than those of the other blends. DSC analyses revealed that Tg and Tm values of the blends were not significantly affected by compatibilizer but, degree of crystallinity was found to be sensitive to compatibilizer type. DMA results showed that the best mechanical properties were obtained for the PLA/PC/SAmfE blend. When all of the results evaluated, it was found that the SAmfE is the most effective compatibilizer among the using compatibilizer types for PLA/PC blends.
10 schema:genre article
11 schema:isAccessibleForFree false
12 schema:isPartOf N24580016bbbc46abb84583b5047f1ad5
13 N329ca7a2d46145bb8727565f17b90e52
14 sg:journal.1136310
15 schema:keywords DMA results
16 DSC analysis
17 Fourier transform IR
18 IR
19 PC
20 PC blends
21 PLA matrix
22 PLA/PC blends
23 Tg
24 Tm values
25 addition
26 agents
27 analysis
28 anhydride copolymer
29 blends
30 break values
31 calorimetry
32 compatibilization
33 compatibilization study
34 compatibilizer
35 compatibilizer type
36 control samples
37 copolymers
38 coupling agent
39 crystallinity
40 degree
41 degree of crystallinity
42 different coupling agents
43 differential scanning calorimetry
44 dynamic mechanical analysis
45 effect
46 effective compatibilizer
47 electron microscope analysis
48 elongation
49 good mechanical properties
50 levels
51 loading levels
52 lower tensile strength values
53 maleic anhydride copolymer
54 matrix
55 mechanical analysis
56 mechanical properties
57 microscope analysis
58 morphological properties
59 oligomeric silsesquioxane
60 order
61 phenyl polyhedral oligomeric silsesquioxane
62 polyhedral oligomeric silsesquioxane
63 properties
64 results
65 samples
66 scanning calorimetry
67 scanning electron microscope analysis
68 silsesquioxane
69 strength
70 strength values
71 study
72 styrene-maleic anhydride copolymer
73 tensile strength
74 tensile strength values
75 tensile test results
76 tensile tests
77 test
78 test results
79 types
80 values
81 variation
82 schema:name Compatibilization of poly(lactic acid)/polycarbonate blends by different coupling agents
83 schema:pagination 1445-1451
84 schema:productId N7856b9efedd9462d9f24d1035bf8c59d
85 Nca5c6006f27c4d9bbffbea96e0dac071
86 schema:sameAs https://app.dimensions.ai/details/publication/pub.1092196412
87 https://doi.org/10.1007/s12221-017-6671-4
88 schema:sdDatePublished 2022-09-02T16:00
89 schema:sdLicense https://scigraph.springernature.com/explorer/license/
90 schema:sdPublisher Naca7f4c300be47f7a537f4c26dbac210
91 schema:url https://doi.org/10.1007/s12221-017-6671-4
92 sgo:license sg:explorer/license/
93 sgo:sdDataset articles
94 rdf:type schema:ScholarlyArticle
95 N24580016bbbc46abb84583b5047f1ad5 schema:volumeNumber 18
96 rdf:type schema:PublicationVolume
97 N329ca7a2d46145bb8727565f17b90e52 schema:issueNumber 8
98 rdf:type schema:PublicationIssue
99 N7856b9efedd9462d9f24d1035bf8c59d schema:name doi
100 schema:value 10.1007/s12221-017-6671-4
101 rdf:type schema:PropertyValue
102 Naca7f4c300be47f7a537f4c26dbac210 schema:name Springer Nature - SN SciGraph project
103 rdf:type schema:Organization
104 Nca5c6006f27c4d9bbffbea96e0dac071 schema:name dimensions_id
105 schema:value pub.1092196412
106 rdf:type schema:PropertyValue
107 Ncdd32253d8c24c12a3393e75a21a72b1 rdf:first sg:person.016365363244.79
108 rdf:rest rdf:nil
109 Nd0110c261772441b8ae9ff4945de1252 rdf:first sg:person.07673733661.92
110 rdf:rest Ncdd32253d8c24c12a3393e75a21a72b1
111 anzsrc-for:03 schema:inDefinedTermSet anzsrc-for:
112 schema:name Chemical Sciences
113 rdf:type schema:DefinedTerm
114 anzsrc-for:0303 schema:inDefinedTermSet anzsrc-for:
115 schema:name Macromolecular and Materials Chemistry
116 rdf:type schema:DefinedTerm
117 sg:journal.1136310 schema:issn 1229-9197
118 1875-0052
119 schema:name Fibers and Polymers
120 schema:publisher Springer Nature
121 rdf:type schema:Periodical
122 sg:person.016365363244.79 schema:affiliation grid-institutes:grid.411105.0
123 schema:familyName Aytac
124 schema:givenName Ayse
125 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016365363244.79
126 rdf:type schema:Person
127 sg:person.07673733661.92 schema:affiliation grid-institutes:grid.411105.0
128 schema:familyName Yemisci
129 schema:givenName Fatma
130 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07673733661.92
131 rdf:type schema:Person
132 sg:pub.10.1007/s00397-011-0538-1 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006464692
133 https://doi.org/10.1007/s00397-011-0538-1
134 rdf:type schema:CreativeWork
135 sg:pub.10.1007/s12221-013-1422-7 schema:sameAs https://app.dimensions.ai/details/publication/pub.1005414943
136 https://doi.org/10.1007/s12221-013-1422-7
137 rdf:type schema:CreativeWork
138 sg:pub.10.1007/s12221-014-2607-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1043580640
139 https://doi.org/10.1007/s12221-014-2607-4
140 rdf:type schema:CreativeWork
141 grid-institutes:grid.411105.0 schema:alternateName Department of Chemical Engineering, Kocaeli University, Engineering Faculty, 41380, Kocaeli, Turkey
142 Department of Polymer Science and Technology, Kocaeli University, 41380, Kocaeli, Turkey
143 schema:name Department of Chemical Engineering, Kocaeli University, Engineering Faculty, 41380, Kocaeli, Turkey
144 Department of Polymer Science and Technology, Kocaeli University, 41380, Kocaeli, Turkey
145 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...