ABSTRACTFailure analysis of liner plate of coke dry quenching chamber was carried out. Crack as well as thinning was observed in the failed plate. Chemical analysis revealed that the liner plate was made of AISI 310 stainless steel. A sample of failed plate was studied under SEM to understand the metallurgical changes. Results showed severe intergranular corrosion near the crack and at thinned region of the failed plate. EDS analysis revealed the formation of chromium carbides along the grain boundary. EDS result also showed the presence of sulfur at the corroded portion. Findings revealed that the plate failed due to intergranular corrosion at elevated temperature; the presence of sulfur compounds aggravated the rate of corrosion. More... »
PAGES697-700
http://scigraph.springernature.com/pub.10.1007/s11668-015-0001-1
DOIhttp://dx.doi.org/10.1007/s11668-015-0001-1
DIMENSIONShttps://app.dimensions.ai/details/publication/pub.1016175504
JSON-LD is the canonical representation for SciGraph data.
TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT
[
{
"@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json",
"about": [
{
"id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09",
"inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/",
"name": "Engineering",
"type": "DefinedTerm"
},
{
"id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912",
"inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/",
"name": "Materials Engineering",
"type": "DefinedTerm"
}
],
"author": [
{
"affiliation": {
"alternateName": "R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India",
"id": "http://www.grid.ac/institutes/grid.460003.1",
"name": [
"R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India"
],
"type": "Organization"
},
"familyName": "Mukhopadhyay",
"givenName": "Suman",
"id": "sg:person.07751146164.66",
"sameAs": [
"https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07751146164.66"
],
"type": "Person"
},
{
"affiliation": {
"alternateName": "R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India",
"id": "http://www.grid.ac/institutes/grid.460003.1",
"name": [
"R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India"
],
"type": "Organization"
},
"familyName": "Jugade",
"givenName": "Hrishikesh R.",
"id": "sg:person.014756156156.88",
"sameAs": [
"https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014756156156.88"
],
"type": "Person"
},
{
"affiliation": {
"alternateName": "R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India",
"id": "http://www.grid.ac/institutes/grid.460003.1",
"name": [
"R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India"
],
"type": "Organization"
},
"familyName": "Mukhopadhyay",
"givenName": "Goutam",
"id": "sg:person.012627373741.97",
"sameAs": [
"https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012627373741.97"
],
"type": "Person"
},
{
"affiliation": {
"alternateName": "R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India",
"id": "http://www.grid.ac/institutes/grid.460003.1",
"name": [
"R&D and Scientific Services, Tata Steel Limited, 831 001, Jamshedpur, India"
],
"type": "Organization"
},
"familyName": "Bhattacharyya",
"givenName": "Sandip",
"id": "sg:person.014376134625.96",
"sameAs": [
"https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014376134625.96"
],
"type": "Person"
}
],
"citation": [
{
"id": "sg:pub.10.1007/bf02652387",
"sameAs": [
"https://app.dimensions.ai/details/publication/pub.1009841603",
"https://doi.org/10.1007/bf02652387"
],
"type": "CreativeWork"
},
{
"id": "sg:pub.10.1007/bf02649264",
"sameAs": [
"https://app.dimensions.ai/details/publication/pub.1031136284",
"https://doi.org/10.1007/bf02649264"
],
"type": "CreativeWork"
}
],
"datePublished": "2015-08-14",
"datePublishedReg": "2015-08-14",
"description": "Failure analysis of liner plate of coke dry quenching chamber was carried out. Crack as well as thinning was observed in the failed plate. Chemical analysis revealed that the liner plate was made of AISI 310 stainless steel. A sample of failed plate was studied under SEM to understand the metallurgical changes. Results showed severe intergranular corrosion near the crack and at thinned region of the failed plate. EDS analysis revealed the formation of chromium carbides along the grain boundary. EDS result also showed the presence of sulfur at the corroded portion. Findings revealed that the plate failed due to intergranular corrosion at elevated temperature; the presence of sulfur compounds aggravated the rate of corrosion.",
"genre": "article",
"id": "sg:pub.10.1007/s11668-015-0001-1",
"inLanguage": "en",
"isAccessibleForFree": false,
"isPartOf": [
{
"id": "sg:journal.1136274",
"issn": [
"1529-8159",
"1547-7029"
],
"name": "Journal of Failure Analysis and Prevention",
"publisher": "Springer Nature",
"type": "Periodical"
},
{
"issueNumber": "5",
"type": "PublicationIssue"
},
{
"type": "PublicationVolume",
"volumeNumber": "15"
}
],
"keywords": [
"liner plate",
"intergranular corrosion",
"failure analysis",
"AISI 310 stainless steel",
"severe intergranular corrosion",
"rate of corrosion",
"metallurgical changes",
"quenching chamber",
"stainless steel",
"chromium carbide",
"AISI 310",
"grain boundaries",
"corrosion",
"EDS analysis",
"elevated temperatures",
"presence of sulfur",
"plate",
"steel",
"cracks",
"carbide",
"EDS",
"chamber",
"SEM",
"sulfur compounds",
"temperature",
"chemical analysis",
"boundaries",
"analysis",
"sulfur",
"formation",
"thinning",
"results",
"rate",
"presence",
"samples",
"region",
"portion",
"changes",
"compounds",
"findings"
],
"name": "Failure Analysis of the Liner Plate of CDQ Chamber Made of AISI 310",
"pagination": "697-700",
"productId": [
{
"name": "dimensions_id",
"type": "PropertyValue",
"value": [
"pub.1016175504"
]
},
{
"name": "doi",
"type": "PropertyValue",
"value": [
"10.1007/s11668-015-0001-1"
]
}
],
"sameAs": [
"https://doi.org/10.1007/s11668-015-0001-1",
"https://app.dimensions.ai/details/publication/pub.1016175504"
],
"sdDataset": "articles",
"sdDatePublished": "2022-05-20T07:31",
"sdLicense": "https://scigraph.springernature.com/explorer/license/",
"sdPublisher": {
"name": "Springer Nature - SN SciGraph project",
"type": "Organization"
},
"sdSource": "s3://com-springernature-scigraph/baseset/20220519/entities/gbq_results/article/article_673.jsonl",
"type": "ScholarlyArticle",
"url": "https://doi.org/10.1007/s11668-015-0001-1"
}
]Download the RDF metadata as: json-ld nt turtle xml License info
JSON-LD is a popular format for linked data which is fully compatible with JSON.
curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11668-015-0001-1'
N-Triples is a line-based linked data format ideal for batch operations.
curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11668-015-0001-1'
Turtle is a human-readable linked data format.
curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11668-015-0001-1'
RDF/XML is a standard XML format for linked data.
curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11668-015-0001-1'
This table displays all metadata directly associated to this object as RDF triples.
127 TRIPLES
22 PREDICATES
67 URIs
57 LITERALS
6 BLANK NODES