Failure Analysis of a Cylindrical Roller Bearing from a Rolling Mill View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2011-03-23

AUTHORS

Goutam Mukhopadhyay, S. Bhattacharya

ABSTRACT

Premature failure of a cylindrical roller bearing of a gear box input shaft from a hot strip mill has been investigated. The pins of the cylindrical rollers of the bearing broke from the welded joints at their ends on the cage ring. Investigations were carried out on the failed roller pin and the welded joint. The investigation consists of visual observation, chemical analysis, characterization of macro- and microstructures, measurement of hardness profile, fractography, and energy dispersive spectroscopy (EDS). The fracture surface of the roller pins exhibits beach marks. Scanning electron microscopy (SEM) of the fracture surfaces reveals striations suggesting fatigue failure. The measured hardness profile along the welded joint shows very high hardness due to the presence of untempered martensite at the fusion boundary as revealed by the microstructural examination. Analyses of the results infer that the roller pins failed by the initiation of fatigue cracks from the welded joint because of the presence of untempered martensite originated due to improper welding process. More... »

PAGES

337-343

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s11668-011-9450-3

DOI

http://dx.doi.org/10.1007/s11668-011-9450-3

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1050488752


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India", 
          "id": "http://www.grid.ac/institutes/grid.460003.1", 
          "name": [
            "Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Mukhopadhyay", 
        "givenName": "Goutam", 
        "id": "sg:person.012627373741.97", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012627373741.97"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India", 
          "id": "http://www.grid.ac/institutes/grid.460003.1", 
          "name": [
            "Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bhattacharya", 
        "givenName": "S.", 
        "id": "sg:person.012650042437.43", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012650042437.43"
        ], 
        "type": "Person"
      }
    ], 
    "datePublished": "2011-03-23", 
    "datePublishedReg": "2011-03-23", 
    "description": "Premature failure of a cylindrical roller bearing of a gear box input shaft from a hot strip mill has been investigated. The pins of the cylindrical rollers of the bearing broke from the welded joints at their ends on the cage ring. Investigations were carried out on the failed roller pin and the welded joint. The investigation consists of visual observation, chemical analysis, characterization of macro- and microstructures, measurement of hardness profile, fractography, and energy dispersive spectroscopy (EDS). The fracture surface of the roller pins exhibits beach marks. Scanning electron microscopy (SEM) of the fracture surfaces reveals striations suggesting fatigue failure. The measured hardness profile along the welded joint shows very high hardness due to the presence of untempered martensite at the fusion boundary as revealed by the microstructural examination. Analyses of the results infer that the roller pins failed by the initiation of fatigue cracks from the welded joint because of the presence of untempered martensite originated due to improper welding process.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s11668-011-9450-3", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136274", 
        "issn": [
          "1529-8159", 
          "1547-7029"
        ], 
        "name": "Journal of Failure Analysis and Prevention", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "4", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "11"
      }
    ], 
    "keywords": [
      "cylindrical roller bearing", 
      "energy dispersive spectroscopy", 
      "fracture surfaces", 
      "untempered martensite", 
      "hardness profile", 
      "roller bearings", 
      "hot strip mill", 
      "measured hardness profile", 
      "welded joints", 
      "welding process", 
      "beach marks", 
      "fatigue cracks", 
      "strip mill", 
      "fatigue failure", 
      "rolling mill", 
      "high hardness", 
      "microstructural examination", 
      "premature failure", 
      "characterization of macro", 
      "failure analysis", 
      "cylindrical rollers", 
      "input shaft", 
      "dispersive spectroscopy", 
      "pin", 
      "martensite", 
      "electron microscopy", 
      "bearing", 
      "mill", 
      "visual observation", 
      "fractography", 
      "surface", 
      "joints", 
      "cracks", 
      "microstructure", 
      "roller", 
      "hardness", 
      "shaft", 
      "chemical analysis", 
      "investigation", 
      "microscopy", 
      "striations", 
      "measurements", 
      "spectroscopy", 
      "failure", 
      "profile", 
      "process", 
      "analysis", 
      "characterization", 
      "macro", 
      "results", 
      "presence", 
      "observations", 
      "fusion", 
      "end", 
      "initiation", 
      "ring", 
      "marks", 
      "examination"
    ], 
    "name": "Failure Analysis of a Cylindrical Roller Bearing from a Rolling Mill", 
    "pagination": "337-343", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1050488752"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s11668-011-9450-3"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s11668-011-9450-3", 
      "https://app.dimensions.ai/details/publication/pub.1050488752"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2022-05-20T07:27", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20220519/entities/gbq_results/article/article_546.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s11668-011-9450-3"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11668-011-9450-3'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11668-011-9450-3'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11668-011-9450-3'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11668-011-9450-3'


 

This table displays all metadata directly associated to this object as RDF triples.

123 TRIPLES      21 PREDICATES      83 URIs      75 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s11668-011-9450-3 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author N0622f1222377431bb9b039e430f77733
4 schema:datePublished 2011-03-23
5 schema:datePublishedReg 2011-03-23
6 schema:description Premature failure of a cylindrical roller bearing of a gear box input shaft from a hot strip mill has been investigated. The pins of the cylindrical rollers of the bearing broke from the welded joints at their ends on the cage ring. Investigations were carried out on the failed roller pin and the welded joint. The investigation consists of visual observation, chemical analysis, characterization of macro- and microstructures, measurement of hardness profile, fractography, and energy dispersive spectroscopy (EDS). The fracture surface of the roller pins exhibits beach marks. Scanning electron microscopy (SEM) of the fracture surfaces reveals striations suggesting fatigue failure. The measured hardness profile along the welded joint shows very high hardness due to the presence of untempered martensite at the fusion boundary as revealed by the microstructural examination. Analyses of the results infer that the roller pins failed by the initiation of fatigue cracks from the welded joint because of the presence of untempered martensite originated due to improper welding process.
7 schema:genre article
8 schema:inLanguage en
9 schema:isAccessibleForFree false
10 schema:isPartOf N53abbeebf08e43539f26f3f03190369c
11 N9b90e6e0381f4514b649a3d14466fcd1
12 sg:journal.1136274
13 schema:keywords analysis
14 beach marks
15 bearing
16 characterization
17 characterization of macro
18 chemical analysis
19 cracks
20 cylindrical roller bearing
21 cylindrical rollers
22 dispersive spectroscopy
23 electron microscopy
24 end
25 energy dispersive spectroscopy
26 examination
27 failure
28 failure analysis
29 fatigue cracks
30 fatigue failure
31 fractography
32 fracture surfaces
33 fusion
34 hardness
35 hardness profile
36 high hardness
37 hot strip mill
38 initiation
39 input shaft
40 investigation
41 joints
42 macro
43 marks
44 martensite
45 measured hardness profile
46 measurements
47 microscopy
48 microstructural examination
49 microstructure
50 mill
51 observations
52 pin
53 premature failure
54 presence
55 process
56 profile
57 results
58 ring
59 roller
60 roller bearings
61 rolling mill
62 shaft
63 spectroscopy
64 striations
65 strip mill
66 surface
67 untempered martensite
68 visual observation
69 welded joints
70 welding process
71 schema:name Failure Analysis of a Cylindrical Roller Bearing from a Rolling Mill
72 schema:pagination 337-343
73 schema:productId N7a3adb9b75e94492aab2a09c22b55f00
74 Nd0c1e5bf10494e2e8a3c4639e9a99c2e
75 schema:sameAs https://app.dimensions.ai/details/publication/pub.1050488752
76 https://doi.org/10.1007/s11668-011-9450-3
77 schema:sdDatePublished 2022-05-20T07:27
78 schema:sdLicense https://scigraph.springernature.com/explorer/license/
79 schema:sdPublisher N8912761c86594d8bb692d1ddf6acba01
80 schema:url https://doi.org/10.1007/s11668-011-9450-3
81 sgo:license sg:explorer/license/
82 sgo:sdDataset articles
83 rdf:type schema:ScholarlyArticle
84 N0622f1222377431bb9b039e430f77733 rdf:first sg:person.012627373741.97
85 rdf:rest N199e5e94a08b4860b6b0d14d90090caa
86 N199e5e94a08b4860b6b0d14d90090caa rdf:first sg:person.012650042437.43
87 rdf:rest rdf:nil
88 N53abbeebf08e43539f26f3f03190369c schema:volumeNumber 11
89 rdf:type schema:PublicationVolume
90 N7a3adb9b75e94492aab2a09c22b55f00 schema:name dimensions_id
91 schema:value pub.1050488752
92 rdf:type schema:PropertyValue
93 N8912761c86594d8bb692d1ddf6acba01 schema:name Springer Nature - SN SciGraph project
94 rdf:type schema:Organization
95 N9b90e6e0381f4514b649a3d14466fcd1 schema:issueNumber 4
96 rdf:type schema:PublicationIssue
97 Nd0c1e5bf10494e2e8a3c4639e9a99c2e schema:name doi
98 schema:value 10.1007/s11668-011-9450-3
99 rdf:type schema:PropertyValue
100 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
101 schema:name Engineering
102 rdf:type schema:DefinedTerm
103 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
104 schema:name Materials Engineering
105 rdf:type schema:DefinedTerm
106 sg:journal.1136274 schema:issn 1529-8159
107 1547-7029
108 schema:name Journal of Failure Analysis and Prevention
109 schema:publisher Springer Nature
110 rdf:type schema:Periodical
111 sg:person.012627373741.97 schema:affiliation grid-institutes:grid.460003.1
112 schema:familyName Mukhopadhyay
113 schema:givenName Goutam
114 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012627373741.97
115 rdf:type schema:Person
116 sg:person.012650042437.43 schema:affiliation grid-institutes:grid.460003.1
117 schema:familyName Bhattacharya
118 schema:givenName S.
119 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012650042437.43
120 rdf:type schema:Person
121 grid-institutes:grid.460003.1 schema:alternateName Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India
122 schema:name Metallurgical Laboratories and QA Group, R&D and Scientific Services, Tata Steel Ltd., 831001, Jamshedpur, India
123 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...