Magnetic and Mechanical Properties of Iron-Based Soft Magnetic Composites Coated with Silane Synergized by Bi2O3 View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2021-02-07

AUTHORS

Wangchang Li, Wanjia Li, Yao Ying, Jing Yu, Jingwu Zheng, Liang Qiao, Juan Li, Lingxiang Zhang, Lun Fan, Naoki Wakiya, Hisao Suzuki, Daxin Bao, Shenglei Che

ABSTRACT

Fe-based soft magnetic composites (SMCs) co-coated with Bi2O3 and silane, used as the low melting point binder and the insulating layer, respectively, were successfully prepared. The SMCs show improved mechanical strength, thermal stability, and insulation compared to other soft magnetic composite materials. The obtained SMCs exhibit a high Bm of 1.2607 T at 5000 A/m, 50 Hz, a high μmax of 497, and a low Pcm of 81.8 W/kg at 50 kHz and 50 mT for a completely homogeneous thin insulating coating. In addition, the transverse rupture strength of such materials is up to 81.2 MPa, which is extremely important for high-speed motors. Furthermore, the permeability and magnetic loss are stable under stress. Nonlinear curve fitting was used to build the loss model and then separated into the hysteresis loss, the eddy current loss, and the excess loss. The loss mechanism of SMCs with different coatings and micro-stress was explored and verified via this model. When compared to traditional SMCs, this material coated with Bi2O3 and silane shows a lower loss and a higher transverse rupture strength. This research expands the application fields of iron-based SMCs, especially in practical applications of soft magnetic components in high-speed motors. More... »

PAGES

2425-2435

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s11664-021-08758-2

DOI

http://dx.doi.org/10.1007/s11664-021-08758-2

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1135200183


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Li", 
        "givenName": "Wangchang", 
        "id": "sg:person.011717237000.43", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011717237000.43"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Li", 
        "givenName": "Wanjia", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Ying", 
        "givenName": "Yao", 
        "id": "sg:person.010652267212.18", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010652267212.18"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Yu", 
        "givenName": "Jing", 
        "id": "sg:person.0741775210.02", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0741775210.02"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Zheng", 
        "givenName": "Jingwu", 
        "id": "sg:person.016222577167.89", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016222577167.89"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Qiao", 
        "givenName": "Liang", 
        "id": "sg:person.015321332757.79", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015321332757.79"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Li", 
        "givenName": "Juan", 
        "id": "sg:person.014563457303.27", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014563457303.27"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Zhang", 
        "givenName": "Lingxiang", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Fan", 
        "givenName": "Lun", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan", 
          "id": "http://www.grid.ac/institutes/grid.263536.7", 
          "name": [
            "Research Institute of Electronics, Shizuoka University, Hamamatsu, Japan", 
            "Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Wakiya", 
        "givenName": "Naoki", 
        "id": "sg:person.012174254311.31", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012174254311.31"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan", 
          "id": "http://www.grid.ac/institutes/grid.263536.7", 
          "name": [
            "Research Institute of Electronics, Shizuoka University, Hamamatsu, Japan", 
            "Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Suzuki", 
        "givenName": "Hisao", 
        "id": "sg:person.012175043001.45", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012175043001.45"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Hengdian Group DMEGC Magnetics Co., Ltd, 322118, Dongyang, China", 
          "id": "http://www.grid.ac/institutes/grid.509132.c", 
          "name": [
            "Hengdian Group DMEGC Magnetics Co., Ltd, 322118, Dongyang, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bao", 
        "givenName": "Daxin", 
        "id": "sg:person.014550131007.54", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014550131007.54"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China", 
          "id": "http://www.grid.ac/institutes/grid.469325.f", 
          "name": [
            "College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China", 
            "Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Che", 
        "givenName": "Shenglei", 
        "id": "sg:person.011030555205.15", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011030555205.15"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1007/s10853-017-0941-9", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1084027273", 
          "https://doi.org/10.1007/s10853-017-0941-9"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11665-018-3759-y", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1109916060", 
          "https://doi.org/10.1007/s11665-018-3759-y"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s10948-013-2249-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006699588", 
          "https://doi.org/10.1007/s10948-013-2249-6"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2021-02-07", 
    "datePublishedReg": "2021-02-07", 
    "description": "Fe-based soft magnetic composites (SMCs) co-coated with Bi2O3 and silane, used as the low melting point binder and the insulating layer, respectively, were successfully prepared. The SMCs show improved mechanical strength, thermal stability, and insulation compared to other soft magnetic composite materials. The obtained SMCs exhibit a high Bm of 1.2607 T at 5000 A/m, 50 Hz, a high \u03bcmax of 497, and a low Pcm of 81.8 W/kg at 50 kHz and 50 mT for a completely homogeneous thin insulating coating. In addition, the transverse rupture strength of such materials is up to 81.2 MPa, which is extremely important for high-speed motors. Furthermore, the permeability and magnetic loss are stable under stress. Nonlinear curve fitting was used to build the loss model and then separated into the hysteresis loss, the eddy current loss, and the excess loss. The loss mechanism of SMCs with different coatings and micro-stress was explored and verified via this model. When compared to traditional SMCs, this material coated with Bi2O3 and silane shows a lower loss and a higher transverse rupture strength. This research expands the application fields of iron-based SMCs, especially in practical applications of soft magnetic components in high-speed motors.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s11664-021-08758-2", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isFundedItemOf": [
      {
        "id": "sg:grant.8891740", 
        "type": "MonetaryGrant"
      }
    ], 
    "isPartOf": [
      {
        "id": "sg:journal.1136213", 
        "issn": [
          "0361-5235", 
          "1543-186X"
        ], 
        "name": "Journal of Electronic Materials", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "4", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "50"
      }
    ], 
    "keywords": [
      "soft magnetic composites", 
      "transverse rupture strength", 
      "high-speed motor", 
      "magnetic composites", 
      "rupture strength", 
      "high transverse rupture strength", 
      "iron-based soft magnetic composites", 
      "soft magnetic composite material", 
      "magnetic composite material", 
      "thin insulating coating", 
      "eddy current loss", 
      "soft magnetic components", 
      "composite materials", 
      "insulating coating", 
      "mechanical properties", 
      "mechanical strength", 
      "lower PCM", 
      "insulating layer", 
      "magnetic loss", 
      "current loss", 
      "different coatings", 
      "hysteresis loss", 
      "low loss", 
      "such materials", 
      "thermal stability", 
      "magnetic components", 
      "composites", 
      "loss mechanisms", 
      "coatings", 
      "application fields", 
      "Bi2O3", 
      "excess loss", 
      "loss model", 
      "practical applications", 
      "nonlinear curve fitting", 
      "silane", 
      "strength", 
      "materials", 
      "motor", 
      "curve fitting", 
      "insulation", 
      "MPa", 
      "binder", 
      "PCM", 
      "highest \u03bcmax", 
      "layer", 
      "Hz", 
      "permeability", 
      "stability", 
      "properties", 
      "model", 
      "Fe", 
      "applications", 
      "\u03bcmax", 
      "loss", 
      "stress", 
      "iron", 
      "field", 
      "fitting", 
      "SMC show", 
      "higher BM", 
      "components", 
      "exhibit", 
      "show", 
      "SMCs exhibit", 
      "addition", 
      "mechanism", 
      "research", 
      "BM", 
      "low melting point binder", 
      "melting point binder", 
      "point binder", 
      "homogeneous thin insulating coating", 
      "traditional SMCs", 
      "Silane Synergized", 
      "Synergized"
    ], 
    "name": "Magnetic and Mechanical Properties of Iron-Based Soft Magnetic Composites Coated with Silane Synergized by Bi2O3", 
    "pagination": "2425-2435", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1135200183"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s11664-021-08758-2"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s11664-021-08758-2", 
      "https://app.dimensions.ai/details/publication/pub.1135200183"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2022-01-01T18:59", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20220101/entities/gbq_results/article/article_882.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s11664-021-08758-2"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11664-021-08758-2'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11664-021-08758-2'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11664-021-08758-2'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11664-021-08758-2'


 

This table displays all metadata directly associated to this object as RDF triples.

237 TRIPLES      22 PREDICATES      104 URIs      93 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s11664-021-08758-2 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author N92d4a12c3ab24497ac77927d56f7cffd
4 schema:citation sg:pub.10.1007/s10853-017-0941-9
5 sg:pub.10.1007/s10948-013-2249-6
6 sg:pub.10.1007/s11665-018-3759-y
7 schema:datePublished 2021-02-07
8 schema:datePublishedReg 2021-02-07
9 schema:description Fe-based soft magnetic composites (SMCs) co-coated with Bi2O3 and silane, used as the low melting point binder and the insulating layer, respectively, were successfully prepared. The SMCs show improved mechanical strength, thermal stability, and insulation compared to other soft magnetic composite materials. The obtained SMCs exhibit a high Bm of 1.2607 T at 5000 A/m, 50 Hz, a high μmax of 497, and a low Pcm of 81.8 W/kg at 50 kHz and 50 mT for a completely homogeneous thin insulating coating. In addition, the transverse rupture strength of such materials is up to 81.2 MPa, which is extremely important for high-speed motors. Furthermore, the permeability and magnetic loss are stable under stress. Nonlinear curve fitting was used to build the loss model and then separated into the hysteresis loss, the eddy current loss, and the excess loss. The loss mechanism of SMCs with different coatings and micro-stress was explored and verified via this model. When compared to traditional SMCs, this material coated with Bi2O3 and silane shows a lower loss and a higher transverse rupture strength. This research expands the application fields of iron-based SMCs, especially in practical applications of soft magnetic components in high-speed motors.
10 schema:genre article
11 schema:inLanguage en
12 schema:isAccessibleForFree false
13 schema:isPartOf N2b9020ef639a4c5f8f1e731705d43887
14 Ne8e4952b61d54a78b54f3916ffe21c46
15 sg:journal.1136213
16 schema:keywords BM
17 Bi2O3
18 Fe
19 Hz
20 MPa
21 PCM
22 SMC show
23 SMCs exhibit
24 Silane Synergized
25 Synergized
26 addition
27 application fields
28 applications
29 binder
30 coatings
31 components
32 composite materials
33 composites
34 current loss
35 curve fitting
36 different coatings
37 eddy current loss
38 excess loss
39 exhibit
40 field
41 fitting
42 high transverse rupture strength
43 high-speed motor
44 higher BM
45 highest μmax
46 homogeneous thin insulating coating
47 hysteresis loss
48 insulating coating
49 insulating layer
50 insulation
51 iron
52 iron-based soft magnetic composites
53 layer
54 loss
55 loss mechanisms
56 loss model
57 low loss
58 low melting point binder
59 lower PCM
60 magnetic components
61 magnetic composite material
62 magnetic composites
63 magnetic loss
64 materials
65 mechanical properties
66 mechanical strength
67 mechanism
68 melting point binder
69 model
70 motor
71 nonlinear curve fitting
72 permeability
73 point binder
74 practical applications
75 properties
76 research
77 rupture strength
78 show
79 silane
80 soft magnetic components
81 soft magnetic composite material
82 soft magnetic composites
83 stability
84 strength
85 stress
86 such materials
87 thermal stability
88 thin insulating coating
89 traditional SMCs
90 transverse rupture strength
91 μmax
92 schema:name Magnetic and Mechanical Properties of Iron-Based Soft Magnetic Composites Coated with Silane Synergized by Bi2O3
93 schema:pagination 2425-2435
94 schema:productId N5e63ebf178364c1c8c5b72121d0be3e4
95 Nb40d4e8eb71f4a18ba9f99bd3564777f
96 schema:sameAs https://app.dimensions.ai/details/publication/pub.1135200183
97 https://doi.org/10.1007/s11664-021-08758-2
98 schema:sdDatePublished 2022-01-01T18:59
99 schema:sdLicense https://scigraph.springernature.com/explorer/license/
100 schema:sdPublisher Nf5aa857470754bfb87f8ffeb5af1e5cb
101 schema:url https://doi.org/10.1007/s11664-021-08758-2
102 sgo:license sg:explorer/license/
103 sgo:sdDataset articles
104 rdf:type schema:ScholarlyArticle
105 N063462419f474bbea533511414cfbaf7 rdf:first N56cb4bd2e1854252bd42f1d56ab2cc23
106 rdf:rest N7ac34a11c9194df39c1432d396912ba3
107 N1960a09c9c614aec8fd0680e1fda767b rdf:first sg:person.010652267212.18
108 rdf:rest N59e9d3068dc94d18bca12772fdb1d9ee
109 N1a24a083159541d7afc3c3581e643fe8 rdf:first N68504395eaab4fa9a7f3e6254e405e68
110 rdf:rest N1960a09c9c614aec8fd0680e1fda767b
111 N2b9020ef639a4c5f8f1e731705d43887 schema:volumeNumber 50
112 rdf:type schema:PublicationVolume
113 N354de9aac4d649afacbd44aa859f3d36 rdf:first sg:person.016222577167.89
114 rdf:rest Nf28f5550952646b4a831932ee75dc338
115 N40e5ff6f7858424986d250b04a9b05c6 schema:affiliation grid-institutes:grid.469325.f
116 schema:familyName Fan
117 schema:givenName Lun
118 rdf:type schema:Person
119 N56cb4bd2e1854252bd42f1d56ab2cc23 schema:affiliation grid-institutes:grid.469325.f
120 schema:familyName Zhang
121 schema:givenName Lingxiang
122 rdf:type schema:Person
123 N59e9d3068dc94d18bca12772fdb1d9ee rdf:first sg:person.0741775210.02
124 rdf:rest N354de9aac4d649afacbd44aa859f3d36
125 N5cb2910ebb074080b2f6d6df0edc2eaa rdf:first sg:person.012175043001.45
126 rdf:rest N6710d1dda1bc4b04bd5caf5ec64cb5b3
127 N5e63ebf178364c1c8c5b72121d0be3e4 schema:name doi
128 schema:value 10.1007/s11664-021-08758-2
129 rdf:type schema:PropertyValue
130 N6710d1dda1bc4b04bd5caf5ec64cb5b3 rdf:first sg:person.014550131007.54
131 rdf:rest Nbe096bb4480845e2b00f86ccb0d2f2d0
132 N68504395eaab4fa9a7f3e6254e405e68 schema:affiliation grid-institutes:grid.469325.f
133 schema:familyName Li
134 schema:givenName Wanjia
135 rdf:type schema:Person
136 N74f690037ea249e49426db1767c0cf9b rdf:first sg:person.014563457303.27
137 rdf:rest N063462419f474bbea533511414cfbaf7
138 N7ac34a11c9194df39c1432d396912ba3 rdf:first N40e5ff6f7858424986d250b04a9b05c6
139 rdf:rest N97498f8ab6994a56b5e0ea3e4c2aee80
140 N92d4a12c3ab24497ac77927d56f7cffd rdf:first sg:person.011717237000.43
141 rdf:rest N1a24a083159541d7afc3c3581e643fe8
142 N97498f8ab6994a56b5e0ea3e4c2aee80 rdf:first sg:person.012174254311.31
143 rdf:rest N5cb2910ebb074080b2f6d6df0edc2eaa
144 Nb40d4e8eb71f4a18ba9f99bd3564777f schema:name dimensions_id
145 schema:value pub.1135200183
146 rdf:type schema:PropertyValue
147 Nbe096bb4480845e2b00f86ccb0d2f2d0 rdf:first sg:person.011030555205.15
148 rdf:rest rdf:nil
149 Ne8e4952b61d54a78b54f3916ffe21c46 schema:issueNumber 4
150 rdf:type schema:PublicationIssue
151 Nf28f5550952646b4a831932ee75dc338 rdf:first sg:person.015321332757.79
152 rdf:rest N74f690037ea249e49426db1767c0cf9b
153 Nf5aa857470754bfb87f8ffeb5af1e5cb schema:name Springer Nature - SN SciGraph project
154 rdf:type schema:Organization
155 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
156 schema:name Engineering
157 rdf:type schema:DefinedTerm
158 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
159 schema:name Materials Engineering
160 rdf:type schema:DefinedTerm
161 sg:grant.8891740 http://pending.schema.org/fundedItem sg:pub.10.1007/s11664-021-08758-2
162 rdf:type schema:MonetaryGrant
163 sg:journal.1136213 schema:issn 0361-5235
164 1543-186X
165 schema:name Journal of Electronic Materials
166 schema:publisher Springer Nature
167 rdf:type schema:Periodical
168 sg:person.010652267212.18 schema:affiliation grid-institutes:grid.469325.f
169 schema:familyName Ying
170 schema:givenName Yao
171 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010652267212.18
172 rdf:type schema:Person
173 sg:person.011030555205.15 schema:affiliation grid-institutes:grid.469325.f
174 schema:familyName Che
175 schema:givenName Shenglei
176 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011030555205.15
177 rdf:type schema:Person
178 sg:person.011717237000.43 schema:affiliation grid-institutes:grid.469325.f
179 schema:familyName Li
180 schema:givenName Wangchang
181 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011717237000.43
182 rdf:type schema:Person
183 sg:person.012174254311.31 schema:affiliation grid-institutes:grid.263536.7
184 schema:familyName Wakiya
185 schema:givenName Naoki
186 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012174254311.31
187 rdf:type schema:Person
188 sg:person.012175043001.45 schema:affiliation grid-institutes:grid.263536.7
189 schema:familyName Suzuki
190 schema:givenName Hisao
191 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012175043001.45
192 rdf:type schema:Person
193 sg:person.014550131007.54 schema:affiliation grid-institutes:grid.509132.c
194 schema:familyName Bao
195 schema:givenName Daxin
196 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014550131007.54
197 rdf:type schema:Person
198 sg:person.014563457303.27 schema:affiliation grid-institutes:grid.469325.f
199 schema:familyName Li
200 schema:givenName Juan
201 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014563457303.27
202 rdf:type schema:Person
203 sg:person.015321332757.79 schema:affiliation grid-institutes:grid.469325.f
204 schema:familyName Qiao
205 schema:givenName Liang
206 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015321332757.79
207 rdf:type schema:Person
208 sg:person.016222577167.89 schema:affiliation grid-institutes:grid.469325.f
209 schema:familyName Zheng
210 schema:givenName Jingwu
211 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016222577167.89
212 rdf:type schema:Person
213 sg:person.0741775210.02 schema:affiliation grid-institutes:grid.469325.f
214 schema:familyName Yu
215 schema:givenName Jing
216 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0741775210.02
217 rdf:type schema:Person
218 sg:pub.10.1007/s10853-017-0941-9 schema:sameAs https://app.dimensions.ai/details/publication/pub.1084027273
219 https://doi.org/10.1007/s10853-017-0941-9
220 rdf:type schema:CreativeWork
221 sg:pub.10.1007/s10948-013-2249-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006699588
222 https://doi.org/10.1007/s10948-013-2249-6
223 rdf:type schema:CreativeWork
224 sg:pub.10.1007/s11665-018-3759-y schema:sameAs https://app.dimensions.ai/details/publication/pub.1109916060
225 https://doi.org/10.1007/s11665-018-3759-y
226 rdf:type schema:CreativeWork
227 grid-institutes:grid.263536.7 schema:alternateName Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan
228 schema:name Department of Electronics and Materials Science, Shizuoka University, Hamamatsu, Japan
229 Research Institute of Electronics, Shizuoka University, Hamamatsu, Japan
230 rdf:type schema:Organization
231 grid-institutes:grid.469325.f schema:alternateName Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China
232 schema:name College of Materials Science and Engineering, Zhejiang University of Technology, 310014, Hangzhou, China
233 Research Center for Magnetic and Electronic Materials, Zhejiang University of Technology, 310014, Hangzhou, China
234 rdf:type schema:Organization
235 grid-institutes:grid.509132.c schema:alternateName Hengdian Group DMEGC Magnetics Co., Ltd, 322118, Dongyang, China
236 schema:name Hengdian Group DMEGC Magnetics Co., Ltd, 322118, Dongyang, China
237 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...