Effect of Firing Temperature and Reducing Gas Composition during Low-Temperature Reduction of Nanocrystalline Fe2O3 View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2007-02-16

AUTHORS

M. BAHGAT, M.H. KHEDR, M.I. NASR, E.K. SEDEEK

ABSTRACT

Pure nanocrystalline hematite (40 to 100 nm) compacts were prepared and sintered at various temperatures (300 °C to 600 °C) and then reduced with 100 pct H2 at 500 °C. On the other hand, fired compacts at 500 °C were reduced with a H2-Ar gas mixture containing different concentration of hydrogen (100, 75, 50, and 25 pct) at 500 °C using thermogravimetric techniques. Nanocrystalline Fe2O3 compacts were characterized before and after reduction with X-ray diffraction, scanning electron microscopy (SEM), vibrating sample magnetometer (VSM), and reflected light microscope. It was found that the fired compacts at 400 °C to 600 °C have relatively faster reaction behaviors compared to that at lower firing temperature 300 °C. By decreasing the firing temperature to 300 °C, partial sintering with grain growth was observed clearly during reduction. Also, it was found that the reduction rate increased with increasing hydrogen content in the reducing gas. Comparatively, grain growth and partial coalescence took place during reduction with 25 pct H2 due to long reaction time. More... »

PAGES

5-11

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s11663-006-9002-5

DOI

http://dx.doi.org/10.1007/s11663-006-9002-5

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1010343115


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt", 
          "id": "http://www.grid.ac/institutes/grid.470969.5", 
          "name": [
            "Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt"
          ], 
          "type": "Organization"
        }, 
        "familyName": "BAHGAT", 
        "givenName": "M.", 
        "id": "sg:person.011313225416.52", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011313225416.52"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Benisuef University, Benisuef, Cairo, Egypt", 
          "id": "http://www.grid.ac/institutes/grid.411662.6", 
          "name": [
            "Benisuef University, Benisuef, Cairo, Egypt"
          ], 
          "type": "Organization"
        }, 
        "familyName": "KHEDR", 
        "givenName": "M.H.", 
        "id": "sg:person.015333711045.11", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015333711045.11"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt", 
          "id": "http://www.grid.ac/institutes/grid.470969.5", 
          "name": [
            "Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt"
          ], 
          "type": "Organization"
        }, 
        "familyName": "NASR", 
        "givenName": "M.I.", 
        "id": "sg:person.010714632367.52", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010714632367.52"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Benisuef University, Benisuef, Cairo, Egypt", 
          "id": "http://www.grid.ac/institutes/grid.411662.6", 
          "name": [
            "Benisuef University, Benisuef, Cairo, Egypt"
          ], 
          "type": "Organization"
        }, 
        "familyName": "SEDEEK", 
        "givenName": "E.K.", 
        "id": "sg:person.014312423653.40", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014312423653.40"
        ], 
        "type": "Person"
      }
    ], 
    "datePublished": "2007-02-16", 
    "datePublishedReg": "2007-02-16", 
    "description": "Pure nanocrystalline hematite (40 to 100\u00a0nm) compacts were prepared and sintered at various temperatures (300\u00a0\u00b0C to 600\u00a0\u00b0C) and then reduced with 100\u00a0pct H2 at 500\u00a0\u00b0C. On the other hand, fired compacts at 500\u00a0\u00b0C were reduced with a H2-Ar gas mixture containing different concentration of hydrogen (100, 75, 50, and 25\u00a0pct) at 500\u00a0\u00b0C using thermogravimetric techniques. Nanocrystalline Fe2O3 compacts were characterized before and after reduction with X-ray diffraction, scanning electron microscopy (SEM), vibrating sample magnetometer (VSM), and reflected light microscope. It was found that the fired compacts at 400\u00a0\u00b0C to 600\u00a0\u00b0C have relatively faster reaction behaviors compared to that at lower firing temperature 300\u00a0\u00b0C. By decreasing the firing temperature to 300\u00a0\u00b0C, partial sintering with grain growth was observed clearly during reduction. Also, it was found that the reduction rate increased with increasing hydrogen content in the reducing gas. Comparatively, grain growth and partial coalescence took place during reduction with 25\u00a0pct H2 due to long reaction time.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s11663-006-9002-5", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136775", 
        "issn": [
          "1073-5615", 
          "1543-1916"
        ], 
        "name": "Metallurgical and Materials Transactions B", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "1", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "38"
      }
    ], 
    "keywords": [
      "pct H2", 
      "grain growth", 
      "firing temperature", 
      "H2-Ar gas mixtures", 
      "partial sintering", 
      "hematite compacts", 
      "low-temperature reduction", 
      "hydrogen content", 
      "nanocrystalline Fe2O3", 
      "gas composition", 
      "gas mixture", 
      "compacts", 
      "temperature 300", 
      "sample magnetometer", 
      "partial coalescence", 
      "Fe2O3 compacts", 
      "thermogravimetric technique", 
      "reaction behavior", 
      "ray diffraction", 
      "electron microscopy", 
      "temperature", 
      "reduction rate", 
      "sintering", 
      "H2", 
      "coalescence", 
      "gas", 
      "magnetometer", 
      "Fe2O3", 
      "microscope", 
      "hydrogen", 
      "diffraction", 
      "different concentrations", 
      "reduction", 
      "reaction time", 
      "longer reaction times", 
      "microscopy", 
      "mixture", 
      "behavior", 
      "technique", 
      "content", 
      "composition", 
      "growth", 
      "concentration", 
      "light microscope", 
      "effect", 
      "rate", 
      "time", 
      "place", 
      "hand", 
      "Pure nanocrystalline hematite (40 to 100\u00a0nm) compacts", 
      "nanocrystalline hematite (40 to 100\u00a0nm) compacts", 
      "Nanocrystalline Fe2O3 compacts", 
      "faster reaction behaviors", 
      "Reducing Gas Composition"
    ], 
    "name": "Effect of Firing Temperature and Reducing Gas Composition during Low-Temperature Reduction of Nanocrystalline Fe2O3", 
    "pagination": "5-11", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1010343115"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s11663-006-9002-5"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s11663-006-9002-5", 
      "https://app.dimensions.ai/details/publication/pub.1010343115"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2021-11-01T18:10", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20211101/entities/gbq_results/article/article_438.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s11663-006-9002-5"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11663-006-9002-5'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11663-006-9002-5'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11663-006-9002-5'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11663-006-9002-5'


 

This table displays all metadata directly associated to this object as RDF triples.

136 TRIPLES      21 PREDICATES      79 URIs      71 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s11663-006-9002-5 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author Nedcbdead3dcb430fa6d23d0ef8fc46d2
4 schema:datePublished 2007-02-16
5 schema:datePublishedReg 2007-02-16
6 schema:description Pure nanocrystalline hematite (40 to 100 nm) compacts were prepared and sintered at various temperatures (300 °C to 600 °C) and then reduced with 100 pct H2 at 500 °C. On the other hand, fired compacts at 500 °C were reduced with a H2-Ar gas mixture containing different concentration of hydrogen (100, 75, 50, and 25 pct) at 500 °C using thermogravimetric techniques. Nanocrystalline Fe2O3 compacts were characterized before and after reduction with X-ray diffraction, scanning electron microscopy (SEM), vibrating sample magnetometer (VSM), and reflected light microscope. It was found that the fired compacts at 400 °C to 600 °C have relatively faster reaction behaviors compared to that at lower firing temperature 300 °C. By decreasing the firing temperature to 300 °C, partial sintering with grain growth was observed clearly during reduction. Also, it was found that the reduction rate increased with increasing hydrogen content in the reducing gas. Comparatively, grain growth and partial coalescence took place during reduction with 25 pct H2 due to long reaction time.
7 schema:genre article
8 schema:inLanguage en
9 schema:isAccessibleForFree false
10 schema:isPartOf Nca15b9cf0c124985b23d1b9713c9ed0e
11 Ne8c6c035dbaf48af9b900e19e7b588f1
12 sg:journal.1136775
13 schema:keywords Fe2O3
14 Fe2O3 compacts
15 H2
16 H2-Ar gas mixtures
17 Nanocrystalline Fe2O3 compacts
18 Pure nanocrystalline hematite (40 to 100 nm) compacts
19 Reducing Gas Composition
20 behavior
21 coalescence
22 compacts
23 composition
24 concentration
25 content
26 different concentrations
27 diffraction
28 effect
29 electron microscopy
30 faster reaction behaviors
31 firing temperature
32 gas
33 gas composition
34 gas mixture
35 grain growth
36 growth
37 hand
38 hematite compacts
39 hydrogen
40 hydrogen content
41 light microscope
42 longer reaction times
43 low-temperature reduction
44 magnetometer
45 microscope
46 microscopy
47 mixture
48 nanocrystalline Fe2O3
49 nanocrystalline hematite (40 to 100 nm) compacts
50 partial coalescence
51 partial sintering
52 pct H2
53 place
54 rate
55 ray diffraction
56 reaction behavior
57 reaction time
58 reduction
59 reduction rate
60 sample magnetometer
61 sintering
62 technique
63 temperature
64 temperature 300
65 thermogravimetric technique
66 time
67 schema:name Effect of Firing Temperature and Reducing Gas Composition during Low-Temperature Reduction of Nanocrystalline Fe2O3
68 schema:pagination 5-11
69 schema:productId N3f9c11d1c18c4eb79fe1400f21386e62
70 N9898925c282a46978977932dabbec50c
71 schema:sameAs https://app.dimensions.ai/details/publication/pub.1010343115
72 https://doi.org/10.1007/s11663-006-9002-5
73 schema:sdDatePublished 2021-11-01T18:10
74 schema:sdLicense https://scigraph.springernature.com/explorer/license/
75 schema:sdPublisher Nac35352ce68341e6a233c41a98d442d7
76 schema:url https://doi.org/10.1007/s11663-006-9002-5
77 sgo:license sg:explorer/license/
78 sgo:sdDataset articles
79 rdf:type schema:ScholarlyArticle
80 N3f9c11d1c18c4eb79fe1400f21386e62 schema:name doi
81 schema:value 10.1007/s11663-006-9002-5
82 rdf:type schema:PropertyValue
83 N8c4439b25aea4af49f20371ba4ddb36b rdf:first sg:person.014312423653.40
84 rdf:rest rdf:nil
85 N9898925c282a46978977932dabbec50c schema:name dimensions_id
86 schema:value pub.1010343115
87 rdf:type schema:PropertyValue
88 Nac35352ce68341e6a233c41a98d442d7 schema:name Springer Nature - SN SciGraph project
89 rdf:type schema:Organization
90 Nca15b9cf0c124985b23d1b9713c9ed0e schema:issueNumber 1
91 rdf:type schema:PublicationIssue
92 Ne068b31f9a014890b273788cc0cabaca rdf:first sg:person.015333711045.11
93 rdf:rest Nfb73dd4bb9c2461a967b6e82278b5407
94 Ne8c6c035dbaf48af9b900e19e7b588f1 schema:volumeNumber 38
95 rdf:type schema:PublicationVolume
96 Nedcbdead3dcb430fa6d23d0ef8fc46d2 rdf:first sg:person.011313225416.52
97 rdf:rest Ne068b31f9a014890b273788cc0cabaca
98 Nfb73dd4bb9c2461a967b6e82278b5407 rdf:first sg:person.010714632367.52
99 rdf:rest N8c4439b25aea4af49f20371ba4ddb36b
100 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
101 schema:name Engineering
102 rdf:type schema:DefinedTerm
103 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
104 schema:name Materials Engineering
105 rdf:type schema:DefinedTerm
106 sg:journal.1136775 schema:issn 1073-5615
107 1543-1916
108 schema:name Metallurgical and Materials Transactions B
109 schema:publisher Springer Nature
110 rdf:type schema:Periodical
111 sg:person.010714632367.52 schema:affiliation grid-institutes:grid.470969.5
112 schema:familyName NASR
113 schema:givenName M.I.
114 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010714632367.52
115 rdf:type schema:Person
116 sg:person.011313225416.52 schema:affiliation grid-institutes:grid.470969.5
117 schema:familyName BAHGAT
118 schema:givenName M.
119 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011313225416.52
120 rdf:type schema:Person
121 sg:person.014312423653.40 schema:affiliation grid-institutes:grid.411662.6
122 schema:familyName SEDEEK
123 schema:givenName E.K.
124 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014312423653.40
125 rdf:type schema:Person
126 sg:person.015333711045.11 schema:affiliation grid-institutes:grid.411662.6
127 schema:familyName KHEDR
128 schema:givenName M.H.
129 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015333711045.11
130 rdf:type schema:Person
131 grid-institutes:grid.411662.6 schema:alternateName Benisuef University, Benisuef, Cairo, Egypt
132 schema:name Benisuef University, Benisuef, Cairo, Egypt
133 rdf:type schema:Organization
134 grid-institutes:grid.470969.5 schema:alternateName Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt
135 schema:name Central Metallurgical Research and Development Institute (CMRDI), 11421, Cairo, Egypt
136 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...