Comparative Study of Sliding, Scratching, and Impact-Loading Behavior of Hard CrB2 and Cr–B–N Films View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2016-09

AUTHORS

Ph. V. Kiryukhantsev-Korneev, J. F. Pierson, M. Y. Bychkova, O. S. Manakova, E. A. Levashov, D. V. Shtansky

ABSTRACT

CrB2 and Cr–B–N films were deposited by magnetron sputtering of CrB2 target in an argon atmosphere or in a gaseous mixture of argon and nitrogen. The films were characterized in terms of their adhesion strength, sliding, and impact wear resistance. Crack resistance of the films was evaluated by micro-indentations. The adhesion strength was studied by means of scratch testing. The wear tests were performed under different loads against chromium steel and WC–Co counterpart materials. In order to determine the film fatigue toughness, dynamic impact tests were carried out. The indentations, scars, wear tracks, and impact cavities on the film surface were examined using optical profilometry, as well as optical and scanning electron microscopy. Comparison of lifetimes of CrB2 and Cr–B–N-coated cemented carbide mills in dry milling of D2 high-chromium steel was also performed. The obtained results show that the CrB2 film has poor adhesion, low fracture toughness, and rapidly fails during sliding and dynamic impact tests. In contrast, the Cr–B–N films with nitrogen content between 7 and 11 at.% exhibited superior adhesion strength (critical load Lc2 = 70–90 N), good tribological properties (friction coefficient against WC–Co <0.4 and wear rate <2×10−6 mm3 N−1 m−1), and reduced impact wear. The lifetime of mills coated with Cr–B–N films was 1.3 and 2.0 times longer as compared to the tools coated with TiN and CrB2 films and uncoated WC–Co tools, respectively. More... »

PAGES

44

References to SciGraph publications

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s11249-016-0729-0

DOI

http://dx.doi.org/10.1007/s11249-016-0729-0

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1007843729


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "National University of Science and Technology", 
          "id": "https://www.grid.ac/institutes/grid.35043.31", 
          "name": [
            "National University of Science and Technology \u201cMISIS\u201d, Leninsky pr., 4, 119049, Moscow, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Kiryukhantsev-Korneev", 
        "givenName": "Ph. V.", 
        "id": "sg:person.012132657251.51", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012132657251.51"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Institut Jean Lamour", 
          "id": "https://www.grid.ac/institutes/grid.461892.0", 
          "name": [
            "Institut Jean Lamour (UMR CNRS 7198), Universit\u00e9 de Lorraine, Parc de Saurupt, CS 50840, 54011, Nancy, France"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Pierson", 
        "givenName": "J. F.", 
        "id": "sg:person.011554143473.68", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011554143473.68"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "National University of Science and Technology", 
          "id": "https://www.grid.ac/institutes/grid.35043.31", 
          "name": [
            "National University of Science and Technology \u201cMISIS\u201d, Leninsky pr., 4, 119049, Moscow, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bychkova", 
        "givenName": "M. Y.", 
        "id": "sg:person.014007667725.17", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014007667725.17"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "National University of Science and Technology", 
          "id": "https://www.grid.ac/institutes/grid.35043.31", 
          "name": [
            "National University of Science and Technology \u201cMISIS\u201d, Leninsky pr., 4, 119049, Moscow, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Manakova", 
        "givenName": "O. S.", 
        "id": "sg:person.015340721157.60", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015340721157.60"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "National University of Science and Technology", 
          "id": "https://www.grid.ac/institutes/grid.35043.31", 
          "name": [
            "National University of Science and Technology \u201cMISIS\u201d, Leninsky pr., 4, 119049, Moscow, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Levashov", 
        "givenName": "E. A.", 
        "id": "sg:person.010111373705.67", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010111373705.67"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "National University of Science and Technology", 
          "id": "https://www.grid.ac/institutes/grid.35043.31", 
          "name": [
            "National University of Science and Technology \u201cMISIS\u201d, Leninsky pr., 4, 119049, Moscow, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Shtansky", 
        "givenName": "D. V.", 
        "id": "sg:person.0604121561.73", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0604121561.73"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.3103/s1068798x10090133", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000467261", 
          "https://doi.org/10.3103/s1068798x10090133"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.3103/s1068798x10090133", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000467261", 
          "https://doi.org/10.3103/s1068798x10090133"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0043-1648(00)00488-9", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000668050"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.tsf.2013.08.093", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000738132"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0043-1648(00)00505-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1001420606"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.ijrmhm.2009.07.012", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1005202407"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.tsf.2004.08.077", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006459834"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.ijrmhm.2009.05.008", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1012958109"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.wear.2005.01.031", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1014787395"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.tsf.2008.11.126", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1019189972"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0040-6090(03)01189-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025155008"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0257-8972(03)00697-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025409380"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0257-8972(03)00697-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025409380"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2012.05.073", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025882467"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2006.04.031", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1027381450"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0043-1648(01)00582-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1028304724"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.matchemphys.2008.10.026", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1031061038"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.ijrmhm.2009.07.014", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1032871621"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2005.02.132", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1033632477"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2011.09.047", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034202815"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2005.02.126", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034563795"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.msea.2013.01.034", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1035444208"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.vacuum.2007.11.003", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1038664488"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0040-6090(02)00942-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1039677330"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0040-6090(02)00942-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1039677330"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0924-0136(02)00715-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040857091"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0924-0136(02)00715-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040857091"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2009.07.009", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1041620240"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1134/s0031918x14040085", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1041896062", 
          "https://doi.org/10.1134/s0031918x14040085"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0257-8972(02)00685-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1042360070"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2007.11.009", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1044500435"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.jallcom.2009.07.060", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1044508453"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2007.06.057", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1048636245"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.surfcoat.2005.11.040", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1052559665"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1126/science.1068609", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1062445840"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2016-09", 
    "datePublishedReg": "2016-09-01", 
    "description": "CrB2 and Cr\u2013B\u2013N films were deposited by magnetron sputtering of CrB2 target in an argon atmosphere or in a gaseous mixture of argon and nitrogen. The films were characterized in terms of their adhesion strength, sliding, and impact wear resistance. Crack resistance of the films was evaluated by micro-indentations. The adhesion strength was studied by means of scratch testing. The wear tests were performed under different loads against chromium steel and WC\u2013Co counterpart materials. In order to determine the film fatigue toughness, dynamic impact tests were carried out. The indentations, scars, wear tracks, and impact cavities on the film surface were examined using optical profilometry, as well as optical and scanning electron microscopy. Comparison of lifetimes of CrB2 and Cr\u2013B\u2013N-coated cemented carbide mills in dry milling of D2 high-chromium steel was also performed. The obtained results show that the CrB2 film has poor adhesion, low fracture toughness, and rapidly fails during sliding and dynamic impact tests. In contrast, the Cr\u2013B\u2013N films with nitrogen content between 7 and 11 at.% exhibited superior adhesion strength (critical load Lc2 = 70\u201390 N), good tribological properties (friction coefficient against WC\u2013Co <0.4 and wear rate <2\u00d710\u22126 mm3 N\u22121 m\u22121), and reduced impact wear. The lifetime of mills coated with Cr\u2013B\u2013N films was 1.3 and 2.0 times longer as compared to the tools coated with TiN and CrB2 films and uncoated WC\u2013Co tools, respectively.", 
    "genre": "research_article", 
    "id": "sg:pub.10.1007/s11249-016-0729-0", 
    "inLanguage": [
      "en"
    ], 
    "isAccessibleForFree": false, 
    "isFundedItemOf": [
      {
        "id": "sg:grant.4896092", 
        "type": "MonetaryGrant"
      }
    ], 
    "isPartOf": [
      {
        "id": "sg:journal.1133987", 
        "issn": [
          "1023-8883", 
          "1573-2711"
        ], 
        "name": "Tribology Letters", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "3", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "63"
      }
    ], 
    "name": "Comparative Study of Sliding, Scratching, and Impact-Loading Behavior of Hard CrB2 and Cr\u2013B\u2013N Films", 
    "pagination": "44", 
    "productId": [
      {
        "name": "readcube_id", 
        "type": "PropertyValue", 
        "value": [
          "255d1c94d41e85929653a0123bc3e2970b06959038a72822c310c95084782b52"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s11249-016-0729-0"
        ]
      }, 
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1007843729"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s11249-016-0729-0", 
      "https://app.dimensions.ai/details/publication/pub.1007843729"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2019-04-11T12:26", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-uberresearch-data-dimensions-target-20181106-alternative/cleanup/v134/2549eaecd7973599484d7c17b260dba0a4ecb94b/merge/v9/a6c9fde33151104705d4d7ff012ea9563521a3ce/jats-lookup/v90/0000000362_0000000362/records_87115_00000000.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://link.springer.com/10.1007%2Fs11249-016-0729-0"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11249-016-0729-0'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11249-016-0729-0'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11249-016-0729-0'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11249-016-0729-0'


 

This table displays all metadata directly associated to this object as RDF triples.

196 TRIPLES      21 PREDICATES      58 URIs      19 LITERALS      7 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s11249-016-0729-0 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author N3e014ded42ac47d58bfa68ab70a53515
4 schema:citation sg:pub.10.1134/s0031918x14040085
5 sg:pub.10.3103/s1068798x10090133
6 https://doi.org/10.1016/j.ijrmhm.2009.05.008
7 https://doi.org/10.1016/j.ijrmhm.2009.07.012
8 https://doi.org/10.1016/j.ijrmhm.2009.07.014
9 https://doi.org/10.1016/j.jallcom.2009.07.060
10 https://doi.org/10.1016/j.matchemphys.2008.10.026
11 https://doi.org/10.1016/j.msea.2013.01.034
12 https://doi.org/10.1016/j.surfcoat.2005.02.126
13 https://doi.org/10.1016/j.surfcoat.2005.02.132
14 https://doi.org/10.1016/j.surfcoat.2005.11.040
15 https://doi.org/10.1016/j.surfcoat.2006.04.031
16 https://doi.org/10.1016/j.surfcoat.2007.06.057
17 https://doi.org/10.1016/j.surfcoat.2007.11.009
18 https://doi.org/10.1016/j.surfcoat.2009.07.009
19 https://doi.org/10.1016/j.surfcoat.2011.09.047
20 https://doi.org/10.1016/j.surfcoat.2012.05.073
21 https://doi.org/10.1016/j.tsf.2004.08.077
22 https://doi.org/10.1016/j.tsf.2008.11.126
23 https://doi.org/10.1016/j.tsf.2013.08.093
24 https://doi.org/10.1016/j.vacuum.2007.11.003
25 https://doi.org/10.1016/j.wear.2005.01.031
26 https://doi.org/10.1016/s0040-6090(02)00942-2
27 https://doi.org/10.1016/s0040-6090(03)01189-1
28 https://doi.org/10.1016/s0043-1648(00)00488-9
29 https://doi.org/10.1016/s0043-1648(00)00505-6
30 https://doi.org/10.1016/s0043-1648(01)00582-8
31 https://doi.org/10.1016/s0257-8972(02)00685-0
32 https://doi.org/10.1016/s0257-8972(03)00697-2
33 https://doi.org/10.1016/s0924-0136(02)00715-x
34 https://doi.org/10.1126/science.1068609
35 schema:datePublished 2016-09
36 schema:datePublishedReg 2016-09-01
37 schema:description CrB2 and Cr–B–N films were deposited by magnetron sputtering of CrB2 target in an argon atmosphere or in a gaseous mixture of argon and nitrogen. The films were characterized in terms of their adhesion strength, sliding, and impact wear resistance. Crack resistance of the films was evaluated by micro-indentations. The adhesion strength was studied by means of scratch testing. The wear tests were performed under different loads against chromium steel and WC–Co counterpart materials. In order to determine the film fatigue toughness, dynamic impact tests were carried out. The indentations, scars, wear tracks, and impact cavities on the film surface were examined using optical profilometry, as well as optical and scanning electron microscopy. Comparison of lifetimes of CrB2 and Cr–B–N-coated cemented carbide mills in dry milling of D2 high-chromium steel was also performed. The obtained results show that the CrB2 film has poor adhesion, low fracture toughness, and rapidly fails during sliding and dynamic impact tests. In contrast, the Cr–B–N films with nitrogen content between 7 and 11 at.% exhibited superior adhesion strength (critical load Lc2 = 70–90 N), good tribological properties (friction coefficient against WC–Co <0.4 and wear rate <2×10−6 mm3 N−1 m−1), and reduced impact wear. The lifetime of mills coated with Cr–B–N films was 1.3 and 2.0 times longer as compared to the tools coated with TiN and CrB2 films and uncoated WC–Co tools, respectively.
38 schema:genre research_article
39 schema:inLanguage en
40 schema:isAccessibleForFree false
41 schema:isPartOf N3758d8deaf1748c6b2846778157877bc
42 Nf2eb2b4a235e4c278486a2ec4ca73771
43 sg:journal.1133987
44 schema:name Comparative Study of Sliding, Scratching, and Impact-Loading Behavior of Hard CrB2 and Cr–B–N Films
45 schema:pagination 44
46 schema:productId N5be0b9ebca464c2a9b00a1a3ac435484
47 N5cc370a720604b1d86a6789c6a5a5e61
48 Nf417d22f39f9408f9086196cf36f5b23
49 schema:sameAs https://app.dimensions.ai/details/publication/pub.1007843729
50 https://doi.org/10.1007/s11249-016-0729-0
51 schema:sdDatePublished 2019-04-11T12:26
52 schema:sdLicense https://scigraph.springernature.com/explorer/license/
53 schema:sdPublisher Nd93b9183234f49678b84c1c907813b92
54 schema:url https://link.springer.com/10.1007%2Fs11249-016-0729-0
55 sgo:license sg:explorer/license/
56 sgo:sdDataset articles
57 rdf:type schema:ScholarlyArticle
58 N1c37b93f989648e4977f9f6de8be3d77 rdf:first sg:person.014007667725.17
59 rdf:rest N4d2b70289019401ebafd4143825df566
60 N2992979df3644b689fb7eeda5fb79607 rdf:first sg:person.0604121561.73
61 rdf:rest rdf:nil
62 N3758d8deaf1748c6b2846778157877bc schema:issueNumber 3
63 rdf:type schema:PublicationIssue
64 N3e014ded42ac47d58bfa68ab70a53515 rdf:first sg:person.012132657251.51
65 rdf:rest Nc3d3d1fedfe745d9ac1448643dda5d75
66 N4d2b70289019401ebafd4143825df566 rdf:first sg:person.015340721157.60
67 rdf:rest N841931d122604b8184a813301d3a789d
68 N5be0b9ebca464c2a9b00a1a3ac435484 schema:name dimensions_id
69 schema:value pub.1007843729
70 rdf:type schema:PropertyValue
71 N5cc370a720604b1d86a6789c6a5a5e61 schema:name doi
72 schema:value 10.1007/s11249-016-0729-0
73 rdf:type schema:PropertyValue
74 N841931d122604b8184a813301d3a789d rdf:first sg:person.010111373705.67
75 rdf:rest N2992979df3644b689fb7eeda5fb79607
76 Nc3d3d1fedfe745d9ac1448643dda5d75 rdf:first sg:person.011554143473.68
77 rdf:rest N1c37b93f989648e4977f9f6de8be3d77
78 Nd93b9183234f49678b84c1c907813b92 schema:name Springer Nature - SN SciGraph project
79 rdf:type schema:Organization
80 Nf2eb2b4a235e4c278486a2ec4ca73771 schema:volumeNumber 63
81 rdf:type schema:PublicationVolume
82 Nf417d22f39f9408f9086196cf36f5b23 schema:name readcube_id
83 schema:value 255d1c94d41e85929653a0123bc3e2970b06959038a72822c310c95084782b52
84 rdf:type schema:PropertyValue
85 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
86 schema:name Engineering
87 rdf:type schema:DefinedTerm
88 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
89 schema:name Materials Engineering
90 rdf:type schema:DefinedTerm
91 sg:grant.4896092 http://pending.schema.org/fundedItem sg:pub.10.1007/s11249-016-0729-0
92 rdf:type schema:MonetaryGrant
93 sg:journal.1133987 schema:issn 1023-8883
94 1573-2711
95 schema:name Tribology Letters
96 rdf:type schema:Periodical
97 sg:person.010111373705.67 schema:affiliation https://www.grid.ac/institutes/grid.35043.31
98 schema:familyName Levashov
99 schema:givenName E. A.
100 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010111373705.67
101 rdf:type schema:Person
102 sg:person.011554143473.68 schema:affiliation https://www.grid.ac/institutes/grid.461892.0
103 schema:familyName Pierson
104 schema:givenName J. F.
105 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011554143473.68
106 rdf:type schema:Person
107 sg:person.012132657251.51 schema:affiliation https://www.grid.ac/institutes/grid.35043.31
108 schema:familyName Kiryukhantsev-Korneev
109 schema:givenName Ph. V.
110 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012132657251.51
111 rdf:type schema:Person
112 sg:person.014007667725.17 schema:affiliation https://www.grid.ac/institutes/grid.35043.31
113 schema:familyName Bychkova
114 schema:givenName M. Y.
115 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014007667725.17
116 rdf:type schema:Person
117 sg:person.015340721157.60 schema:affiliation https://www.grid.ac/institutes/grid.35043.31
118 schema:familyName Manakova
119 schema:givenName O. S.
120 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015340721157.60
121 rdf:type schema:Person
122 sg:person.0604121561.73 schema:affiliation https://www.grid.ac/institutes/grid.35043.31
123 schema:familyName Shtansky
124 schema:givenName D. V.
125 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.0604121561.73
126 rdf:type schema:Person
127 sg:pub.10.1134/s0031918x14040085 schema:sameAs https://app.dimensions.ai/details/publication/pub.1041896062
128 https://doi.org/10.1134/s0031918x14040085
129 rdf:type schema:CreativeWork
130 sg:pub.10.3103/s1068798x10090133 schema:sameAs https://app.dimensions.ai/details/publication/pub.1000467261
131 https://doi.org/10.3103/s1068798x10090133
132 rdf:type schema:CreativeWork
133 https://doi.org/10.1016/j.ijrmhm.2009.05.008 schema:sameAs https://app.dimensions.ai/details/publication/pub.1012958109
134 rdf:type schema:CreativeWork
135 https://doi.org/10.1016/j.ijrmhm.2009.07.012 schema:sameAs https://app.dimensions.ai/details/publication/pub.1005202407
136 rdf:type schema:CreativeWork
137 https://doi.org/10.1016/j.ijrmhm.2009.07.014 schema:sameAs https://app.dimensions.ai/details/publication/pub.1032871621
138 rdf:type schema:CreativeWork
139 https://doi.org/10.1016/j.jallcom.2009.07.060 schema:sameAs https://app.dimensions.ai/details/publication/pub.1044508453
140 rdf:type schema:CreativeWork
141 https://doi.org/10.1016/j.matchemphys.2008.10.026 schema:sameAs https://app.dimensions.ai/details/publication/pub.1031061038
142 rdf:type schema:CreativeWork
143 https://doi.org/10.1016/j.msea.2013.01.034 schema:sameAs https://app.dimensions.ai/details/publication/pub.1035444208
144 rdf:type schema:CreativeWork
145 https://doi.org/10.1016/j.surfcoat.2005.02.126 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034563795
146 rdf:type schema:CreativeWork
147 https://doi.org/10.1016/j.surfcoat.2005.02.132 schema:sameAs https://app.dimensions.ai/details/publication/pub.1033632477
148 rdf:type schema:CreativeWork
149 https://doi.org/10.1016/j.surfcoat.2005.11.040 schema:sameAs https://app.dimensions.ai/details/publication/pub.1052559665
150 rdf:type schema:CreativeWork
151 https://doi.org/10.1016/j.surfcoat.2006.04.031 schema:sameAs https://app.dimensions.ai/details/publication/pub.1027381450
152 rdf:type schema:CreativeWork
153 https://doi.org/10.1016/j.surfcoat.2007.06.057 schema:sameAs https://app.dimensions.ai/details/publication/pub.1048636245
154 rdf:type schema:CreativeWork
155 https://doi.org/10.1016/j.surfcoat.2007.11.009 schema:sameAs https://app.dimensions.ai/details/publication/pub.1044500435
156 rdf:type schema:CreativeWork
157 https://doi.org/10.1016/j.surfcoat.2009.07.009 schema:sameAs https://app.dimensions.ai/details/publication/pub.1041620240
158 rdf:type schema:CreativeWork
159 https://doi.org/10.1016/j.surfcoat.2011.09.047 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034202815
160 rdf:type schema:CreativeWork
161 https://doi.org/10.1016/j.surfcoat.2012.05.073 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025882467
162 rdf:type schema:CreativeWork
163 https://doi.org/10.1016/j.tsf.2004.08.077 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006459834
164 rdf:type schema:CreativeWork
165 https://doi.org/10.1016/j.tsf.2008.11.126 schema:sameAs https://app.dimensions.ai/details/publication/pub.1019189972
166 rdf:type schema:CreativeWork
167 https://doi.org/10.1016/j.tsf.2013.08.093 schema:sameAs https://app.dimensions.ai/details/publication/pub.1000738132
168 rdf:type schema:CreativeWork
169 https://doi.org/10.1016/j.vacuum.2007.11.003 schema:sameAs https://app.dimensions.ai/details/publication/pub.1038664488
170 rdf:type schema:CreativeWork
171 https://doi.org/10.1016/j.wear.2005.01.031 schema:sameAs https://app.dimensions.ai/details/publication/pub.1014787395
172 rdf:type schema:CreativeWork
173 https://doi.org/10.1016/s0040-6090(02)00942-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1039677330
174 rdf:type schema:CreativeWork
175 https://doi.org/10.1016/s0040-6090(03)01189-1 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025155008
176 rdf:type schema:CreativeWork
177 https://doi.org/10.1016/s0043-1648(00)00488-9 schema:sameAs https://app.dimensions.ai/details/publication/pub.1000668050
178 rdf:type schema:CreativeWork
179 https://doi.org/10.1016/s0043-1648(00)00505-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1001420606
180 rdf:type schema:CreativeWork
181 https://doi.org/10.1016/s0043-1648(01)00582-8 schema:sameAs https://app.dimensions.ai/details/publication/pub.1028304724
182 rdf:type schema:CreativeWork
183 https://doi.org/10.1016/s0257-8972(02)00685-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1042360070
184 rdf:type schema:CreativeWork
185 https://doi.org/10.1016/s0257-8972(03)00697-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025409380
186 rdf:type schema:CreativeWork
187 https://doi.org/10.1016/s0924-0136(02)00715-x schema:sameAs https://app.dimensions.ai/details/publication/pub.1040857091
188 rdf:type schema:CreativeWork
189 https://doi.org/10.1126/science.1068609 schema:sameAs https://app.dimensions.ai/details/publication/pub.1062445840
190 rdf:type schema:CreativeWork
191 https://www.grid.ac/institutes/grid.35043.31 schema:alternateName National University of Science and Technology
192 schema:name National University of Science and Technology “MISIS”, Leninsky pr., 4, 119049, Moscow, Russia
193 rdf:type schema:Organization
194 https://www.grid.ac/institutes/grid.461892.0 schema:alternateName Institut Jean Lamour
195 schema:name Institut Jean Lamour (UMR CNRS 7198), Université de Lorraine, Parc de Saurupt, CS 50840, 54011, Nancy, France
196 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...