Laser Clad and HVOF-Sprayed Stellite 6 Coating in Chlorine-Rich Environment with KCl at 700 °C View Full Text


Ontology type: schema:ScholarlyArticle      Open Access: True


Article Info

DATE

2017-04-20

AUTHORS

Zdenek Pala, Mingwen Bai, Frantisek Lukac, Tanvir Hussain

ABSTRACT

Laser clads and HVOF coatings from a stellite 6 alloy (Co–Cr–W–C alloy) on 304 stainless steel substrates were exposed both bare and with KCl deposits in 500 ppm HCl with 5% O2 for 250 h at 700 °C. SEM/EDX and PXRD analyses with Rietveld refinement were used for assessment of the attack and for analysis of the scales. The bare samples suffered from scale spallation and the scale was mostly composed of Cr2O3, CoCr2O4 and CoO, although due to dilution haematite (Fe2O3) was detected in the scale formed on the laser clad sample. A small amount of hydrated HCl was detected in bare samples. While the corrosion of the bare surfaces was limited to comparatively shallow depths and manifested by η and M7C3 carbide formation, the presence of KCl on the surface led to severe Cr depletion from the HVOF coating (to 1 wt%). Both inward and outward diffusion of elements occurred in the HVOF coating resulting in Kirdendall voids at the coating–steel interface. The laser clad sample performed significantly better in conditions of the KCl-deposit-induced corrosion. In addition to the oxides, CoCl2 was detected in the HVOF sample and K3CrO4 was detected in the laser clad sample. Thermodynamic calculations and kinetic simulations were carried out to interpret the oxidation and diffusion behaviours of coatings. More... »

PAGES

749-771

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s11085-017-9776-7

DOI

http://dx.doi.org/10.1007/s11085-017-9776-7

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1084986460


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK", 
          "id": "http://www.grid.ac/institutes/grid.4563.4", 
          "name": [
            "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Pala", 
        "givenName": "Zdenek", 
        "id": "sg:person.010663526767.14", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010663526767.14"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK", 
          "id": "http://www.grid.ac/institutes/grid.4563.4", 
          "name": [
            "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bai", 
        "givenName": "Mingwen", 
        "id": "sg:person.07630614502.09", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07630614502.09"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Institute of Plasma Physics CAS, Za Slovankou 3, Prague, Czech Republic", 
          "id": "http://www.grid.ac/institutes/grid.425087.c", 
          "name": [
            "Institute of Plasma Physics CAS, Za Slovankou 3, Prague, Czech Republic"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Lukac", 
        "givenName": "Frantisek", 
        "id": "sg:person.012203715233.30", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012203715233.30"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK", 
          "id": "http://www.grid.ac/institutes/grid.4563.4", 
          "name": [
            "Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Hussain", 
        "givenName": "Tanvir", 
        "id": "sg:person.012712727557.79", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012712727557.79"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1007/bf03338205", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1006242745", 
          "https://doi.org/10.1007/bf03338205"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf00608018", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1017221436", 
          "https://doi.org/10.1007/bf00608018"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11085-015-9546-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1004025716", 
          "https://doi.org/10.1007/s11085-015-9546-3"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11085-014-9507-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1022332833", 
          "https://doi.org/10.1007/s11085-014-9507-2"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf00614619", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1019283359", 
          "https://doi.org/10.1007/bf00614619"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf00665445", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1022527039", 
          "https://doi.org/10.1007/bf00665445"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11666-015-0365-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1013355151", 
          "https://doi.org/10.1007/s11666-015-0365-5"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11085-009-9156-z", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1017460882", 
          "https://doi.org/10.1007/s11085-009-9156-z"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11085-005-5704-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1020222080", 
          "https://doi.org/10.1007/s11085-005-5704-3"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02402776", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049075041", 
          "https://doi.org/10.1007/bf02402776"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11085-009-9153-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1001772074", 
          "https://doi.org/10.1007/s11085-009-9153-2"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2017-04-20", 
    "datePublishedReg": "2017-04-20", 
    "description": "Laser clads and HVOF coatings from a stellite 6 alloy (Co\u2013Cr\u2013W\u2013C alloy) on 304 stainless steel substrates were exposed both bare and with KCl deposits in 500\u00a0ppm HCl with 5% O2 for 250\u00a0h at 700\u00a0\u00b0C. SEM/EDX and PXRD analyses with Rietveld refinement were used for assessment of the attack and for analysis of the scales. The bare samples suffered from scale spallation and the scale was mostly composed of Cr2O3, CoCr2O4 and CoO, although due to dilution haematite (Fe2O3) was detected in the scale formed on the laser clad sample. A small amount of hydrated HCl was detected in bare samples. While the corrosion of the bare surfaces was limited to comparatively shallow depths and manifested by \u03b7 and M7C3 carbide formation, the presence of KCl on the surface led to severe Cr depletion from the HVOF coating (to 1\u00a0wt%). Both inward and outward diffusion of elements occurred in the HVOF coating resulting in Kirdendall voids at the coating\u2013steel interface. The laser clad sample performed significantly better in conditions of the KCl-deposit-induced corrosion. In addition to the oxides, CoCl2 was detected in the HVOF sample and K3CrO4 was detected in the laser clad sample. Thermodynamic calculations and kinetic simulations were carried out to interpret the oxidation and diffusion behaviours of coatings.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s11085-017-9776-7", 
    "isAccessibleForFree": true, 
    "isFundedItemOf": [
      {
        "id": "sg:grant.3956594", 
        "type": "MonetaryGrant"
      }
    ], 
    "isPartOf": [
      {
        "id": "sg:journal.1136631", 
        "issn": [
          "0030-770X", 
          "1573-4889"
        ], 
        "name": "Oxidation of Metals", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "5-6", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "88"
      }
    ], 
    "keywords": [
      "HVOF coatings", 
      "laser clad", 
      "bare sample", 
      "coating\u2013steel interface", 
      "Stellite 6 coating", 
      "stainless steel substrates", 
      "severe Cr depletion", 
      "steel substrate", 
      "scale spallation", 
      "SEM/EDX", 
      "KCl deposit", 
      "carbide formation", 
      "outward diffusion", 
      "Cr depletion", 
      "ppm HCl", 
      "coatings", 
      "chlorine\u2013rich environment", 
      "diffusion behavior", 
      "bare surface", 
      "thermodynamic calculations", 
      "corrosion", 
      "kinetic simulations", 
      "clad", 
      "laser", 
      "HVOF", 
      "Rietveld refinement", 
      "surface", 
      "alloy", 
      "spallation", 
      "PXRD analysis", 
      "small amount", 
      "Cr2O3", 
      "CoCr2O4", 
      "EDX", 
      "voids", 
      "simulations", 
      "oxide", 
      "interface", 
      "HCl", 
      "diffusion", 
      "substrate", 
      "CoO", 
      "depth", 
      "behavior", 
      "oxidation", 
      "scale", 
      "samples", 
      "calculations", 
      "conditions", 
      "refinement", 
      "haematite", 
      "O2", 
      "presence of KCl", 
      "analysis", 
      "elements", 
      "amount", 
      "formation", 
      "environment", 
      "addition", 
      "deposits", 
      "KCl", 
      "presence", 
      "CoCl2", 
      "assessment", 
      "attacks", 
      "depletion"
    ], 
    "name": "Laser Clad and HVOF-Sprayed Stellite 6 Coating in Chlorine-Rich Environment with KCl at 700 \u00b0C", 
    "pagination": "749-771", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1084986460"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s11085-017-9776-7"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s11085-017-9776-7", 
      "https://app.dimensions.ai/details/publication/pub.1084986460"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2022-11-24T21:01", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20221124/entities/gbq_results/article/article_725.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s11085-017-9776-7"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s11085-017-9776-7'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s11085-017-9776-7'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s11085-017-9776-7'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s11085-017-9776-7'


 

This table displays all metadata directly associated to this object as RDF triples.

193 TRIPLES      21 PREDICATES      101 URIs      82 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s11085-017-9776-7 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author Nf447fbdfe8bf45ee9cfda89ca9d0feae
4 schema:citation sg:pub.10.1007/bf00608018
5 sg:pub.10.1007/bf00614619
6 sg:pub.10.1007/bf00665445
7 sg:pub.10.1007/bf02402776
8 sg:pub.10.1007/bf03338205
9 sg:pub.10.1007/s11085-005-5704-3
10 sg:pub.10.1007/s11085-009-9153-2
11 sg:pub.10.1007/s11085-009-9156-z
12 sg:pub.10.1007/s11085-014-9507-2
13 sg:pub.10.1007/s11085-015-9546-3
14 sg:pub.10.1007/s11666-015-0365-5
15 schema:datePublished 2017-04-20
16 schema:datePublishedReg 2017-04-20
17 schema:description Laser clads and HVOF coatings from a stellite 6 alloy (Co–Cr–W–C alloy) on 304 stainless steel substrates were exposed both bare and with KCl deposits in 500 ppm HCl with 5% O2 for 250 h at 700 °C. SEM/EDX and PXRD analyses with Rietveld refinement were used for assessment of the attack and for analysis of the scales. The bare samples suffered from scale spallation and the scale was mostly composed of Cr2O3, CoCr2O4 and CoO, although due to dilution haematite (Fe2O3) was detected in the scale formed on the laser clad sample. A small amount of hydrated HCl was detected in bare samples. While the corrosion of the bare surfaces was limited to comparatively shallow depths and manifested by η and M7C3 carbide formation, the presence of KCl on the surface led to severe Cr depletion from the HVOF coating (to 1 wt%). Both inward and outward diffusion of elements occurred in the HVOF coating resulting in Kirdendall voids at the coating–steel interface. The laser clad sample performed significantly better in conditions of the KCl-deposit-induced corrosion. In addition to the oxides, CoCl2 was detected in the HVOF sample and K3CrO4 was detected in the laser clad sample. Thermodynamic calculations and kinetic simulations were carried out to interpret the oxidation and diffusion behaviours of coatings.
18 schema:genre article
19 schema:isAccessibleForFree true
20 schema:isPartOf N26738471dca64a5b8227144e8008865b
21 N5cdba517cc1d4c2b9810773c1c1ab938
22 sg:journal.1136631
23 schema:keywords CoCl2
24 CoCr2O4
25 CoO
26 Cr depletion
27 Cr2O3
28 EDX
29 HCl
30 HVOF
31 HVOF coatings
32 KCl
33 KCl deposit
34 O2
35 PXRD analysis
36 Rietveld refinement
37 SEM/EDX
38 Stellite 6 coating
39 addition
40 alloy
41 amount
42 analysis
43 assessment
44 attacks
45 bare sample
46 bare surface
47 behavior
48 calculations
49 carbide formation
50 chlorine–rich environment
51 clad
52 coatings
53 coating–steel interface
54 conditions
55 corrosion
56 depletion
57 deposits
58 depth
59 diffusion
60 diffusion behavior
61 elements
62 environment
63 formation
64 haematite
65 interface
66 kinetic simulations
67 laser
68 laser clad
69 outward diffusion
70 oxidation
71 oxide
72 ppm HCl
73 presence
74 presence of KCl
75 refinement
76 samples
77 scale
78 scale spallation
79 severe Cr depletion
80 simulations
81 small amount
82 spallation
83 stainless steel substrates
84 steel substrate
85 substrate
86 surface
87 thermodynamic calculations
88 voids
89 schema:name Laser Clad and HVOF-Sprayed Stellite 6 Coating in Chlorine-Rich Environment with KCl at 700 °C
90 schema:pagination 749-771
91 schema:productId N473006a0c7244e4ca6a5d86a889c416a
92 Nbc9524533556484785f9927d6e7c3a9b
93 schema:sameAs https://app.dimensions.ai/details/publication/pub.1084986460
94 https://doi.org/10.1007/s11085-017-9776-7
95 schema:sdDatePublished 2022-11-24T21:01
96 schema:sdLicense https://scigraph.springernature.com/explorer/license/
97 schema:sdPublisher Nc60de94fed0b49a8b9e85efd988ad8c7
98 schema:url https://doi.org/10.1007/s11085-017-9776-7
99 sgo:license sg:explorer/license/
100 sgo:sdDataset articles
101 rdf:type schema:ScholarlyArticle
102 N26738471dca64a5b8227144e8008865b schema:issueNumber 5-6
103 rdf:type schema:PublicationIssue
104 N4234a646ac604dd2b8b7e76d2f221366 rdf:first sg:person.012203715233.30
105 rdf:rest Nd18c103d000a4133977379f98fb65c24
106 N473006a0c7244e4ca6a5d86a889c416a schema:name doi
107 schema:value 10.1007/s11085-017-9776-7
108 rdf:type schema:PropertyValue
109 N5cdba517cc1d4c2b9810773c1c1ab938 schema:volumeNumber 88
110 rdf:type schema:PublicationVolume
111 Nbc9524533556484785f9927d6e7c3a9b schema:name dimensions_id
112 schema:value pub.1084986460
113 rdf:type schema:PropertyValue
114 Nc60de94fed0b49a8b9e85efd988ad8c7 schema:name Springer Nature - SN SciGraph project
115 rdf:type schema:Organization
116 Nc6c553cb05c5487c8ff6c9a6e8d9aa03 rdf:first sg:person.07630614502.09
117 rdf:rest N4234a646ac604dd2b8b7e76d2f221366
118 Nd18c103d000a4133977379f98fb65c24 rdf:first sg:person.012712727557.79
119 rdf:rest rdf:nil
120 Nf447fbdfe8bf45ee9cfda89ca9d0feae rdf:first sg:person.010663526767.14
121 rdf:rest Nc6c553cb05c5487c8ff6c9a6e8d9aa03
122 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
123 schema:name Engineering
124 rdf:type schema:DefinedTerm
125 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
126 schema:name Materials Engineering
127 rdf:type schema:DefinedTerm
128 sg:grant.3956594 http://pending.schema.org/fundedItem sg:pub.10.1007/s11085-017-9776-7
129 rdf:type schema:MonetaryGrant
130 sg:journal.1136631 schema:issn 0030-770X
131 1573-4889
132 schema:name Oxidation of Metals
133 schema:publisher Springer Nature
134 rdf:type schema:Periodical
135 sg:person.010663526767.14 schema:affiliation grid-institutes:grid.4563.4
136 schema:familyName Pala
137 schema:givenName Zdenek
138 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010663526767.14
139 rdf:type schema:Person
140 sg:person.012203715233.30 schema:affiliation grid-institutes:grid.425087.c
141 schema:familyName Lukac
142 schema:givenName Frantisek
143 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012203715233.30
144 rdf:type schema:Person
145 sg:person.012712727557.79 schema:affiliation grid-institutes:grid.4563.4
146 schema:familyName Hussain
147 schema:givenName Tanvir
148 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012712727557.79
149 rdf:type schema:Person
150 sg:person.07630614502.09 schema:affiliation grid-institutes:grid.4563.4
151 schema:familyName Bai
152 schema:givenName Mingwen
153 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07630614502.09
154 rdf:type schema:Person
155 sg:pub.10.1007/bf00608018 schema:sameAs https://app.dimensions.ai/details/publication/pub.1017221436
156 https://doi.org/10.1007/bf00608018
157 rdf:type schema:CreativeWork
158 sg:pub.10.1007/bf00614619 schema:sameAs https://app.dimensions.ai/details/publication/pub.1019283359
159 https://doi.org/10.1007/bf00614619
160 rdf:type schema:CreativeWork
161 sg:pub.10.1007/bf00665445 schema:sameAs https://app.dimensions.ai/details/publication/pub.1022527039
162 https://doi.org/10.1007/bf00665445
163 rdf:type schema:CreativeWork
164 sg:pub.10.1007/bf02402776 schema:sameAs https://app.dimensions.ai/details/publication/pub.1049075041
165 https://doi.org/10.1007/bf02402776
166 rdf:type schema:CreativeWork
167 sg:pub.10.1007/bf03338205 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006242745
168 https://doi.org/10.1007/bf03338205
169 rdf:type schema:CreativeWork
170 sg:pub.10.1007/s11085-005-5704-3 schema:sameAs https://app.dimensions.ai/details/publication/pub.1020222080
171 https://doi.org/10.1007/s11085-005-5704-3
172 rdf:type schema:CreativeWork
173 sg:pub.10.1007/s11085-009-9153-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1001772074
174 https://doi.org/10.1007/s11085-009-9153-2
175 rdf:type schema:CreativeWork
176 sg:pub.10.1007/s11085-009-9156-z schema:sameAs https://app.dimensions.ai/details/publication/pub.1017460882
177 https://doi.org/10.1007/s11085-009-9156-z
178 rdf:type schema:CreativeWork
179 sg:pub.10.1007/s11085-014-9507-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1022332833
180 https://doi.org/10.1007/s11085-014-9507-2
181 rdf:type schema:CreativeWork
182 sg:pub.10.1007/s11085-015-9546-3 schema:sameAs https://app.dimensions.ai/details/publication/pub.1004025716
183 https://doi.org/10.1007/s11085-015-9546-3
184 rdf:type schema:CreativeWork
185 sg:pub.10.1007/s11666-015-0365-5 schema:sameAs https://app.dimensions.ai/details/publication/pub.1013355151
186 https://doi.org/10.1007/s11666-015-0365-5
187 rdf:type schema:CreativeWork
188 grid-institutes:grid.425087.c schema:alternateName Institute of Plasma Physics CAS, Za Slovankou 3, Prague, Czech Republic
189 schema:name Institute of Plasma Physics CAS, Za Slovankou 3, Prague, Czech Republic
190 rdf:type schema:Organization
191 grid-institutes:grid.4563.4 schema:alternateName Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK
192 schema:name Faculty of Engineering, University of Nottingham, University Park, NG7 2RD, Nottingham, UK
193 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...