Comparison of drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu solder joints subjected to drop test View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2010-05-15

AUTHORS

Ning Zhang, Yaowu Shi, Fu Guo, Yongping Lei, Zhidong Xia, Zhenhua Chen, Li Tian

ABSTRACT

This study was concerned with the drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu (wt. %) solder joints when the specimens were subjected to drop test after soldering process. The U-notch butt-jointed specimen was adopted and a lab-designed drop tester was employed. Meanwhile, the electrical resistance values of two kinds of solder joints were measured and recorded after certain drop tests, and finally drop number versus resistance curves were plotted and compared. From the resistance variation with the drop number, it was observed that the Sn37Pb joints presented significantly higher drop performance than the Sn3.8Ag0.7Cu ones. For the Sn3.8Ag0.7Cu specimens, the average drop number before failure was approximately 15-18 and then the resistance values sharply increased. However, the average drop number of the Sn37Pb joints was over 110 and the increasing rate of the electrical resistance was smooth, which is consistent with the results of the board-level drop test. Moreover, one specimen of each kind was picked out and the microstructural observation was carried out to investigate the joint deformation behavior in the dynamic load. It was obvious that the plastic deformation capacity of the Sn37Pb joints was remarkably higher than the one of the Sn3.8Ag0.7Cu joints, proving that most of SnAgCu-based solders presented low deformation compatibility and low energy absorption. More... »

PAGES

292-298

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s10854-010-0131-x

DOI

http://dx.doi.org/10.1007/s10854-010-0131-x

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1048508887


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0906", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Electrical and Electronic Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Zhang", 
        "givenName": "Ning", 
        "id": "sg:person.014056156001.08", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014056156001.08"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Shi", 
        "givenName": "Yaowu", 
        "id": "sg:person.010147557037.66", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010147557037.66"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Guo", 
        "givenName": "Fu", 
        "id": "sg:person.014627203474.59", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014627203474.59"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Lei", 
        "givenName": "Yongping", 
        "id": "sg:person.012521025203.12", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012521025203.12"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Xia", 
        "givenName": "Zhidong", 
        "id": "sg:person.016447555263.38", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016447555263.38"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/grid.28703.3e", 
          "name": [
            "College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Chen", 
        "givenName": "Zhenhua", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "R&D Center, China Building Material Test & Certification Center, 1 Guanzhuang Dongli, 100024, Chaoyang District, Beijing, People\u2019s Republic of China", 
          "id": "http://www.grid.ac/institutes/None", 
          "name": [
            "R&D Center, China Building Material Test & Certification Center, 1 Guanzhuang Dongli, 100024, Chaoyang District, Beijing, People\u2019s Republic of China"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Tian", 
        "givenName": "Li", 
        "id": "sg:person.012757714405.32", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012757714405.32"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1007/s11664-007-0316-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1015142756", 
          "https://doi.org/10.1007/s11664-007-0316-0"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s10854-006-9016-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1001579177", 
          "https://doi.org/10.1007/s10854-006-9016-4"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11664-007-0260-z", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040427975", 
          "https://doi.org/10.1007/s11664-007-0260-z"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11664-008-0506-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1015830933", 
          "https://doi.org/10.1007/s11664-008-0506-4"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1557/jmr.2008.0129", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1020380582", 
          "https://doi.org/10.1557/jmr.2008.0129"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11664-008-0633-y", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1007872482", 
          "https://doi.org/10.1007/s11664-008-0633-y"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/s11664-008-0400-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1031759789", 
          "https://doi.org/10.1007/s11664-008-0400-0"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2010-05-15", 
    "datePublishedReg": "2010-05-15", 
    "description": "This study was concerned with the drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu (wt. %) solder joints when the specimens were subjected to drop test after soldering process. The U-notch butt-jointed specimen was adopted and a lab-designed drop tester was employed. Meanwhile, the electrical resistance values of two kinds of solder joints were measured and recorded after certain drop tests, and finally drop number versus resistance curves were plotted and compared. From the resistance variation with the drop number, it was observed that the Sn37Pb joints presented significantly higher drop performance than the Sn3.8Ag0.7Cu ones. For the Sn3.8Ag0.7Cu specimens, the average drop number before failure was approximately 15-18 and then the resistance values sharply increased. However, the average drop number of the Sn37Pb joints was over 110 and the increasing rate of the electrical resistance was smooth, which is consistent with the results of the board-level drop test. Moreover, one specimen of each kind was picked out and the microstructural observation was carried out to investigate the joint deformation behavior in the dynamic load. It was obvious that the plastic deformation capacity of the Sn37Pb joints was remarkably higher than the one of the Sn3.8Ag0.7Cu joints, proving that most of SnAgCu-based solders presented low deformation compatibility and low energy absorption.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s10854-010-0131-x", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136825", 
        "issn": [
          "0957-4522", 
          "1573-482X"
        ], 
        "name": "Journal of Materials Science: Materials in Electronics", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "3", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "22"
      }
    ], 
    "keywords": [
      "average drop number", 
      "drop performance", 
      "solder joints", 
      "drop test", 
      "board-level drop test", 
      "drop number", 
      "high drop performance", 
      "joint deformation behavior", 
      "plastic deformation capacity", 
      "resistance values", 
      "deformation capacity", 
      "deformation compatibility", 
      "deformation behavior", 
      "drop tester", 
      "microstructural observations", 
      "resistance curves", 
      "energy absorption", 
      "dynamic load", 
      "resistance variation", 
      "electrical resistance", 
      "Sn37Pb", 
      "joints", 
      "electrical resistance values", 
      "low energy absorption", 
      "SnAgCu", 
      "solder", 
      "performance", 
      "specimen", 
      "load", 
      "tester", 
      "specimens", 
      "test", 
      "compatibility", 
      "kind", 
      "resistance", 
      "behavior", 
      "process", 
      "absorption", 
      "values", 
      "capacity", 
      "curves", 
      "results", 
      "variation", 
      "failure", 
      "comparison", 
      "number", 
      "rate", 
      "observations", 
      "one", 
      "study", 
      "notch butt-jointed specimen", 
      "butt-jointed specimen", 
      "lab-designed drop tester", 
      "certain drop tests", 
      "Sn37Pb joints", 
      "low deformation compatibility"
    ], 
    "name": "Comparison of drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu solder joints subjected to drop test", 
    "pagination": "292-298", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1048508887"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s10854-010-0131-x"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s10854-010-0131-x", 
      "https://app.dimensions.ai/details/publication/pub.1048508887"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2021-12-01T19:22", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20211201/entities/gbq_results/article/article_510.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s10854-010-0131-x"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s10854-010-0131-x'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s10854-010-0131-x'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s10854-010-0131-x'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s10854-010-0131-x'


 

This table displays all metadata directly associated to this object as RDF triples.

190 TRIPLES      22 PREDICATES      89 URIs      73 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s10854-010-0131-x schema:about anzsrc-for:09
2 anzsrc-for:0906
3 anzsrc-for:0912
4 schema:author Nfcc873cfecf84f4c94b712b9307be2e9
5 schema:citation sg:pub.10.1007/s10854-006-9016-4
6 sg:pub.10.1007/s11664-007-0260-z
7 sg:pub.10.1007/s11664-007-0316-0
8 sg:pub.10.1007/s11664-008-0400-0
9 sg:pub.10.1007/s11664-008-0506-4
10 sg:pub.10.1007/s11664-008-0633-y
11 sg:pub.10.1557/jmr.2008.0129
12 schema:datePublished 2010-05-15
13 schema:datePublishedReg 2010-05-15
14 schema:description This study was concerned with the drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu (wt. %) solder joints when the specimens were subjected to drop test after soldering process. The U-notch butt-jointed specimen was adopted and a lab-designed drop tester was employed. Meanwhile, the electrical resistance values of two kinds of solder joints were measured and recorded after certain drop tests, and finally drop number versus resistance curves were plotted and compared. From the resistance variation with the drop number, it was observed that the Sn37Pb joints presented significantly higher drop performance than the Sn3.8Ag0.7Cu ones. For the Sn3.8Ag0.7Cu specimens, the average drop number before failure was approximately 15-18 and then the resistance values sharply increased. However, the average drop number of the Sn37Pb joints was over 110 and the increasing rate of the electrical resistance was smooth, which is consistent with the results of the board-level drop test. Moreover, one specimen of each kind was picked out and the microstructural observation was carried out to investigate the joint deformation behavior in the dynamic load. It was obvious that the plastic deformation capacity of the Sn37Pb joints was remarkably higher than the one of the Sn3.8Ag0.7Cu joints, proving that most of SnAgCu-based solders presented low deformation compatibility and low energy absorption.
15 schema:genre article
16 schema:inLanguage en
17 schema:isAccessibleForFree false
18 schema:isPartOf N5aeabf5d875a4dc1849a26e67f99b06f
19 Nf6c3df8bf0ab4c20af9cec4b42c16fd1
20 sg:journal.1136825
21 schema:keywords Sn37Pb
22 Sn37Pb joints
23 SnAgCu
24 absorption
25 average drop number
26 behavior
27 board-level drop test
28 butt-jointed specimen
29 capacity
30 certain drop tests
31 comparison
32 compatibility
33 curves
34 deformation behavior
35 deformation capacity
36 deformation compatibility
37 drop number
38 drop performance
39 drop test
40 drop tester
41 dynamic load
42 electrical resistance
43 electrical resistance values
44 energy absorption
45 failure
46 high drop performance
47 joint deformation behavior
48 joints
49 kind
50 lab-designed drop tester
51 load
52 low deformation compatibility
53 low energy absorption
54 microstructural observations
55 notch butt-jointed specimen
56 number
57 observations
58 one
59 performance
60 plastic deformation capacity
61 process
62 rate
63 resistance
64 resistance curves
65 resistance values
66 resistance variation
67 results
68 solder
69 solder joints
70 specimen
71 specimens
72 study
73 test
74 tester
75 values
76 variation
77 schema:name Comparison of drop performance between the Sn37Pb and the Sn3.8Ag0.7Cu solder joints subjected to drop test
78 schema:pagination 292-298
79 schema:productId N0f236142fbd34cfaacacdb21a1c065e5
80 N9c72bd0c05f14a588a3a7e62bb64e985
81 schema:sameAs https://app.dimensions.ai/details/publication/pub.1048508887
82 https://doi.org/10.1007/s10854-010-0131-x
83 schema:sdDatePublished 2021-12-01T19:22
84 schema:sdLicense https://scigraph.springernature.com/explorer/license/
85 schema:sdPublisher N24b634778f154e7886f78978955bd5a2
86 schema:url https://doi.org/10.1007/s10854-010-0131-x
87 sgo:license sg:explorer/license/
88 sgo:sdDataset articles
89 rdf:type schema:ScholarlyArticle
90 N086c43505daf41b08f0a166a03c69dc4 rdf:first Ne907ec938e374d1380d21f975a7bef7e
91 rdf:rest N338a9ee2aa44402ba1e8575eb4466a30
92 N0f236142fbd34cfaacacdb21a1c065e5 schema:name doi
93 schema:value 10.1007/s10854-010-0131-x
94 rdf:type schema:PropertyValue
95 N24b634778f154e7886f78978955bd5a2 schema:name Springer Nature - SN SciGraph project
96 rdf:type schema:Organization
97 N338a9ee2aa44402ba1e8575eb4466a30 rdf:first sg:person.012757714405.32
98 rdf:rest rdf:nil
99 N5aeabf5d875a4dc1849a26e67f99b06f schema:issueNumber 3
100 rdf:type schema:PublicationIssue
101 N7313da9fe453461e892bf616c45b5027 rdf:first sg:person.016447555263.38
102 rdf:rest N086c43505daf41b08f0a166a03c69dc4
103 N947f8db6dde948068807743904a326bf rdf:first sg:person.010147557037.66
104 rdf:rest Nc1fd3c39b6d1429385c6acd0e8af87ae
105 N9c72bd0c05f14a588a3a7e62bb64e985 schema:name dimensions_id
106 schema:value pub.1048508887
107 rdf:type schema:PropertyValue
108 Nc1fd3c39b6d1429385c6acd0e8af87ae rdf:first sg:person.014627203474.59
109 rdf:rest Nc3b57743ef054d8a8e619cd046a37a61
110 Nc3b57743ef054d8a8e619cd046a37a61 rdf:first sg:person.012521025203.12
111 rdf:rest N7313da9fe453461e892bf616c45b5027
112 Ne907ec938e374d1380d21f975a7bef7e schema:affiliation grid-institutes:grid.28703.3e
113 schema:familyName Chen
114 schema:givenName Zhenhua
115 rdf:type schema:Person
116 Nf6c3df8bf0ab4c20af9cec4b42c16fd1 schema:volumeNumber 22
117 rdf:type schema:PublicationVolume
118 Nfcc873cfecf84f4c94b712b9307be2e9 rdf:first sg:person.014056156001.08
119 rdf:rest N947f8db6dde948068807743904a326bf
120 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
121 schema:name Engineering
122 rdf:type schema:DefinedTerm
123 anzsrc-for:0906 schema:inDefinedTermSet anzsrc-for:
124 schema:name Electrical and Electronic Engineering
125 rdf:type schema:DefinedTerm
126 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
127 schema:name Materials Engineering
128 rdf:type schema:DefinedTerm
129 sg:journal.1136825 schema:issn 0957-4522
130 1573-482X
131 schema:name Journal of Materials Science: Materials in Electronics
132 schema:publisher Springer Nature
133 rdf:type schema:Periodical
134 sg:person.010147557037.66 schema:affiliation grid-institutes:grid.28703.3e
135 schema:familyName Shi
136 schema:givenName Yaowu
137 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.010147557037.66
138 rdf:type schema:Person
139 sg:person.012521025203.12 schema:affiliation grid-institutes:grid.28703.3e
140 schema:familyName Lei
141 schema:givenName Yongping
142 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012521025203.12
143 rdf:type schema:Person
144 sg:person.012757714405.32 schema:affiliation grid-institutes:None
145 schema:familyName Tian
146 schema:givenName Li
147 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012757714405.32
148 rdf:type schema:Person
149 sg:person.014056156001.08 schema:affiliation grid-institutes:grid.28703.3e
150 schema:familyName Zhang
151 schema:givenName Ning
152 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014056156001.08
153 rdf:type schema:Person
154 sg:person.014627203474.59 schema:affiliation grid-institutes:grid.28703.3e
155 schema:familyName Guo
156 schema:givenName Fu
157 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.014627203474.59
158 rdf:type schema:Person
159 sg:person.016447555263.38 schema:affiliation grid-institutes:grid.28703.3e
160 schema:familyName Xia
161 schema:givenName Zhidong
162 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016447555263.38
163 rdf:type schema:Person
164 sg:pub.10.1007/s10854-006-9016-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1001579177
165 https://doi.org/10.1007/s10854-006-9016-4
166 rdf:type schema:CreativeWork
167 sg:pub.10.1007/s11664-007-0260-z schema:sameAs https://app.dimensions.ai/details/publication/pub.1040427975
168 https://doi.org/10.1007/s11664-007-0260-z
169 rdf:type schema:CreativeWork
170 sg:pub.10.1007/s11664-007-0316-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1015142756
171 https://doi.org/10.1007/s11664-007-0316-0
172 rdf:type schema:CreativeWork
173 sg:pub.10.1007/s11664-008-0400-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1031759789
174 https://doi.org/10.1007/s11664-008-0400-0
175 rdf:type schema:CreativeWork
176 sg:pub.10.1007/s11664-008-0506-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1015830933
177 https://doi.org/10.1007/s11664-008-0506-4
178 rdf:type schema:CreativeWork
179 sg:pub.10.1007/s11664-008-0633-y schema:sameAs https://app.dimensions.ai/details/publication/pub.1007872482
180 https://doi.org/10.1007/s11664-008-0633-y
181 rdf:type schema:CreativeWork
182 sg:pub.10.1557/jmr.2008.0129 schema:sameAs https://app.dimensions.ai/details/publication/pub.1020380582
183 https://doi.org/10.1557/jmr.2008.0129
184 rdf:type schema:CreativeWork
185 grid-institutes:None schema:alternateName R&D Center, China Building Material Test & Certification Center, 1 Guanzhuang Dongli, 100024, Chaoyang District, Beijing, People’s Republic of China
186 schema:name R&D Center, China Building Material Test & Certification Center, 1 Guanzhuang Dongli, 100024, Chaoyang District, Beijing, People’s Republic of China
187 rdf:type schema:Organization
188 grid-institutes:grid.28703.3e schema:alternateName College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People’s Republic of China
189 schema:name College of Materials Science and Engineering, Beijing University of Technology, 100 Ping Le Yuan, 100124, Chaoyang District, Beijing, People’s Republic of China
190 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...