Synthesis of nickel boride by thermal explosion in ball-milled powder mixtures View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

2018-04-05

AUTHORS

Michail A. Korchagin, Dina V. Dudina, Boris B. Bokhonov, Natalia V. Bulina, Arina V. Ukhina, Igor S. Batraev

ABSTRACT

In this work, a synthesis route of Ni3B, an attractive material for making heating elements and a promising component for catalysts, was developed using high-energy ball milling of nickel and boron powder mixtures. The milling duration was varied from 1 to 15 min. Ball milling led to partial dissolution of boron in the crystalline lattice of nickel and crystallite size refinement of nickel. Heating of the ball-milled mixtures at a constant rate led to thermal explosion, the indications of which were a rapid temperature rise and the formation of boride phases. The duration of ball milling was shown to influence the phase composition of the products of thermal explosion. The time of milling ensuring the formation of single-phase Ni3B was determined to be 7 min. The ignition temperature of thermal explosion decreased with the milling time: a decrease by more than 300 °C was observed for the mixture milled for 15 min relative to the non-milled mixture. The maximum temperature developed during thermal explosion increased in the mixture milled for 1 min relative to the non-milled mixture and then decreased with the milling time reaching the level of the non-milled mixture after 15 min of milling. The observed dependence of the maximum temperature on the milling time is related to the net effect of mixing uniformity improvement between the reactants and a partial transformation of the reaction mixtures into Ni(B) solid solutions and Ni3B during milling. The proposed synthesis route of a single-phase Ni3B powder has advantages of short processing time and low-energy consumption. More... »

PAGES

13592-13599

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s10853-018-2290-8

DOI

http://dx.doi.org/10.1007/s10853-018-2290-8

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1103166031


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/03", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Chemical Sciences", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0399", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Other Chemical Sciences", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "National Research Tomsk State University, Lenin Ave. 36, 634050, Tomsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.77602.34", 
          "name": [
            "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia", 
            "Novosibirsk State Technical University, K. Marx Ave. 20, 630073, Novosibirsk, Russia", 
            "National Research Tomsk State University, Lenin Ave. 36, 634050, Tomsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Korchagin", 
        "givenName": "Michail A.", 
        "id": "sg:person.015025417455.23", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015025417455.23"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.436213.1", 
          "name": [
            "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia", 
            "Novosibirsk State Technical University, K. Marx Ave. 20, 630073, Novosibirsk, Russia", 
            "Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Dudina", 
        "givenName": "Dina V.", 
        "id": "sg:person.013776453602.94", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013776453602.94"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Novosibirsk State University, Pirogova str. 2, 630090, Novosibirsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.4605.7", 
          "name": [
            "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia", 
            "Novosibirsk State University, Pirogova str. 2, 630090, Novosibirsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bokhonov", 
        "givenName": "Boris B.", 
        "id": "sg:person.013054306634.87", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013054306634.87"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.435414.3", 
          "name": [
            "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Bulina", 
        "givenName": "Natalia V.", 
        "id": "sg:person.016042210634.19", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016042210634.19"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.435414.3", 
          "name": [
            "Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Ukhina", 
        "givenName": "Arina V.", 
        "id": "sg:person.011461345634.12", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011461345634.12"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia", 
          "id": "http://www.grid.ac/institutes/grid.436213.1", 
          "name": [
            "Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Batraev", 
        "givenName": "Igor S.", 
        "id": "sg:person.07570665211.30", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07570665211.30"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "sg:pub.10.1134/s0010508216020131", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1045217429", 
          "https://doi.org/10.1134/s0010508216020131"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1134/s0010508215050093", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1039075603", 
          "https://doi.org/10.1134/s0010508215050093"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.3103/s1068375514050081", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1051704126", 
          "https://doi.org/10.3103/s1068375514050081"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1134/s0020168509040074", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1042325505", 
          "https://doi.org/10.1134/s0020168509040074"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2018-04-05", 
    "datePublishedReg": "2018-04-05", 
    "description": "In this work, a synthesis route of Ni3B, an attractive material for making heating elements and a promising component for catalysts, was developed using high-energy ball milling of nickel and boron powder mixtures. The milling duration was varied from 1 to 15\u00a0min. Ball milling led to partial dissolution of boron in the crystalline lattice of nickel and crystallite size refinement of nickel. Heating of the ball-milled mixtures at a constant rate led to thermal explosion, the indications of which were a rapid temperature rise and the formation of boride phases. The duration of ball milling was shown to influence the phase composition of the products of thermal explosion. The time of milling ensuring the formation of single-phase Ni3B was determined to be 7\u00a0min. The ignition temperature of thermal explosion decreased with the milling time: a decrease by more than 300\u00a0\u00b0C was observed for the mixture milled for 15\u00a0min relative to the non-milled mixture. The maximum temperature developed during thermal explosion increased in the mixture milled for 1\u00a0min relative to the non-milled mixture and then decreased with the milling time reaching the level of the non-milled mixture after 15\u00a0min of milling. The observed dependence of the maximum temperature on the milling time is related to the net effect of mixing uniformity improvement between the reactants and a partial transformation of the reaction mixtures into Ni(B) solid solutions and Ni3B during milling. The proposed synthesis route of a single-phase Ni3B powder has advantages of short processing time and low-energy consumption.", 
    "genre": "article", 
    "id": "sg:pub.10.1007/s10853-018-2290-8", 
    "inLanguage": "en", 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1312116", 
        "issn": [
          "0022-2461", 
          "1573-4811"
        ], 
        "name": "Journal of Materials Science", 
        "publisher": "Springer Nature", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "19", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "53"
      }
    ], 
    "keywords": [
      "non-milled mixture", 
      "thermal explosion", 
      "powder mixtures", 
      "ball milling", 
      "ball-milled powder mixtures", 
      "high-energy ball milling", 
      "low-energy consumption", 
      "boron powder mixtures", 
      "crystallite size refinement", 
      "maximum temperature", 
      "ball-milled mixture", 
      "synthesis route", 
      "rapid temperature rise", 
      "short processing time", 
      "size refinement", 
      "heating element", 
      "min of milling", 
      "boride phases", 
      "ignition temperature", 
      "attractive material", 
      "milling time", 
      "uniformity improvement", 
      "temperature rise", 
      "phase composition", 
      "Ni3B", 
      "milling", 
      "solid solution", 
      "nickel boride", 
      "partial dissolution", 
      "nickel", 
      "processing time", 
      "temperature", 
      "promising component", 
      "partial transformation", 
      "explosion", 
      "crystalline lattice", 
      "mixture", 
      "borides", 
      "powder", 
      "observed dependence", 
      "heating", 
      "constant rate", 
      "boron", 
      "materials", 
      "dissolution", 
      "route", 
      "solution", 
      "formation", 
      "phase", 
      "time", 
      "reactants", 
      "min", 
      "refinement", 
      "advantages", 
      "consumption", 
      "work", 
      "dependence", 
      "catalyst", 
      "elements", 
      "composition", 
      "components", 
      "improvement", 
      "net effect", 
      "lattice", 
      "products", 
      "effect", 
      "rate", 
      "transformation", 
      "reaction mixture", 
      "decrease", 
      "rise", 
      "synthesis", 
      "duration", 
      "levels", 
      "indications", 
      "single-phase Ni3B", 
      "single-phase Ni3B powder", 
      "Ni3B powder"
    ], 
    "name": "Synthesis of nickel boride by thermal explosion in ball-milled powder mixtures", 
    "pagination": "13592-13599", 
    "productId": [
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1103166031"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s10853-018-2290-8"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s10853-018-2290-8", 
      "https://app.dimensions.ai/details/publication/pub.1103166031"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2021-12-01T19:40", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-springernature-scigraph/baseset/20211201/entities/gbq_results/article/article_760.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "https://doi.org/10.1007/s10853-018-2290-8"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s10853-018-2290-8'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s10853-018-2290-8'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s10853-018-2290-8'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s10853-018-2290-8'


 

This table displays all metadata directly associated to this object as RDF triples.

201 TRIPLES      22 PREDICATES      107 URIs      95 LITERALS      6 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s10853-018-2290-8 schema:about anzsrc-for:03
2 anzsrc-for:0399
3 schema:author N27a4318ab41c41408c8086af344dbdea
4 schema:citation sg:pub.10.1134/s0010508215050093
5 sg:pub.10.1134/s0010508216020131
6 sg:pub.10.1134/s0020168509040074
7 sg:pub.10.3103/s1068375514050081
8 schema:datePublished 2018-04-05
9 schema:datePublishedReg 2018-04-05
10 schema:description In this work, a synthesis route of Ni3B, an attractive material for making heating elements and a promising component for catalysts, was developed using high-energy ball milling of nickel and boron powder mixtures. The milling duration was varied from 1 to 15 min. Ball milling led to partial dissolution of boron in the crystalline lattice of nickel and crystallite size refinement of nickel. Heating of the ball-milled mixtures at a constant rate led to thermal explosion, the indications of which were a rapid temperature rise and the formation of boride phases. The duration of ball milling was shown to influence the phase composition of the products of thermal explosion. The time of milling ensuring the formation of single-phase Ni3B was determined to be 7 min. The ignition temperature of thermal explosion decreased with the milling time: a decrease by more than 300 °C was observed for the mixture milled for 15 min relative to the non-milled mixture. The maximum temperature developed during thermal explosion increased in the mixture milled for 1 min relative to the non-milled mixture and then decreased with the milling time reaching the level of the non-milled mixture after 15 min of milling. The observed dependence of the maximum temperature on the milling time is related to the net effect of mixing uniformity improvement between the reactants and a partial transformation of the reaction mixtures into Ni(B) solid solutions and Ni3B during milling. The proposed synthesis route of a single-phase Ni3B powder has advantages of short processing time and low-energy consumption.
11 schema:genre article
12 schema:inLanguage en
13 schema:isAccessibleForFree false
14 schema:isPartOf N201a94f4e63843e1877ed47b316736c0
15 N4a691795a09d495c8bd609f97447ebb8
16 sg:journal.1312116
17 schema:keywords Ni3B
18 Ni3B powder
19 advantages
20 attractive material
21 ball milling
22 ball-milled mixture
23 ball-milled powder mixtures
24 boride phases
25 borides
26 boron
27 boron powder mixtures
28 catalyst
29 components
30 composition
31 constant rate
32 consumption
33 crystalline lattice
34 crystallite size refinement
35 decrease
36 dependence
37 dissolution
38 duration
39 effect
40 elements
41 explosion
42 formation
43 heating
44 heating element
45 high-energy ball milling
46 ignition temperature
47 improvement
48 indications
49 lattice
50 levels
51 low-energy consumption
52 materials
53 maximum temperature
54 milling
55 milling time
56 min
57 min of milling
58 mixture
59 net effect
60 nickel
61 nickel boride
62 non-milled mixture
63 observed dependence
64 partial dissolution
65 partial transformation
66 phase
67 phase composition
68 powder
69 powder mixtures
70 processing time
71 products
72 promising component
73 rapid temperature rise
74 rate
75 reactants
76 reaction mixture
77 refinement
78 rise
79 route
80 short processing time
81 single-phase Ni3B
82 single-phase Ni3B powder
83 size refinement
84 solid solution
85 solution
86 synthesis
87 synthesis route
88 temperature
89 temperature rise
90 thermal explosion
91 time
92 transformation
93 uniformity improvement
94 work
95 schema:name Synthesis of nickel boride by thermal explosion in ball-milled powder mixtures
96 schema:pagination 13592-13599
97 schema:productId N5dd2f27f80a34da9977c0eeae31e7efc
98 Nb985afa4723647958a610fec325c95bc
99 schema:sameAs https://app.dimensions.ai/details/publication/pub.1103166031
100 https://doi.org/10.1007/s10853-018-2290-8
101 schema:sdDatePublished 2021-12-01T19:40
102 schema:sdLicense https://scigraph.springernature.com/explorer/license/
103 schema:sdPublisher Nf2ebd4c13bdb400387adf31378d8d505
104 schema:url https://doi.org/10.1007/s10853-018-2290-8
105 sgo:license sg:explorer/license/
106 sgo:sdDataset articles
107 rdf:type schema:ScholarlyArticle
108 N147233aae150417cb6b131354021b997 rdf:first sg:person.07570665211.30
109 rdf:rest rdf:nil
110 N201a94f4e63843e1877ed47b316736c0 schema:volumeNumber 53
111 rdf:type schema:PublicationVolume
112 N27a4318ab41c41408c8086af344dbdea rdf:first sg:person.015025417455.23
113 rdf:rest Na9ac9b986c724966a95c929c64896197
114 N4a691795a09d495c8bd609f97447ebb8 schema:issueNumber 19
115 rdf:type schema:PublicationIssue
116 N5dd2f27f80a34da9977c0eeae31e7efc schema:name dimensions_id
117 schema:value pub.1103166031
118 rdf:type schema:PropertyValue
119 N743b2e96b54e42a18ac9d832a8dea65c rdf:first sg:person.011461345634.12
120 rdf:rest N147233aae150417cb6b131354021b997
121 Na9ac9b986c724966a95c929c64896197 rdf:first sg:person.013776453602.94
122 rdf:rest Nd46745a11d294928865b3c2077a68b35
123 Nb985afa4723647958a610fec325c95bc schema:name doi
124 schema:value 10.1007/s10853-018-2290-8
125 rdf:type schema:PropertyValue
126 Ncc4690f8d5ca40a3a44105ef3e20358a rdf:first sg:person.016042210634.19
127 rdf:rest N743b2e96b54e42a18ac9d832a8dea65c
128 Nd46745a11d294928865b3c2077a68b35 rdf:first sg:person.013054306634.87
129 rdf:rest Ncc4690f8d5ca40a3a44105ef3e20358a
130 Nf2ebd4c13bdb400387adf31378d8d505 schema:name Springer Nature - SN SciGraph project
131 rdf:type schema:Organization
132 anzsrc-for:03 schema:inDefinedTermSet anzsrc-for:
133 schema:name Chemical Sciences
134 rdf:type schema:DefinedTerm
135 anzsrc-for:0399 schema:inDefinedTermSet anzsrc-for:
136 schema:name Other Chemical Sciences
137 rdf:type schema:DefinedTerm
138 sg:journal.1312116 schema:issn 0022-2461
139 1573-4811
140 schema:name Journal of Materials Science
141 schema:publisher Springer Nature
142 rdf:type schema:Periodical
143 sg:person.011461345634.12 schema:affiliation grid-institutes:grid.435414.3
144 schema:familyName Ukhina
145 schema:givenName Arina V.
146 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011461345634.12
147 rdf:type schema:Person
148 sg:person.013054306634.87 schema:affiliation grid-institutes:grid.4605.7
149 schema:familyName Bokhonov
150 schema:givenName Boris B.
151 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013054306634.87
152 rdf:type schema:Person
153 sg:person.013776453602.94 schema:affiliation grid-institutes:grid.436213.1
154 schema:familyName Dudina
155 schema:givenName Dina V.
156 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.013776453602.94
157 rdf:type schema:Person
158 sg:person.015025417455.23 schema:affiliation grid-institutes:grid.77602.34
159 schema:familyName Korchagin
160 schema:givenName Michail A.
161 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.015025417455.23
162 rdf:type schema:Person
163 sg:person.016042210634.19 schema:affiliation grid-institutes:grid.435414.3
164 schema:familyName Bulina
165 schema:givenName Natalia V.
166 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016042210634.19
167 rdf:type schema:Person
168 sg:person.07570665211.30 schema:affiliation grid-institutes:grid.436213.1
169 schema:familyName Batraev
170 schema:givenName Igor S.
171 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.07570665211.30
172 rdf:type schema:Person
173 sg:pub.10.1134/s0010508215050093 schema:sameAs https://app.dimensions.ai/details/publication/pub.1039075603
174 https://doi.org/10.1134/s0010508215050093
175 rdf:type schema:CreativeWork
176 sg:pub.10.1134/s0010508216020131 schema:sameAs https://app.dimensions.ai/details/publication/pub.1045217429
177 https://doi.org/10.1134/s0010508216020131
178 rdf:type schema:CreativeWork
179 sg:pub.10.1134/s0020168509040074 schema:sameAs https://app.dimensions.ai/details/publication/pub.1042325505
180 https://doi.org/10.1134/s0020168509040074
181 rdf:type schema:CreativeWork
182 sg:pub.10.3103/s1068375514050081 schema:sameAs https://app.dimensions.ai/details/publication/pub.1051704126
183 https://doi.org/10.3103/s1068375514050081
184 rdf:type schema:CreativeWork
185 grid-institutes:grid.435414.3 schema:alternateName Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia
186 schema:name Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia
187 rdf:type schema:Organization
188 grid-institutes:grid.436213.1 schema:alternateName Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia
189 schema:name Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia
190 Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, 630090, Novosibirsk, Russia
191 Novosibirsk State Technical University, K. Marx Ave. 20, 630073, Novosibirsk, Russia
192 rdf:type schema:Organization
193 grid-institutes:grid.4605.7 schema:alternateName Novosibirsk State University, Pirogova str. 2, 630090, Novosibirsk, Russia
194 schema:name Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia
195 Novosibirsk State University, Pirogova str. 2, 630090, Novosibirsk, Russia
196 rdf:type schema:Organization
197 grid-institutes:grid.77602.34 schema:alternateName National Research Tomsk State University, Lenin Ave. 36, 634050, Tomsk, Russia
198 schema:name Institute of Solid State Chemistry and Mechanochemistry SB RAS, Kutateladze str. 18, 630128, Novosibirsk, Russia
199 National Research Tomsk State University, Lenin Ave. 36, 634050, Tomsk, Russia
200 Novosibirsk State Technical University, K. Marx Ave. 20, 630073, Novosibirsk, Russia
201 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...