Production of a self-adhering mesophase powder from anthracene oil for low pressure forming of graphite artefacts View Full Text


Ontology type: schema:ScholarlyArticle      Open Access: True


Article Info

DATE

2016-07

AUTHORS

Matthys R. Delport, Heinrich Badenhorst

ABSTRACT

The objective of the investigation was to produce a high mesophase content pitch from low-cost anthracene oil without the use of catalysts. The pitch product was then used to produce graphitic artefacts using only a low pressure (5 MPa) forming step followed by carbonization and graphitization at a comparatively high heating rate. The heat treatment times and temperatures were varied across a wide range but only material treated at 475 °C produced a significant amount of mesophase. Furthermore only one pitch material resulted in a successful moulding which could be carbonized and graphitized. This pitch contained a significant portion (~8 wt%) of light material, which results in melting and flow behaviour during pressing, rather than sintering, if it is removed the material can no longer be successfully pressed. Due to the high mesophase content of the pitch, a high density (1720 kg m−3), highly graphitic artefact with minimal deformation during heat treatment is produced. The graphite product demonstrates grain separation but still results in a reasonable flexural strength of 4.5 MPa which may be improved further by re-impregnation depending on the requirement. This combined with its excellent purity and high yield makes it a good candidate for nuclear applications. More... »

PAGES

6309-6318

References to SciGraph publications

Journal

TITLE

Journal of Materials Science

ISSUE

13

VOLUME

51

Author Affiliations

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/s10853-016-9927-2

DOI

http://dx.doi.org/10.1007/s10853-016-9927-2

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1006721410


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "University of Pretoria", 
          "id": "https://www.grid.ac/institutes/grid.49697.35", 
          "name": [
            "SARChI Chair in Carbon Materials and Technology, Department of Chemical Engineering, University of Pretoria, Lynnwood Road, 0002, Pretoria, South Africa"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Delport", 
        "givenName": "Matthys R.", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "University of Pretoria", 
          "id": "https://www.grid.ac/institutes/grid.49697.35", 
          "name": [
            "SARChI Chair in Carbon Materials and Technology, Department of Chemical Engineering, University of Pretoria, Lynnwood Road, 0002, Pretoria, South Africa"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Badenhorst", 
        "givenName": "Heinrich", 
        "id": "sg:person.011761023503.43", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011761023503.43"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "https://doi.org/10.1016/0016-2361(88)90051-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000691067"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0016-2361(88)90051-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1000691067"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02402792", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1005784027", 
          "https://doi.org/10.1007/bf02402792"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02402792", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1005784027", 
          "https://doi.org/10.1007/bf02402792"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0008-6223(98)00321-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1007640427"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(94)90219-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1010427320"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(94)90219-4", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1010427320"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0008-6223(96)00114-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1010758888"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.jmatprotec.2008.01.019", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1015795575"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.carbon.2003.09.020", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1016290474"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(94)00134-l", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1019543396"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1023/b:jmsc.0000016178.95230.04", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1023048925", 
          "https://doi.org/10.1023/b:jmsc.0000016178.95230.04"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1023/a:1021859329162", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1024556328", 
          "https://doi.org/10.1023/a:1021859329162"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1023/a:1023740517269", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025672803", 
          "https://doi.org/10.1023/a:1023740517269"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1023/a:1018587418496", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025856870", 
          "https://doi.org/10.1023/a:1018587418496"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1023/a:1004672117361", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1026837524", 
          "https://doi.org/10.1023/a:1004672117361"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0008-6223(98)00081-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1028304427"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(94)90056-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1030670168"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(94)90056-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1030670168"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.jpowsour.2005.10.096", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034428195"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0008-6223(95)91245-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1042305803"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0008-6223(98)00298-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1043841449"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.carbon.2011.03.044", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1044573526"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.carbon.2011.09.052", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1048029684"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/j.carbon.2003.12.037", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1048092792"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "2016-07", 
    "datePublishedReg": "2016-07-01", 
    "description": "The objective of the investigation was to produce a high mesophase content pitch from low-cost anthracene oil without the use of catalysts. The pitch product was then used to produce graphitic artefacts using only a low pressure (5 MPa) forming step followed by carbonization and graphitization at a comparatively high heating rate. The heat treatment times and temperatures were varied across a wide range but only material treated at 475 \u00b0C produced a significant amount of mesophase. Furthermore only one pitch material resulted in a successful moulding which could be carbonized and graphitized. This pitch contained a significant portion (~8 wt%) of light material, which results in melting and flow behaviour during pressing, rather than sintering, if it is removed the material can no longer be successfully pressed. Due to the high mesophase content of the pitch, a high density (1720 kg m\u22123), highly graphitic artefact with minimal deformation during heat treatment is produced. The graphite product demonstrates grain separation but still results in a reasonable flexural strength of 4.5 MPa which may be improved further by re-impregnation depending on the requirement. This combined with its excellent purity and high yield makes it a good candidate for nuclear applications.", 
    "genre": "research_article", 
    "id": "sg:pub.10.1007/s10853-016-9927-2", 
    "inLanguage": [
      "en"
    ], 
    "isAccessibleForFree": true, 
    "isPartOf": [
      {
        "id": "sg:journal.1312116", 
        "issn": [
          "0022-2461", 
          "1573-4811"
        ], 
        "name": "Journal of Materials Science", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "13", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "51"
      }
    ], 
    "name": "Production of a self-adhering mesophase powder from anthracene oil for low pressure forming of graphite artefacts", 
    "pagination": "6309-6318", 
    "productId": [
      {
        "name": "readcube_id", 
        "type": "PropertyValue", 
        "value": [
          "20041e5bd3fc98848dec6cb340b3a39e58cb1a0eccc24b709450ba5fc5c64713"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/s10853-016-9927-2"
        ]
      }, 
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1006721410"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/s10853-016-9927-2", 
      "https://app.dimensions.ai/details/publication/pub.1006721410"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2019-04-10T21:36", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-uberresearch-data-dimensions-target-20181106-alternative/cleanup/v134/2549eaecd7973599484d7c17b260dba0a4ecb94b/merge/v9/a6c9fde33151104705d4d7ff012ea9563521a3ce/jats-lookup/v90/0000000001_0000000264/records_8687_00000510.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "http://link.springer.com/10.1007%2Fs10853-016-9927-2"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/s10853-016-9927-2'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/s10853-016-9927-2'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/s10853-016-9927-2'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/s10853-016-9927-2'


 

This table displays all metadata directly associated to this object as RDF triples.

136 TRIPLES      21 PREDICATES      48 URIs      19 LITERALS      7 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/s10853-016-9927-2 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author N0767880537fb4e6583d8eca369e60ba5
4 schema:citation sg:pub.10.1007/bf02402792
5 sg:pub.10.1023/a:1004672117361
6 sg:pub.10.1023/a:1018587418496
7 sg:pub.10.1023/a:1021859329162
8 sg:pub.10.1023/a:1023740517269
9 sg:pub.10.1023/b:jmsc.0000016178.95230.04
10 https://doi.org/10.1016/0008-6223(94)00134-l
11 https://doi.org/10.1016/0008-6223(94)90056-6
12 https://doi.org/10.1016/0008-6223(94)90219-4
13 https://doi.org/10.1016/0008-6223(95)91245-3
14 https://doi.org/10.1016/0016-2361(88)90051-8
15 https://doi.org/10.1016/j.carbon.2003.09.020
16 https://doi.org/10.1016/j.carbon.2003.12.037
17 https://doi.org/10.1016/j.carbon.2011.03.044
18 https://doi.org/10.1016/j.carbon.2011.09.052
19 https://doi.org/10.1016/j.jmatprotec.2008.01.019
20 https://doi.org/10.1016/j.jpowsour.2005.10.096
21 https://doi.org/10.1016/s0008-6223(96)00114-5
22 https://doi.org/10.1016/s0008-6223(98)00081-5
23 https://doi.org/10.1016/s0008-6223(98)00298-x
24 https://doi.org/10.1016/s0008-6223(98)00321-2
25 schema:datePublished 2016-07
26 schema:datePublishedReg 2016-07-01
27 schema:description The objective of the investigation was to produce a high mesophase content pitch from low-cost anthracene oil without the use of catalysts. The pitch product was then used to produce graphitic artefacts using only a low pressure (5 MPa) forming step followed by carbonization and graphitization at a comparatively high heating rate. The heat treatment times and temperatures were varied across a wide range but only material treated at 475 °C produced a significant amount of mesophase. Furthermore only one pitch material resulted in a successful moulding which could be carbonized and graphitized. This pitch contained a significant portion (~8 wt%) of light material, which results in melting and flow behaviour during pressing, rather than sintering, if it is removed the material can no longer be successfully pressed. Due to the high mesophase content of the pitch, a high density (1720 kg m−3), highly graphitic artefact with minimal deformation during heat treatment is produced. The graphite product demonstrates grain separation but still results in a reasonable flexural strength of 4.5 MPa which may be improved further by re-impregnation depending on the requirement. This combined with its excellent purity and high yield makes it a good candidate for nuclear applications.
28 schema:genre research_article
29 schema:inLanguage en
30 schema:isAccessibleForFree true
31 schema:isPartOf N27b3843b50bf4ccbb5182921f0b53b9c
32 N6372a789e8944d1fab5d2d53596b8331
33 sg:journal.1312116
34 schema:name Production of a self-adhering mesophase powder from anthracene oil for low pressure forming of graphite artefacts
35 schema:pagination 6309-6318
36 schema:productId N6fbf8afbc1a043a4a5dac512ff950053
37 N7329fda2f3c845068a41f2881f6d6a7c
38 Nf39d5d6a3e93449a8055d775880204c5
39 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006721410
40 https://doi.org/10.1007/s10853-016-9927-2
41 schema:sdDatePublished 2019-04-10T21:36
42 schema:sdLicense https://scigraph.springernature.com/explorer/license/
43 schema:sdPublisher N4e606fa7df82401eaec16968dc53c29b
44 schema:url http://link.springer.com/10.1007%2Fs10853-016-9927-2
45 sgo:license sg:explorer/license/
46 sgo:sdDataset articles
47 rdf:type schema:ScholarlyArticle
48 N0767880537fb4e6583d8eca369e60ba5 rdf:first N189527406a454045a7f1c7df5aa8d3d5
49 rdf:rest N0a8d7cd39727443fa4fa8e6e2a092613
50 N0a8d7cd39727443fa4fa8e6e2a092613 rdf:first sg:person.011761023503.43
51 rdf:rest rdf:nil
52 N189527406a454045a7f1c7df5aa8d3d5 schema:affiliation https://www.grid.ac/institutes/grid.49697.35
53 schema:familyName Delport
54 schema:givenName Matthys R.
55 rdf:type schema:Person
56 N27b3843b50bf4ccbb5182921f0b53b9c schema:volumeNumber 51
57 rdf:type schema:PublicationVolume
58 N4e606fa7df82401eaec16968dc53c29b schema:name Springer Nature - SN SciGraph project
59 rdf:type schema:Organization
60 N6372a789e8944d1fab5d2d53596b8331 schema:issueNumber 13
61 rdf:type schema:PublicationIssue
62 N6fbf8afbc1a043a4a5dac512ff950053 schema:name readcube_id
63 schema:value 20041e5bd3fc98848dec6cb340b3a39e58cb1a0eccc24b709450ba5fc5c64713
64 rdf:type schema:PropertyValue
65 N7329fda2f3c845068a41f2881f6d6a7c schema:name dimensions_id
66 schema:value pub.1006721410
67 rdf:type schema:PropertyValue
68 Nf39d5d6a3e93449a8055d775880204c5 schema:name doi
69 schema:value 10.1007/s10853-016-9927-2
70 rdf:type schema:PropertyValue
71 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
72 schema:name Engineering
73 rdf:type schema:DefinedTerm
74 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
75 schema:name Materials Engineering
76 rdf:type schema:DefinedTerm
77 sg:journal.1312116 schema:issn 0022-2461
78 1573-4811
79 schema:name Journal of Materials Science
80 rdf:type schema:Periodical
81 sg:person.011761023503.43 schema:affiliation https://www.grid.ac/institutes/grid.49697.35
82 schema:familyName Badenhorst
83 schema:givenName Heinrich
84 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.011761023503.43
85 rdf:type schema:Person
86 sg:pub.10.1007/bf02402792 schema:sameAs https://app.dimensions.ai/details/publication/pub.1005784027
87 https://doi.org/10.1007/bf02402792
88 rdf:type schema:CreativeWork
89 sg:pub.10.1023/a:1004672117361 schema:sameAs https://app.dimensions.ai/details/publication/pub.1026837524
90 https://doi.org/10.1023/a:1004672117361
91 rdf:type schema:CreativeWork
92 sg:pub.10.1023/a:1018587418496 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025856870
93 https://doi.org/10.1023/a:1018587418496
94 rdf:type schema:CreativeWork
95 sg:pub.10.1023/a:1021859329162 schema:sameAs https://app.dimensions.ai/details/publication/pub.1024556328
96 https://doi.org/10.1023/a:1021859329162
97 rdf:type schema:CreativeWork
98 sg:pub.10.1023/a:1023740517269 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025672803
99 https://doi.org/10.1023/a:1023740517269
100 rdf:type schema:CreativeWork
101 sg:pub.10.1023/b:jmsc.0000016178.95230.04 schema:sameAs https://app.dimensions.ai/details/publication/pub.1023048925
102 https://doi.org/10.1023/b:jmsc.0000016178.95230.04
103 rdf:type schema:CreativeWork
104 https://doi.org/10.1016/0008-6223(94)00134-l schema:sameAs https://app.dimensions.ai/details/publication/pub.1019543396
105 rdf:type schema:CreativeWork
106 https://doi.org/10.1016/0008-6223(94)90056-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1030670168
107 rdf:type schema:CreativeWork
108 https://doi.org/10.1016/0008-6223(94)90219-4 schema:sameAs https://app.dimensions.ai/details/publication/pub.1010427320
109 rdf:type schema:CreativeWork
110 https://doi.org/10.1016/0008-6223(95)91245-3 schema:sameAs https://app.dimensions.ai/details/publication/pub.1042305803
111 rdf:type schema:CreativeWork
112 https://doi.org/10.1016/0016-2361(88)90051-8 schema:sameAs https://app.dimensions.ai/details/publication/pub.1000691067
113 rdf:type schema:CreativeWork
114 https://doi.org/10.1016/j.carbon.2003.09.020 schema:sameAs https://app.dimensions.ai/details/publication/pub.1016290474
115 rdf:type schema:CreativeWork
116 https://doi.org/10.1016/j.carbon.2003.12.037 schema:sameAs https://app.dimensions.ai/details/publication/pub.1048092792
117 rdf:type schema:CreativeWork
118 https://doi.org/10.1016/j.carbon.2011.03.044 schema:sameAs https://app.dimensions.ai/details/publication/pub.1044573526
119 rdf:type schema:CreativeWork
120 https://doi.org/10.1016/j.carbon.2011.09.052 schema:sameAs https://app.dimensions.ai/details/publication/pub.1048029684
121 rdf:type schema:CreativeWork
122 https://doi.org/10.1016/j.jmatprotec.2008.01.019 schema:sameAs https://app.dimensions.ai/details/publication/pub.1015795575
123 rdf:type schema:CreativeWork
124 https://doi.org/10.1016/j.jpowsour.2005.10.096 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034428195
125 rdf:type schema:CreativeWork
126 https://doi.org/10.1016/s0008-6223(96)00114-5 schema:sameAs https://app.dimensions.ai/details/publication/pub.1010758888
127 rdf:type schema:CreativeWork
128 https://doi.org/10.1016/s0008-6223(98)00081-5 schema:sameAs https://app.dimensions.ai/details/publication/pub.1028304427
129 rdf:type schema:CreativeWork
130 https://doi.org/10.1016/s0008-6223(98)00298-x schema:sameAs https://app.dimensions.ai/details/publication/pub.1043841449
131 rdf:type schema:CreativeWork
132 https://doi.org/10.1016/s0008-6223(98)00321-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1007640427
133 rdf:type schema:CreativeWork
134 https://www.grid.ac/institutes/grid.49697.35 schema:alternateName University of Pretoria
135 schema:name SARChI Chair in Carbon Materials and Technology, Department of Chemical Engineering, University of Pretoria, Lynnwood Road, 0002, Pretoria, South Africa
136 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...