Loading rate and test temperature effects on fracture ofIn Situ niobium silicide-niobium composites View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

1996-10

AUTHORS

Joseph D. Rigney, John J. Lewandowski

ABSTRACT

Arc cast, extruded, and heat-treatedin situ composites of niobium suicide (Nb5Si3) intermetallic with niobium phases (primary—Nbp and secondary—Nbs) exhibited high fracture resistance in comparison to monolithic Nb5Si3. In toughness tests conducted at 298 K and slow applied loading rates, the fracture process proceeded by the microcracking of the Nb5Si3 and plastic deformation of the Nbp and Nbs phases, producing resistance-curve behavior and toughnesses of 28 MPa√m with damage zone lengths less than 500μm. The effects of changes in the Nbp yield strength and fracture behavior on the measured toughnesses were investigated by varying the loading rates during fracture tests at both 77 and 298 K. Quantitative fractography was utilized to completely characterize each fracture surface created at 298 K in order to determine the type of fracture mode (i.e., dimpled, cleavage) exhibited by the Nbp. Specimens tested at either higher loading rates or lower test temperatures consistently exhibited a greater amount of cleavage fracture in the Nbp, while the Nbs, always remained ductile. However, the fracture toughness values determined from experiments spanning six orders of magnitude in loading rate at 298 and 77 K exhibited little variation, even under conditions when the majority of Nbp phases failed by cleavage at 77 K. The changes in fracture mode with increasing loading rate and/or decreasing test temperature and their effects on fracture toughness are rationalized by comparison to existing theoretical models. More... »

PAGES

3292-3306

References to SciGraph publications

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/bf02663879

DOI

http://dx.doi.org/10.1007/bf02663879

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1030925261


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/1103", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Clinical Sciences", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/11", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Medical and Health Sciences", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "name": [
            "ALCOA Technical Center, Alcoa Center, 15069, PA"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Rigney", 
        "givenName": "Joseph D.", 
        "id": "sg:person.012142177017.32", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012142177017.32"
        ], 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "Case Western Reserve University", 
          "id": "https://www.grid.ac/institutes/grid.67105.35", 
          "name": [
            "Department of Materials Science and Engineering, the Case School of Engineering, Case Western Reserve University, 44106, Cleveland, OH"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Lewandowski", 
        "givenName": "John J.", 
        "id": "sg:person.016454024011.53", 
        "sameAs": [
          "https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016454024011.53"
        ], 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "https://doi.org/10.1016/0956-7151(94)00391-t", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1002597702"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(72)90100-9", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1003749622"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(72)90100-9", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1003749622"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0022-5096(98)90003-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1004503435"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/s0022-5096(98)90003-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1004503435"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1080/01418618308236538", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1009005505"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf01082105", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1013343416", 
          "https://doi.org/10.1007/bf01082105"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf01082105", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1013343416", 
          "https://doi.org/10.1007/bf01082105"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(65)90129-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1024280698"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(65)90129-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1024280698"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(88)90149-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025016591"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(88)90149-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025016591"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90069-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025846976"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90069-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1025846976"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02657338", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1027606179", 
          "https://doi.org/10.1007/bf02657338"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02700449", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029377611", 
          "https://doi.org/10.1007/bf02700449"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90332-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029836403"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90332-5", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029836403"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0956-716x(91)90387-g", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029981250"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0956-716x(91)90387-g", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029981250"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02817275", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1033213380", 
          "https://doi.org/10.1007/bf02817275"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5096(85)90029-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1034920361"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(60)90118-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1036184036"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(60)90118-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1036184036"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02667370", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037784908", 
          "https://doi.org/10.1007/bf02667370"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02667370", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037784908", 
          "https://doi.org/10.1007/bf02667370"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0925-8388(93)90629-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037816277"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0925-8388(93)90629-2", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037816277"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02670764", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1038684763", 
          "https://doi.org/10.1007/bf02670764"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "sg:pub.10.1007/bf02670764", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1038684763", 
          "https://doi.org/10.1007/bf02670764"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5088(62)90062-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1039391377"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5088(62)90062-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1039391377"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5088(70)90042-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040803029"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5088(70)90042-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1040803029"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1111/j.1151-2916.1981.tb10313.x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1041470573"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(60)90211-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1045363438"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(60)90211-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1045363438"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0921-5093(92)90312-o", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1048309398"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0921-5093(92)90312-o", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1048309398"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5096(68)90013-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049693747"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5096(68)90013-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1049693747"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5096(71)90009-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1050259456"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0022-5096(71)90009-3", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1050259456"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90207-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1051492600"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(89)90207-1", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1051492600"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "1996-10", 
    "datePublishedReg": "1996-10-01", 
    "description": "Arc cast, extruded, and heat-treatedin situ composites of niobium suicide (Nb5Si3) intermetallic with niobium phases (primary\u2014Nbp and secondary\u2014Nbs) exhibited high fracture resistance in comparison to monolithic Nb5Si3. In toughness tests conducted at 298 K and slow applied loading rates, the fracture process proceeded by the microcracking of the Nb5Si3 and plastic deformation of the Nbp and Nbs phases, producing resistance-curve behavior and toughnesses of 28 MPa\u221am with damage zone lengths less than 500\u03bcm. The effects of changes in the Nbp yield strength and fracture behavior on the measured toughnesses were investigated by varying the loading rates during fracture tests at both 77 and 298 K. Quantitative fractography was utilized to completely characterize each fracture surface created at 298 K in order to determine the type of fracture mode (i.e., dimpled, cleavage) exhibited by the Nbp. Specimens tested at either higher loading rates or lower test temperatures consistently exhibited a greater amount of cleavage fracture in the Nbp, while the Nbs, always remained ductile. However, the fracture toughness values determined from experiments spanning six orders of magnitude in loading rate at 298 and 77 K exhibited little variation, even under conditions when the majority of Nbp phases failed by cleavage at 77 K. The changes in fracture mode with increasing loading rate and/or decreasing test temperature and their effects on fracture toughness are rationalized by comparison to existing theoretical models.", 
    "genre": "research_article", 
    "id": "sg:pub.10.1007/bf02663879", 
    "inLanguage": [
      "en"
    ], 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1136292", 
        "issn": [
          "1073-5623", 
          "1543-1940"
        ], 
        "name": "Metallurgical and Materials Transactions A", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "10", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "27"
      }
    ], 
    "name": "Loading rate and test temperature effects on fracture ofIn Situ niobium silicide-niobium composites", 
    "pagination": "3292-3306", 
    "productId": [
      {
        "name": "readcube_id", 
        "type": "PropertyValue", 
        "value": [
          "9353323804a3dc0a261147ff9848cf46dc942e3ad2047ee84ca5ba456035bcd9"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/bf02663879"
        ]
      }, 
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1030925261"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/bf02663879", 
      "https://app.dimensions.ai/details/publication/pub.1030925261"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2019-04-11T13:36", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-uberresearch-data-dimensions-target-20181106-alternative/cleanup/v134/2549eaecd7973599484d7c17b260dba0a4ecb94b/merge/v9/a6c9fde33151104705d4d7ff012ea9563521a3ce/jats-lookup/v90/0000000370_0000000370/records_46779_00000001.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "http://link.springer.com/10.1007%2FBF02663879"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/bf02663879'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/bf02663879'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/bf02663879'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/bf02663879'


 

This table displays all metadata directly associated to this object as RDF triples.

154 TRIPLES      21 PREDICATES      53 URIs      19 LITERALS      7 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/bf02663879 schema:about anzsrc-for:11
2 anzsrc-for:1103
3 schema:author Nf0e487b9a62f4f78ba6bd0e8a7dc3886
4 schema:citation sg:pub.10.1007/bf01082105
5 sg:pub.10.1007/bf02657338
6 sg:pub.10.1007/bf02667370
7 sg:pub.10.1007/bf02670764
8 sg:pub.10.1007/bf02700449
9 sg:pub.10.1007/bf02817275
10 https://doi.org/10.1016/0001-6160(60)90118-8
11 https://doi.org/10.1016/0001-6160(60)90211-x
12 https://doi.org/10.1016/0001-6160(65)90129-x
13 https://doi.org/10.1016/0001-6160(72)90100-9
14 https://doi.org/10.1016/0001-6160(88)90149-6
15 https://doi.org/10.1016/0001-6160(89)90069-2
16 https://doi.org/10.1016/0001-6160(89)90207-1
17 https://doi.org/10.1016/0001-6160(89)90332-5
18 https://doi.org/10.1016/0022-5088(62)90062-0
19 https://doi.org/10.1016/0022-5088(70)90042-1
20 https://doi.org/10.1016/0022-5096(68)90013-6
21 https://doi.org/10.1016/0022-5096(71)90009-3
22 https://doi.org/10.1016/0022-5096(85)90029-8
23 https://doi.org/10.1016/0921-5093(92)90312-o
24 https://doi.org/10.1016/0925-8388(93)90629-2
25 https://doi.org/10.1016/0956-7151(94)00391-t
26 https://doi.org/10.1016/0956-716x(91)90387-g
27 https://doi.org/10.1016/s0022-5096(98)90003-5
28 https://doi.org/10.1080/01418618308236538
29 https://doi.org/10.1111/j.1151-2916.1981.tb10313.x
30 schema:datePublished 1996-10
31 schema:datePublishedReg 1996-10-01
32 schema:description Arc cast, extruded, and heat-treatedin situ composites of niobium suicide (Nb5Si3) intermetallic with niobium phases (primary—Nbp and secondary—Nbs) exhibited high fracture resistance in comparison to monolithic Nb5Si3. In toughness tests conducted at 298 K and slow applied loading rates, the fracture process proceeded by the microcracking of the Nb5Si3 and plastic deformation of the Nbp and Nbs phases, producing resistance-curve behavior and toughnesses of 28 MPa√m with damage zone lengths less than 500μm. The effects of changes in the Nbp yield strength and fracture behavior on the measured toughnesses were investigated by varying the loading rates during fracture tests at both 77 and 298 K. Quantitative fractography was utilized to completely characterize each fracture surface created at 298 K in order to determine the type of fracture mode (i.e., dimpled, cleavage) exhibited by the Nbp. Specimens tested at either higher loading rates or lower test temperatures consistently exhibited a greater amount of cleavage fracture in the Nbp, while the Nbs, always remained ductile. However, the fracture toughness values determined from experiments spanning six orders of magnitude in loading rate at 298 and 77 K exhibited little variation, even under conditions when the majority of Nbp phases failed by cleavage at 77 K. The changes in fracture mode with increasing loading rate and/or decreasing test temperature and their effects on fracture toughness are rationalized by comparison to existing theoretical models.
33 schema:genre research_article
34 schema:inLanguage en
35 schema:isAccessibleForFree false
36 schema:isPartOf N8d2d9e43ca314ee8b9f7f9e4a31359c3
37 Nb5716dba10714ae1a05e2ab8776411f0
38 sg:journal.1136292
39 schema:name Loading rate and test temperature effects on fracture ofIn Situ niobium silicide-niobium composites
40 schema:pagination 3292-3306
41 schema:productId N724043d3ac1f419f9ebfd8d64e1d77be
42 N73574c40c4044119a246cb2a6bfc600b
43 N8b8da7051d0945e49fc28803b699ef5c
44 schema:sameAs https://app.dimensions.ai/details/publication/pub.1030925261
45 https://doi.org/10.1007/bf02663879
46 schema:sdDatePublished 2019-04-11T13:36
47 schema:sdLicense https://scigraph.springernature.com/explorer/license/
48 schema:sdPublisher Nb947e343f0f44edbb2e7933933d8f68b
49 schema:url http://link.springer.com/10.1007%2FBF02663879
50 sgo:license sg:explorer/license/
51 sgo:sdDataset articles
52 rdf:type schema:ScholarlyArticle
53 N1254616d9146435d98a1e0fb0fa974c6 rdf:first sg:person.016454024011.53
54 rdf:rest rdf:nil
55 N724043d3ac1f419f9ebfd8d64e1d77be schema:name doi
56 schema:value 10.1007/bf02663879
57 rdf:type schema:PropertyValue
58 N73574c40c4044119a246cb2a6bfc600b schema:name readcube_id
59 schema:value 9353323804a3dc0a261147ff9848cf46dc942e3ad2047ee84ca5ba456035bcd9
60 rdf:type schema:PropertyValue
61 N8b8da7051d0945e49fc28803b699ef5c schema:name dimensions_id
62 schema:value pub.1030925261
63 rdf:type schema:PropertyValue
64 N8d2d9e43ca314ee8b9f7f9e4a31359c3 schema:volumeNumber 27
65 rdf:type schema:PublicationVolume
66 Nb5716dba10714ae1a05e2ab8776411f0 schema:issueNumber 10
67 rdf:type schema:PublicationIssue
68 Nb947e343f0f44edbb2e7933933d8f68b schema:name Springer Nature - SN SciGraph project
69 rdf:type schema:Organization
70 Nd379e9e1935044a892ae2c32d5ed3d48 schema:name ALCOA Technical Center, Alcoa Center, 15069, PA
71 rdf:type schema:Organization
72 Nf0e487b9a62f4f78ba6bd0e8a7dc3886 rdf:first sg:person.012142177017.32
73 rdf:rest N1254616d9146435d98a1e0fb0fa974c6
74 anzsrc-for:11 schema:inDefinedTermSet anzsrc-for:
75 schema:name Medical and Health Sciences
76 rdf:type schema:DefinedTerm
77 anzsrc-for:1103 schema:inDefinedTermSet anzsrc-for:
78 schema:name Clinical Sciences
79 rdf:type schema:DefinedTerm
80 sg:journal.1136292 schema:issn 1073-5623
81 1543-1940
82 schema:name Metallurgical and Materials Transactions A
83 rdf:type schema:Periodical
84 sg:person.012142177017.32 schema:affiliation Nd379e9e1935044a892ae2c32d5ed3d48
85 schema:familyName Rigney
86 schema:givenName Joseph D.
87 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.012142177017.32
88 rdf:type schema:Person
89 sg:person.016454024011.53 schema:affiliation https://www.grid.ac/institutes/grid.67105.35
90 schema:familyName Lewandowski
91 schema:givenName John J.
92 schema:sameAs https://app.dimensions.ai/discover/publication?and_facet_researcher=ur.016454024011.53
93 rdf:type schema:Person
94 sg:pub.10.1007/bf01082105 schema:sameAs https://app.dimensions.ai/details/publication/pub.1013343416
95 https://doi.org/10.1007/bf01082105
96 rdf:type schema:CreativeWork
97 sg:pub.10.1007/bf02657338 schema:sameAs https://app.dimensions.ai/details/publication/pub.1027606179
98 https://doi.org/10.1007/bf02657338
99 rdf:type schema:CreativeWork
100 sg:pub.10.1007/bf02667370 schema:sameAs https://app.dimensions.ai/details/publication/pub.1037784908
101 https://doi.org/10.1007/bf02667370
102 rdf:type schema:CreativeWork
103 sg:pub.10.1007/bf02670764 schema:sameAs https://app.dimensions.ai/details/publication/pub.1038684763
104 https://doi.org/10.1007/bf02670764
105 rdf:type schema:CreativeWork
106 sg:pub.10.1007/bf02700449 schema:sameAs https://app.dimensions.ai/details/publication/pub.1029377611
107 https://doi.org/10.1007/bf02700449
108 rdf:type schema:CreativeWork
109 sg:pub.10.1007/bf02817275 schema:sameAs https://app.dimensions.ai/details/publication/pub.1033213380
110 https://doi.org/10.1007/bf02817275
111 rdf:type schema:CreativeWork
112 https://doi.org/10.1016/0001-6160(60)90118-8 schema:sameAs https://app.dimensions.ai/details/publication/pub.1036184036
113 rdf:type schema:CreativeWork
114 https://doi.org/10.1016/0001-6160(60)90211-x schema:sameAs https://app.dimensions.ai/details/publication/pub.1045363438
115 rdf:type schema:CreativeWork
116 https://doi.org/10.1016/0001-6160(65)90129-x schema:sameAs https://app.dimensions.ai/details/publication/pub.1024280698
117 rdf:type schema:CreativeWork
118 https://doi.org/10.1016/0001-6160(72)90100-9 schema:sameAs https://app.dimensions.ai/details/publication/pub.1003749622
119 rdf:type schema:CreativeWork
120 https://doi.org/10.1016/0001-6160(88)90149-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025016591
121 rdf:type schema:CreativeWork
122 https://doi.org/10.1016/0001-6160(89)90069-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1025846976
123 rdf:type schema:CreativeWork
124 https://doi.org/10.1016/0001-6160(89)90207-1 schema:sameAs https://app.dimensions.ai/details/publication/pub.1051492600
125 rdf:type schema:CreativeWork
126 https://doi.org/10.1016/0001-6160(89)90332-5 schema:sameAs https://app.dimensions.ai/details/publication/pub.1029836403
127 rdf:type schema:CreativeWork
128 https://doi.org/10.1016/0022-5088(62)90062-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1039391377
129 rdf:type schema:CreativeWork
130 https://doi.org/10.1016/0022-5088(70)90042-1 schema:sameAs https://app.dimensions.ai/details/publication/pub.1040803029
131 rdf:type schema:CreativeWork
132 https://doi.org/10.1016/0022-5096(68)90013-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1049693747
133 rdf:type schema:CreativeWork
134 https://doi.org/10.1016/0022-5096(71)90009-3 schema:sameAs https://app.dimensions.ai/details/publication/pub.1050259456
135 rdf:type schema:CreativeWork
136 https://doi.org/10.1016/0022-5096(85)90029-8 schema:sameAs https://app.dimensions.ai/details/publication/pub.1034920361
137 rdf:type schema:CreativeWork
138 https://doi.org/10.1016/0921-5093(92)90312-o schema:sameAs https://app.dimensions.ai/details/publication/pub.1048309398
139 rdf:type schema:CreativeWork
140 https://doi.org/10.1016/0925-8388(93)90629-2 schema:sameAs https://app.dimensions.ai/details/publication/pub.1037816277
141 rdf:type schema:CreativeWork
142 https://doi.org/10.1016/0956-7151(94)00391-t schema:sameAs https://app.dimensions.ai/details/publication/pub.1002597702
143 rdf:type schema:CreativeWork
144 https://doi.org/10.1016/0956-716x(91)90387-g schema:sameAs https://app.dimensions.ai/details/publication/pub.1029981250
145 rdf:type schema:CreativeWork
146 https://doi.org/10.1016/s0022-5096(98)90003-5 schema:sameAs https://app.dimensions.ai/details/publication/pub.1004503435
147 rdf:type schema:CreativeWork
148 https://doi.org/10.1080/01418618308236538 schema:sameAs https://app.dimensions.ai/details/publication/pub.1009005505
149 rdf:type schema:CreativeWork
150 https://doi.org/10.1111/j.1151-2916.1981.tb10313.x schema:sameAs https://app.dimensions.ai/details/publication/pub.1041470573
151 rdf:type schema:CreativeWork
152 https://www.grid.ac/institutes/grid.67105.35 schema:alternateName Case Western Reserve University
153 schema:name Department of Materials Science and Engineering, the Case School of Engineering, Case Western Reserve University, 44106, Cleveland, OH
154 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...