The effect of particle content and matrix grain size on the recrystallisation of two-phase aluminium-iron alloys View Full Text


Ontology type: schema:ScholarlyArticle     


Article Info

DATE

1967-05

AUTHORS

P. R. Mould, P. Cotterill

ABSTRACT

The recrystallisation of aluminium alloys in the composition range 0.002 to 1.08 wt% iron has been followed metallographically and by hardness measurements. The recrystallisation of solid-solution alloys was retarded as the iron content increased, whereas that of the two-phase alloys was accelerated. This latter effect was associated with a marked increase in nucleation rate, with no significant change of growth rate, as the Al3Fe particle spacing decreased from 15 to 4μm. Decreasing the grain size of the two-phase alloys, at constant composition, also caused an acceleration of recrystallisation, the magnitude of which decreased as the Al3Fe content increased. These effects have been shown to be independent of the size of the Al3Fe particles, within the range studied (diameters 0.6 to 2.2μm). The results are discussed in terms of a model (which is based on metallographic observations) of nucleation at matrix grain boundaries and at particle/ matrix interfaces. It is suggested that the retardation of nucleation, observed by other workers, in more closely spaced dispersions, occurs because nucleation at particle/ matrix interfaces becomes difficult when the inter-particle spacing becomes of the same order as the diameter of the sub-structure of the deformed matrix. More... »

PAGES

241-255

Journal

TITLE

Journal of Materials Science

ISSUE

3

VOLUME

2

Author Affiliations

Identifiers

URI

http://scigraph.springernature.com/pub.10.1007/bf00555381

DOI

http://dx.doi.org/10.1007/bf00555381

DIMENSIONS

https://app.dimensions.ai/details/publication/pub.1006271660


Indexing Status Check whether this publication has been indexed by Scopus and Web Of Science using the SN Indexing Status Tool
Incoming Citations Browse incoming citations for this publication using opencitations.net

JSON-LD is the canonical representation for SciGraph data.

TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

[
  {
    "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
    "about": [
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/0912", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Materials Engineering", 
        "type": "DefinedTerm"
      }, 
      {
        "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/09", 
        "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
        "name": "Engineering", 
        "type": "DefinedTerm"
      }
    ], 
    "author": [
      {
        "affiliation": {
          "alternateName": "University of Surrey", 
          "id": "https://www.grid.ac/institutes/grid.5475.3", 
          "name": [
            "Department of Metallurgy and Materials Technology, University of Surrey, SW11, London, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Mould", 
        "givenName": "P. R.", 
        "type": "Person"
      }, 
      {
        "affiliation": {
          "alternateName": "University of Surrey", 
          "id": "https://www.grid.ac/institutes/grid.5475.3", 
          "name": [
            "Department of Metallurgy and Materials Technology, University of Surrey, SW11, London, UK"
          ], 
          "type": "Organization"
        }, 
        "familyName": "Cotterill", 
        "givenName": "P.", 
        "type": "Person"
      }
    ], 
    "citation": [
      {
        "id": "https://doi.org/10.1016/0001-6160(57)90109-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1015037628"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(57)90109-8", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1015037628"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1080/14786436008241221", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1016054959"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1098/rspa.1962.0080", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1017357570"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(53)90048-0", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1029272626"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(64)90044-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037664916"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(64)90044-6", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1037664916"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1098/rspa.1952.0228", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1038028595"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(61)90147-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1043380350"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1016/0001-6160(61)90147-x", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1043380350"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1179/mtlr.1961.6.1.193", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1044134037"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1080/14786436108238371", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1047805926"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1063/1.1699614", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1057770058"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1063/1.1728543", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1057795043"
        ], 
        "type": "CreativeWork"
      }, 
      {
        "id": "https://doi.org/10.1179/095066061790425983", 
        "sameAs": [
          "https://app.dimensions.ai/details/publication/pub.1064103385"
        ], 
        "type": "CreativeWork"
      }
    ], 
    "datePublished": "1967-05", 
    "datePublishedReg": "1967-05-01", 
    "description": "The recrystallisation of aluminium alloys in the composition range 0.002 to 1.08 wt% iron has been followed metallographically and by hardness measurements. The recrystallisation of solid-solution alloys was retarded as the iron content increased, whereas that of the two-phase alloys was accelerated. This latter effect was associated with a marked increase in nucleation rate, with no significant change of growth rate, as the Al3Fe particle spacing decreased from 15 to 4\u03bcm. Decreasing the grain size of the two-phase alloys, at constant composition, also caused an acceleration of recrystallisation, the magnitude of which decreased as the Al3Fe content increased. These effects have been shown to be independent of the size of the Al3Fe particles, within the range studied (diameters 0.6 to 2.2\u03bcm). The results are discussed in terms of a model (which is based on metallographic observations) of nucleation at matrix grain boundaries and at particle/ matrix interfaces. It is suggested that the retardation of nucleation, observed by other workers, in more closely spaced dispersions, occurs because nucleation at particle/ matrix interfaces becomes difficult when the inter-particle spacing becomes of the same order as the diameter of the sub-structure of the deformed matrix.", 
    "genre": "research_article", 
    "id": "sg:pub.10.1007/bf00555381", 
    "inLanguage": [
      "en"
    ], 
    "isAccessibleForFree": false, 
    "isPartOf": [
      {
        "id": "sg:journal.1312116", 
        "issn": [
          "0022-2461", 
          "1573-4811"
        ], 
        "name": "Journal of Materials Science", 
        "type": "Periodical"
      }, 
      {
        "issueNumber": "3", 
        "type": "PublicationIssue"
      }, 
      {
        "type": "PublicationVolume", 
        "volumeNumber": "2"
      }
    ], 
    "name": "The effect of particle content and matrix grain size on the recrystallisation of two-phase aluminium-iron alloys", 
    "pagination": "241-255", 
    "productId": [
      {
        "name": "readcube_id", 
        "type": "PropertyValue", 
        "value": [
          "1ddfd2de1d99244f911e980390c7794fcee2b0589377111ecf74bcb58b3e06a1"
        ]
      }, 
      {
        "name": "doi", 
        "type": "PropertyValue", 
        "value": [
          "10.1007/bf00555381"
        ]
      }, 
      {
        "name": "dimensions_id", 
        "type": "PropertyValue", 
        "value": [
          "pub.1006271660"
        ]
      }
    ], 
    "sameAs": [
      "https://doi.org/10.1007/bf00555381", 
      "https://app.dimensions.ai/details/publication/pub.1006271660"
    ], 
    "sdDataset": "articles", 
    "sdDatePublished": "2019-04-11T13:56", 
    "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
    "sdPublisher": {
      "name": "Springer Nature - SN SciGraph project", 
      "type": "Organization"
    }, 
    "sdSource": "s3://com-uberresearch-data-dimensions-target-20181106-alternative/cleanup/v134/2549eaecd7973599484d7c17b260dba0a4ecb94b/merge/v9/a6c9fde33151104705d4d7ff012ea9563521a3ce/jats-lookup/v90/0000000371_0000000371/records_130817_00000000.jsonl", 
    "type": "ScholarlyArticle", 
    "url": "http://link.springer.com/10.1007/BF00555381"
  }
]
 

Download the RDF metadata as:  json-ld nt turtle xml License info

HOW TO GET THIS DATA PROGRAMMATICALLY:

JSON-LD is a popular format for linked data which is fully compatible with JSON.

curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/pub.10.1007/bf00555381'

N-Triples is a line-based linked data format ideal for batch operations.

curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/pub.10.1007/bf00555381'

Turtle is a human-readable linked data format.

curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/pub.10.1007/bf00555381'

RDF/XML is a standard XML format for linked data.

curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/pub.10.1007/bf00555381'


 

This table displays all metadata directly associated to this object as RDF triples.

102 TRIPLES      21 PREDICATES      39 URIs      19 LITERALS      7 BLANK NODES

Subject Predicate Object
1 sg:pub.10.1007/bf00555381 schema:about anzsrc-for:09
2 anzsrc-for:0912
3 schema:author Nef67a3a6fddb42ceabb70df981c3753d
4 schema:citation https://doi.org/10.1016/0001-6160(53)90048-0
5 https://doi.org/10.1016/0001-6160(57)90109-8
6 https://doi.org/10.1016/0001-6160(61)90147-x
7 https://doi.org/10.1016/0001-6160(64)90044-6
8 https://doi.org/10.1063/1.1699614
9 https://doi.org/10.1063/1.1728543
10 https://doi.org/10.1080/14786436008241221
11 https://doi.org/10.1080/14786436108238371
12 https://doi.org/10.1098/rspa.1952.0228
13 https://doi.org/10.1098/rspa.1962.0080
14 https://doi.org/10.1179/095066061790425983
15 https://doi.org/10.1179/mtlr.1961.6.1.193
16 schema:datePublished 1967-05
17 schema:datePublishedReg 1967-05-01
18 schema:description The recrystallisation of aluminium alloys in the composition range 0.002 to 1.08 wt% iron has been followed metallographically and by hardness measurements. The recrystallisation of solid-solution alloys was retarded as the iron content increased, whereas that of the two-phase alloys was accelerated. This latter effect was associated with a marked increase in nucleation rate, with no significant change of growth rate, as the Al3Fe particle spacing decreased from 15 to 4μm. Decreasing the grain size of the two-phase alloys, at constant composition, also caused an acceleration of recrystallisation, the magnitude of which decreased as the Al3Fe content increased. These effects have been shown to be independent of the size of the Al3Fe particles, within the range studied (diameters 0.6 to 2.2μm). The results are discussed in terms of a model (which is based on metallographic observations) of nucleation at matrix grain boundaries and at particle/ matrix interfaces. It is suggested that the retardation of nucleation, observed by other workers, in more closely spaced dispersions, occurs because nucleation at particle/ matrix interfaces becomes difficult when the inter-particle spacing becomes of the same order as the diameter of the sub-structure of the deformed matrix.
19 schema:genre research_article
20 schema:inLanguage en
21 schema:isAccessibleForFree false
22 schema:isPartOf N62dc329344c6481f903147240cfb083e
23 Nf019347d34b247bbaeab74ea64e601e3
24 sg:journal.1312116
25 schema:name The effect of particle content and matrix grain size on the recrystallisation of two-phase aluminium-iron alloys
26 schema:pagination 241-255
27 schema:productId N360c772f8e1144dfb6f014bcb38f17c8
28 Na2ec3b59565546bca689546f4e0b3b0e
29 Na9e025990d8442e6813fd65346848316
30 schema:sameAs https://app.dimensions.ai/details/publication/pub.1006271660
31 https://doi.org/10.1007/bf00555381
32 schema:sdDatePublished 2019-04-11T13:56
33 schema:sdLicense https://scigraph.springernature.com/explorer/license/
34 schema:sdPublisher N623bf7c092dc4526b409aaec7acb4ff0
35 schema:url http://link.springer.com/10.1007/BF00555381
36 sgo:license sg:explorer/license/
37 sgo:sdDataset articles
38 rdf:type schema:ScholarlyArticle
39 N360c772f8e1144dfb6f014bcb38f17c8 schema:name dimensions_id
40 schema:value pub.1006271660
41 rdf:type schema:PropertyValue
42 N3a081fc6206b473f855623be7ef242aa schema:affiliation https://www.grid.ac/institutes/grid.5475.3
43 schema:familyName Mould
44 schema:givenName P. R.
45 rdf:type schema:Person
46 N623bf7c092dc4526b409aaec7acb4ff0 schema:name Springer Nature - SN SciGraph project
47 rdf:type schema:Organization
48 N62dc329344c6481f903147240cfb083e schema:issueNumber 3
49 rdf:type schema:PublicationIssue
50 N956db9c75d594c7cab91b66be08f5e2b schema:affiliation https://www.grid.ac/institutes/grid.5475.3
51 schema:familyName Cotterill
52 schema:givenName P.
53 rdf:type schema:Person
54 Na2ec3b59565546bca689546f4e0b3b0e schema:name doi
55 schema:value 10.1007/bf00555381
56 rdf:type schema:PropertyValue
57 Na9e025990d8442e6813fd65346848316 schema:name readcube_id
58 schema:value 1ddfd2de1d99244f911e980390c7794fcee2b0589377111ecf74bcb58b3e06a1
59 rdf:type schema:PropertyValue
60 Ne5a7bfc437a040e49e802e9c6fdbdc16 rdf:first N956db9c75d594c7cab91b66be08f5e2b
61 rdf:rest rdf:nil
62 Nef67a3a6fddb42ceabb70df981c3753d rdf:first N3a081fc6206b473f855623be7ef242aa
63 rdf:rest Ne5a7bfc437a040e49e802e9c6fdbdc16
64 Nf019347d34b247bbaeab74ea64e601e3 schema:volumeNumber 2
65 rdf:type schema:PublicationVolume
66 anzsrc-for:09 schema:inDefinedTermSet anzsrc-for:
67 schema:name Engineering
68 rdf:type schema:DefinedTerm
69 anzsrc-for:0912 schema:inDefinedTermSet anzsrc-for:
70 schema:name Materials Engineering
71 rdf:type schema:DefinedTerm
72 sg:journal.1312116 schema:issn 0022-2461
73 1573-4811
74 schema:name Journal of Materials Science
75 rdf:type schema:Periodical
76 https://doi.org/10.1016/0001-6160(53)90048-0 schema:sameAs https://app.dimensions.ai/details/publication/pub.1029272626
77 rdf:type schema:CreativeWork
78 https://doi.org/10.1016/0001-6160(57)90109-8 schema:sameAs https://app.dimensions.ai/details/publication/pub.1015037628
79 rdf:type schema:CreativeWork
80 https://doi.org/10.1016/0001-6160(61)90147-x schema:sameAs https://app.dimensions.ai/details/publication/pub.1043380350
81 rdf:type schema:CreativeWork
82 https://doi.org/10.1016/0001-6160(64)90044-6 schema:sameAs https://app.dimensions.ai/details/publication/pub.1037664916
83 rdf:type schema:CreativeWork
84 https://doi.org/10.1063/1.1699614 schema:sameAs https://app.dimensions.ai/details/publication/pub.1057770058
85 rdf:type schema:CreativeWork
86 https://doi.org/10.1063/1.1728543 schema:sameAs https://app.dimensions.ai/details/publication/pub.1057795043
87 rdf:type schema:CreativeWork
88 https://doi.org/10.1080/14786436008241221 schema:sameAs https://app.dimensions.ai/details/publication/pub.1016054959
89 rdf:type schema:CreativeWork
90 https://doi.org/10.1080/14786436108238371 schema:sameAs https://app.dimensions.ai/details/publication/pub.1047805926
91 rdf:type schema:CreativeWork
92 https://doi.org/10.1098/rspa.1952.0228 schema:sameAs https://app.dimensions.ai/details/publication/pub.1038028595
93 rdf:type schema:CreativeWork
94 https://doi.org/10.1098/rspa.1962.0080 schema:sameAs https://app.dimensions.ai/details/publication/pub.1017357570
95 rdf:type schema:CreativeWork
96 https://doi.org/10.1179/095066061790425983 schema:sameAs https://app.dimensions.ai/details/publication/pub.1064103385
97 rdf:type schema:CreativeWork
98 https://doi.org/10.1179/mtlr.1961.6.1.193 schema:sameAs https://app.dimensions.ai/details/publication/pub.1044134037
99 rdf:type schema:CreativeWork
100 https://www.grid.ac/institutes/grid.5475.3 schema:alternateName University of Surrey
101 schema:name Department of Metallurgy and Materials Technology, University of Surrey, SW11, London, UK
102 rdf:type schema:Organization
 




Preview window. Press ESC to close (or click here)


...