Clarification of mechanism of re-deterioration caused in RC after repair and application to maintenance management system View Homepage


Ontology type: schema:MonetaryGrant     


Grant Info

YEARS

2014-2017

FUNDING AMOUNT

13130000 JPY

ABSTRACT

The effect of the repair with silane-type surface penetrant material under an environment of ultraviolet rays was investigated. A low water permeability was kept for 20 years. On the other hand, a low chloride permeability was kept for 10 years but decreased at 20th year. However, it could be recovered by second application.Secondly, it is easy to adsorb chloride ions on a formwork plane compared with a cut plane. However, the difference decreased in a concrete with high strength.Further, when PC beams repaired a section, a step-by-step restoration distributed the pre-stress to several-time. Therefore, the pre-stress did not decrease when a section was cut down. As a result, the load of the stress increment of the existing concrete decreased, and the crack occurrence load of the repair part became large. More... »

URL

https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-26289137

Related SciGraph Publications

  • 2018. Study on Triage for Deteriorated Concrete Structures by JSCE-342 in THE AGEING OF MATERIALS AND STRUCTURES
  • JSON-LD is the canonical representation for SciGraph data.

    TIP: You can open this SciGraph record using an external JSON-LD service: JSON-LD Playground Google SDTT

    [
      {
        "@context": "https://springernature.github.io/scigraph/jsonld/sgcontext.json", 
        "about": [
          {
            "id": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/2209", 
            "inDefinedTermSet": "http://purl.org/au-research/vocabulary/anzsrc-for/2008/", 
            "type": "DefinedTerm"
          }
        ], 
        "amount": {
          "currency": "JPY", 
          "type": "MonetaryAmount", 
          "value": "13130000"
        }, 
        "description": "The effect of the repair with silane-type surface penetrant material under an environment of ultraviolet rays was investigated. A low water permeability was kept for 20 years. On the other hand, a low chloride permeability was kept for 10 years but decreased at 20th year. However, it could be recovered by second application.Secondly, it is easy to adsorb chloride ions on a formwork plane compared with a cut plane. However, the difference decreased in a concrete with high strength.Further, when PC beams repaired a section, a step-by-step restoration distributed the pre-stress to several-time. Therefore, the pre-stress did not decrease when a section was cut down. As a result, the load of the stress increment of the existing concrete decreased, and the crack occurrence load of the repair part became large.", 
        "endDate": "2017-03-31T00:00:00Z", 
        "funder": {
          "id": "https://www.grid.ac/institutes/grid.54432.34", 
          "type": "Organization"
        }, 
        "id": "sg:grant.6137675", 
        "identifier": [
          {
            "name": "dimensions_id", 
            "type": "PropertyValue", 
            "value": [
              "6137675"
            ]
          }, 
          {
            "name": "kaken_id", 
            "type": "PropertyValue", 
            "value": [
              "26289137"
            ]
          }
        ], 
        "inLanguage": [
          "en"
        ], 
        "keywords": [
          "differences", 
          "cut plane", 
          "silane-type surface penetrant material", 
          "step restoration", 
          "low water permeability", 
          "crack occurrence load", 
          "clarification", 
          "steps", 
          "ultraviolet rays", 
          "second application", 
          "repair parts", 
          "concrete", 
          "20th year", 
          "RC", 
          "effect", 
          "formwork plane", 
          "application", 
          "lower chloride permeability", 
          "mechanism", 
          "sections", 
          "high strength", 
          "years", 
          "PC", 
          "stress increment", 
          "other hand", 
          "environment", 
          "deterioration", 
          "load", 
          "pre-stress", 
          "maintenance management system", 
          "repair", 
          "results", 
          "chloride ions"
        ], 
        "name": "Clarification of mechanism of re-deterioration caused in RC after repair and application to maintenance management system", 
        "recipient": [
          {
            "id": "https://www.grid.ac/institutes/grid.444537.5", 
            "type": "Organization"
          }
        ], 
        "sameAs": [
          "https://app.dimensions.ai/details/grant/grant.6137675"
        ], 
        "sdDataset": "grants", 
        "sdDatePublished": "2019-03-07T11:49", 
        "sdLicense": "https://scigraph.springernature.com/explorer/license/", 
        "sdPublisher": {
          "name": "Springer Nature - SN SciGraph project", 
          "type": "Organization"
        }, 
        "sdSource": "s3://com.uberresearch.data.processor/core_data/20181219_192338/projects/base/kaken_projects_31.xml.gz", 
        "startDate": "2014-04-01T00:00:00Z", 
        "type": "MonetaryGrant", 
        "url": "https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-26289137"
      }
    ]
     

    Download the RDF metadata as:  json-ld nt turtle xml License info

    HOW TO GET THIS DATA PROGRAMMATICALLY:

    JSON-LD is a popular format for linked data which is fully compatible with JSON.

    curl -H 'Accept: application/ld+json' 'https://scigraph.springernature.com/grant.6137675'

    N-Triples is a line-based linked data format ideal for batch operations.

    curl -H 'Accept: application/n-triples' 'https://scigraph.springernature.com/grant.6137675'

    Turtle is a human-readable linked data format.

    curl -H 'Accept: text/turtle' 'https://scigraph.springernature.com/grant.6137675'

    RDF/XML is a standard XML format for linked data.

    curl -H 'Accept: application/rdf+xml' 'https://scigraph.springernature.com/grant.6137675'


     

    This table displays all metadata directly associated to this object as RDF triples.

    67 TRIPLES      19 PREDICATES      53 URIs      46 LITERALS      4 BLANK NODES

    Subject Predicate Object
    1 sg:grant.6137675 schema:about anzsrc-for:2209
    2 schema:amount N4cce58ec97e84857ab381dcf8e0eaa99
    3 schema:description The effect of the repair with silane-type surface penetrant material under an environment of ultraviolet rays was investigated. A low water permeability was kept for 20 years. On the other hand, a low chloride permeability was kept for 10 years but decreased at 20th year. However, it could be recovered by second application.Secondly, it is easy to adsorb chloride ions on a formwork plane compared with a cut plane. However, the difference decreased in a concrete with high strength.Further, when PC beams repaired a section, a step-by-step restoration distributed the pre-stress to several-time. Therefore, the pre-stress did not decrease when a section was cut down. As a result, the load of the stress increment of the existing concrete decreased, and the crack occurrence load of the repair part became large.
    4 schema:endDate 2017-03-31T00:00:00Z
    5 schema:funder https://www.grid.ac/institutes/grid.54432.34
    6 schema:identifier N17b6a3fe66c247fb99caca771b840db1
    7 N966658f42e1f48a8a1ae605551a69b48
    8 schema:inLanguage en
    9 schema:keywords 20th year
    10 PC
    11 RC
    12 application
    13 chloride ions
    14 clarification
    15 concrete
    16 crack occurrence load
    17 cut plane
    18 deterioration
    19 differences
    20 effect
    21 environment
    22 formwork plane
    23 high strength
    24 load
    25 low water permeability
    26 lower chloride permeability
    27 maintenance management system
    28 mechanism
    29 other hand
    30 pre-stress
    31 repair
    32 repair parts
    33 results
    34 second application
    35 sections
    36 silane-type surface penetrant material
    37 step restoration
    38 steps
    39 stress increment
    40 ultraviolet rays
    41 years
    42 schema:name Clarification of mechanism of re-deterioration caused in RC after repair and application to maintenance management system
    43 schema:recipient https://www.grid.ac/institutes/grid.444537.5
    44 schema:sameAs https://app.dimensions.ai/details/grant/grant.6137675
    45 schema:sdDatePublished 2019-03-07T11:49
    46 schema:sdLicense https://scigraph.springernature.com/explorer/license/
    47 schema:sdPublisher N90fad894a4af40bf9c4667d73f877c74
    48 schema:startDate 2014-04-01T00:00:00Z
    49 schema:url https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-26289137
    50 sgo:license sg:explorer/license/
    51 sgo:sdDataset grants
    52 rdf:type schema:MonetaryGrant
    53 N17b6a3fe66c247fb99caca771b840db1 schema:name dimensions_id
    54 schema:value 6137675
    55 rdf:type schema:PropertyValue
    56 N4cce58ec97e84857ab381dcf8e0eaa99 schema:currency JPY
    57 schema:value 13130000
    58 rdf:type schema:MonetaryAmount
    59 N90fad894a4af40bf9c4667d73f877c74 schema:name Springer Nature - SN SciGraph project
    60 rdf:type schema:Organization
    61 N966658f42e1f48a8a1ae605551a69b48 schema:name kaken_id
    62 schema:value 26289137
    63 rdf:type schema:PropertyValue
    64 anzsrc-for:2209 schema:inDefinedTermSet anzsrc-for:
    65 rdf:type schema:DefinedTerm
    66 https://www.grid.ac/institutes/grid.444537.5 schema:Organization
    67 https://www.grid.ac/institutes/grid.54432.34 schema:Organization
     




    Preview window. Press ESC to close (or click here)


    ...